Synthesis and characterization of biocompatible hydroxyapatite coated ferrite

Ferrite particles coated with biocompatible phases can be used for hyperthermia treatment of cancer. We have synthesized substituted calcium hexaferrite, which is not stable on its own but is stabilized with small substitution of La. Hexaferrite of chemical composition (CaO)_0.75(La₂0₃)_0.20(Fe₂O₃)₆ was prepared using citrate gel method. Hydroxyapatite was prepared by precipitating it from aqueous solution of Ca(NO₃)₂ and (NH₄)₂HPO₄ maintaining pH above 11. Four different methods were used for coating of hydroxyapatite on ferrite particles. SEM with EDX and X-ray diffraction analysis shows clear evidence of coating of hydroxyapatite on ferrite particles. These coated ferrite particles exhibited coercive field up to 2 kOe, which could be made useful for hysteresis heating in hyperthermia. Studies by culturing BHK-21 cells and WBC over the samples show evidence of biocompatibility. SEM micrographs and cell counts give clear indication of cell growth on the surface of the sample. Finally coated ferrite particle was implanted in Kasaulli mouse to test its biocompatibility. The magnetic properties and biocompatibility studies show that these hydroxyapatite coated ferrites could be useful for hyperthermia.     

Electrochemical synthesis and characterization of chloride doped polyaniline

Chloride doped polyaniline conducting polymer films have been prepared in a protic acid medium (HCl) by potentiodynamic method in an electrochemical cell and studied by cyclic voltammetry and FTIR techniques. The FTIR spectra confirmed Cl^- ion doping in the polymers. The polymerization rate was found to increase with increasing concentration of aniline monomer. But the films obtained at high monomer concentration were rough having a nonuniform flaky polyaniline distribution. Results showed that the polymerization rate did not increase beyond a critical HCl concentration. Cyclic voltammetry suggested that, the oxidation-reduction current increased with an increase in scan rate and that the undoped polyaniline films were not hygroscopic whereas chloride doped polyaniline films were found to be highly hygroscopic.     

负载型复合载体及其镍基催化剂的性能

采用溶胶-凝胶法制备了负载型ZrO_2/Al_2O_3和ZrO_2/Al_2O_3-SiO_2复合载体,研究了不同复合载体对Ni基催化剂CO_2重整甲烷反应和性能的影响,并用XRD、IR、TPR、TPD和BET等方法对复合载体及催化剂进行了表征。结果表明,ZrO_2负载在基载体后比表面积、碱性、活性组分Ni的分散度和Ni与ZrO_2的相互作用增大。NiO在复合载体表面的分散容量与ZrO_2的负载量有关,ZrO_2的负载量为37．5%时NiO的分散容量达最高值(24．0%)。与Ni/ZrO_2相比,Ni/ZrO_2/Al_2O_3-SiO_2和Ni/ZrO_2/Al_2O_3催化剂对CO_2的吸附能力增大,CO_2吸附量增加,酸强度降低,CO_2重整CH_4反应活性提高,其中以Ni/ZrO_2/Al_2O_3催化剂的活性最好。     

溶剂脱沥青组合工艺生产重交通道路沥青

中国石化荆门分公司以江汉-阿曼混合原油和江汉-鲁宁混合原油为原料,分别采用减压蒸馏—丙烷脱沥青和减压蒸馏—添加催化裂化油浆—丙烷脱沥青工艺,生产出符合SH 0522—2000的100号道路沥青。结果表明,江汉-阿曼混合原油减压渣油中掺兑质量分数为30%的催化裂化油浆后,脱油沥青的各项性能均满足AH-70或AH-90重交通道路沥青的要求,而且薄膜烘箱试验表明,试样延度超过标准要求。     

广州清洁燃料汽车发展方向

选择好合适的汽车替代燃料，科学确定一个地区清洁燃料汽车的发展方向，是减少机动车有害尾气排放、控制城市大气环境污染重大而紧迫的课题。国内外汽车清洁燃料的发展规律表明，天然气特别是液化天然气，是汽车替代燃料的最佳选择与发展方向。为此，探讨了随着天然气工业的加快发展，作为广州这样一座已经发展液化石油气汽车并已形成有一定规模的城市，如何适应新形势的需求，科学决策，选择符合国家能源发展政策并适应当地具体实际的汽车清洁燃料路线，寻求顺利实施液化石油气与天然气两种清洁燃料平稳过渡的具体措施。最后提出以下建议：加速LNG加气站和液化天然气汽车（LNGV）相关技术规范的制定；加快实现LNG关键设备，如LNG泵、LNG售气机、车用LNG储罐的国产化步伐，以降低LNGV和加气站的成本；鉴于LNGV改装技术的现状，不提倡对在用车进行改装，而应加大力度，逐步推广单燃料LNG汽车。     

