Failure of a Cast Aluminum Engine Head in a High Performance Application

The investigation described in this article examined a cast aluminum head used in a high performance (drag racing) application. These engine heads had been failing within a few seconds of startup. A sample head was examined to determine the cause. Visual inspection found two cracks on the exhaust side of the head. One crack initiated at the bottom of a spark plug well. The head was then sectioned for metallographic examination and fracture analysis. Metallographic examination revealed a large number of shrinkage pores throughout the casting. The fracture surface intersected many of these shrinkage pores. A significantly sized pore was located near the bottom of the suspect spark plug well near a stress-concentrating feature. This pore acted as the crack-initiating defect, which caused the engine head to fail.     

High Gd Concentration GaGdN Grown at Low Temperatures

GaGdN layers were grown at temperatures below 300°C by radio-frequency plasma-assisted molecular beam epitaxy on sapphire substrates. GaGdN samples with high Gd concentration as high as 12.5% were obtained by lowering the growth temperature. X-ray diffraction results showed no obvious secondary phase, which means that the phase separation can be suppressed by the growth at low temperatures. All samples, including those grown at room temperature, showed ferromagnetic characteristics. Photoluminescence emission was observed, though spectra exhibit broad and sharp luminescence bands related to many kinds of defects. It is suggested that electrons coming from defects, especially, nitrogen vacancy, stabilize ferromagnetism, and that the carrier-induced ferromagnetism occurs in the low-temperature-growth GaGdN.     

新经济增长理论对我国人力资本发展的借鉴

新经济增长理论为人力资本理论注入了新的内容,为各国如何利用人力资本发展经济提供了理论指导。分析了新经济增长理论中有关人力资本的理论,以此对我国经济和人力资本的发展提出了一些借鉴;收益递增模型。