催化精馏合成N-异丙基苯胺

在Joback基团贡献法估算反应的G ibbs函数的基础上,得到了异丙醇与苯胺合成N-异丙基苯胺的平衡常数与反应温度的关系式。研究了回流比、异丙醇与苯胺的摩尔比、塔釜操作温度、苯胺进料口位置距塔顶的距离对异丙醇与苯胺催化精馏合成N-异丙基苯胺的影响,确定了适宜的工艺条件:回流比2.5~3.5、异丙醇与苯胺的摩尔比1.5、塔釜操作温度223℃、苯胺进料口位置距塔顶300~400mm。在优化条件下,苯胺的转化率可达到99%,N-异丙基苯胺的选择性可达到99.5%,N-异丙基苯胺的质量分数可稳定在98.8%以上。     

H型丝光沸石催化剂催化甲苯与叔丁醇的烷基化反应

针对合成对叔丁基甲苯传统工艺中存在的缺点,采用环境友好、可重复利用的H型丝光沸石催化剂(以下简称催化剂)进行了甲苯与叔丁醇的烷基化反应,并用X射线衍射和氨程序升温脱附等方法对不同焙烧温度下得到的催化剂的物相结构和酸性质进行了表征,研究了各种反应条件对催化剂的催化性能的影响。实验结果发现,在适宜的操作条件下,即催化剂的焙烧温度823K、反应温度180℃、反应时间3h、初始压力1.0MPa、原料与催化剂的质量比为8、叔丁醇与甲苯的摩尔比为4、溶剂环己烷与甲苯的摩尔比为5时,甲苯转化率达42.73%,叔丁基甲苯的选择性为96.30%,对叔丁基甲苯的选择性为80.37%。     

Automatic image hanging protocol for chest radiographs in PACS.

Chest radiography is one of the most widely used techniques in diagnostic imaging. It comprises at least one-third of all diagnostic radiographic procedures in hospitals. However, in the picture archive and communication system, images are often stored with the projection and orientation unknown or mislabeled, which causes inefficiency for radiologists' interpretation. To address this problem, an automatic hanging protocol for chest radiographs is presented. The method targets the most effective region in a chest radiograph, and extracts a set of size-, rotation-, and translation-invariant features from it. Then, a well-trained classifier is used to recognize the projection. The orientation of the radiograph is later identified by locating the neck, heart, and abdomen positions in the radiographs. Initial experiments are performed on the radiographs collected from daily routine chest exams in hospitals and show promising results. Using the presented protocol, 98.2% of all cases could be hung correctly on projection view (without protocol, 62%), and 96.1% had correct orientation (without protocol, 75%). A workflow study on the protocol also demonstrates a significant improvement in efficiency for image display.     

On the Feasibility of Growing Pb[(Zn1/3Nb2/3)0.91Ti0.09]O3 Single Crystals

Pb[(Zn_1/3Nb_2/3)_0.91Ti_0.09]O₃ (PZNT91/9) single crystals were grown by two methods: from solution using PbO as a self‐fluxing agent (SC method) and directly from the melt without fluxing (MC method). In both growth methods, an allomeric Pb[(Mg_1/3‐Nb_2/3)_0.69Ti_0.31]O₃ (PMNT69/31) single crystal was used as a seed. X‐ray diffraction patterns of ground crystals showed that phase‐pure perovskite PZNT91/9 single crystals were successfully fabricated by the above two methods. The composition of the crystals obtained by both the SC and MC methods was analyzed using X‐ray fluorescence, which confirmed that the crystal composition is close to the nominal value, although volatilization of PbO and segregation during crystal growth are inevitable. The MC PZNT91/9 crystals exhibit excellent piezoelectric properties, with the piezoelectric constant, d₃₃, in the range of 1800–2200 pC N^–1. This value is comparable to that of the SC crystals. However, the MC crystals show an abnormal dielectric behavior. In contrast with the SC crystals, in the MC crystals a much broader dielectric peak appears in the dielectric response curves, accompanied by a much lower peak temperature of around 105 °C. Furthermore, frequency dispersion is apparent over a much wider temperature range (even more apparent than in pure relaxors), where a large, i.e., about 70 °C, full width at half maximum (FWHM) for the dielectric peaks is observed in the dielectric response. It is speculated that such an unusual phenomenon correlates with defects, microinhomogeneities, and polar regions in the as‐grown MC crystals. The origins of this abnormality have not been interpreted in detail until now. However, optical observation of the domain structure confirms that both the SC and MC crystals possess complex structural states.