Crack Stability and Its Effect on Fracture Toughness of Hot-Pressed Silicon Nitride Beam Specimens

The effect of stable crack extension on fracture toughness test results was determined using single-edge precracked beam specimens. Crack growth stability was examined theoretically for bars loaded in three-point bending under displacement control. The calculations took into account the stiffness of both the specimen and the loading system. The results indicated that the stiffness of the testing system played a major role in crack growth stability. Accordingly, a test system and specimen dimensions were selected which would result in unstable or stable crack extension during the fracture toughness test, depending on the exact test conditions. Hot-pressed silicon nitride bend bars (NC132) were prepared with precracks of different lengths, resulting in specimens with different stiffnesses. The specimens with the shorter precracks and thus higher stiffness broke without stable crack extension, while those with longer cracks, and lower stiffness, broke after some stable crack extension. The fracture toughness values from the unstable tests were 10% higher than those from the stable tests. This difference, albeit small, is systematic and is not considered to be due to material or specimen-to-specimen variation. It is concluded that instability due to the stiffness of test system and specimen must be minimized to ensure some stable crack extension in a fracture toughness test of brittle materials in order to avoid inflated fracture toughness values.     

Computer-Aided Design of Corn Dryers With Quality Prediction

A new dynamic model of corn drying based on compartmental structure and quality prediction was built up from a thin layer model to industrial scale. From the system analysis to the programming, we focus mainly on numerical resolution of the equations and on the ergonomy of the software.     

Characterization of Dip-Coated Boron Nitride on Silicon Carbide Fibers

Amorphous boron nitride thin coatings (∼0.2 μm) have been formed on Nicalon and C-Nicaion (pre-carbon-coated Nicalon) yarns via dip coating in boric acid solution followed by heating and nitriding in NH₃gas at 1000°C. X-ray photoelectron spectroscopy (XPS) and Auger electron spec-troscopy (AES) studies have shown the formation of boron nitride. The coating was boron rich and contains oxygen. The N/B and O/B ratios range from 0.6 to 0.8 and from 0.1 to 0.25, respectively. Tensile strength measurements revealed that the BN-coated C-Nicalon yarn maintained ∼85% of its original strength while BN-coated Nicalon lost ∼85% of its original strength. Auger depth profiles showed that there was a consumption of carbon during the heating and nitridation process for both BN-coated Nicalon and C-Nicalon fibers. However, the depletion of carbon in BN-coated Nicalon fibers was much more severe than that in BN-coated C-Nicalon fibers.     

Offset dual-disk dielectric resonator antenna of very highpermittivity

An aperture-coupled offset dual-disk dielectric resonator antenna of very high permittivity is investigated experimentally. It is found that the new configuration offers an impedance bandwidth 4.6 times wider than that of the single element. The voltage standing wave ratio, radiation patterns, and antenna gain of the configuration are studied     

Fugitive Diffusion Barrier for Integration of Sol-Gel-Derived Lead Titanate with Oxidized Silicon Substrates

The crystalline phase development and microstructural changes with heating of sol-gel-derived lead titanate (PT) particles and films on silica with and without a fugitive (or removable) diffusion barrier layer were investigated. Amorphous gel-derived PT particles were deposited on SiO₂-coated TEM grids with and without polyimide (PI) or carbon barrier layers between SiO₂ and PT. TEM analysis showed that PI or carbon barriers prevented reaction between the gel-derived PT particles and SiO₂. PT particles crystallize and then the PI or carbon film decomposes. Sol-gel-derived PT films were deposited on oxidized Si substrates (Si/SiO₂) with and without a PI barrier layer. Perovskite PT films were prepared on Si/SiO₂ substrates with a PI barrier; however, some porosity remained in the films. Identically prepared films without the PI barrier formed a mixture of pyrochlore and perovskite. X-ray photoelectron spectroscopy results indicate that the PI film pre- vents the diffusion of Si into the PT film.     

A Generic Pigment Model for Digital Painting

We propose a generic pigment model suitable for digital painting in a wide range of genres including traditional Chinese painting and water-based painting. The model embodies a simulation of the pigment-water solution and its interaction with the brush and the paper at the level of pigment particles; such a level of detail is needed for achieving highly intricate effects by the artist. The simulation covers pigment diffusion and sorption processes at the paper surface, and aspects of pigment particle deposition on the paper. We follow rules and formulations from quantitative studies of adsorption and diffusion processes in surface chemistry and the textile industry. The result is a pigment model that spans a continuum from the very wet to the very dry brush stroke effects. We also propose a new pigment mixing method based on machine learning techniques to emulate pigment mixing in real life as well as to support the creation of new artificial pigments. To experiment with the proposed model, we embedded the model in a sophisticated digital brush system. The combined system exhibits interactive speed on a modest PC platform. http://www.cs.hku.hk/~songhua/pigment provides supplementary materials for this paper.     

Risk factors for osteoporosis in men

Three months after the launch of the MMR programme in the United Kingdom and the Republic of Ireland, a postal questionnaire was sent to all GP scheme trainees in both Northern Ireland and the Republic of Ireland. The response rate was 81%. All trainees were enthusiastic about promoting MMR immunisation; with 27% favouring compulsory immunisation. 9% had never seen a patient with measles. This did not alter their attitude towards the beneficial effects of MMR immunisation. Of pre-practice year trainees 26% felt their level of knowledge of immunisation was inadequate, 59% claimed to have received no education on immunisation during their vocational training to date. This may reflects deficiencies in their medical curriculum to-date. 95% of third-year trainees indicated that their practice experience had been the source of at least some of their education on immunisation. Only 46% of trainees in the Republic of Ireland were aware of their Department of Health's aims in launching the MMR immunisation campaign.     

Rheological Property and Stress Development during Drying of Tape-Cast Ceramic Layers

Rheological property and stress development of tape-cast ceramic layers derived from nonaqueous alumina (A1₂O₃)-poly(vinyl butyral) (PVB) suspensions were observed during drying. Casting suspensions exhibited strong shear-thinning behavior, with a low shear Newtonian plateau apparent viscosity >10² Pa^.s. The apparent suspension viscosity displayed a power-law dependence on the A1₂O₃ volume fraction during the initial stage of drying (<30% solvent loss). Stress development, measured by a cantilever deflection method, and parallel weight loss measurements were performed during the drying of tape-cast layers and pure binder coatings. Maximum drying stresses (σ_max) of 1.37-0.77 MPa were observed for plasticized tapes cast at gap heights of 150-400 μm. In contrast, nonplasticized tapes of similar thickness displayed a more gradual stress increase, with σ_max values approximately an order of magnitude higher than their plasticized counterparts. The stress histories of the corresponding binder coatings were quite similar to the tape-cast layers, albeit slightly lower σ _max values were observed. Stresses decayed beyond σ_max with a logarithmic time dependence to an almost constant value of 0.2-0.4 MPa for the plasticized tapes. Based on these observations, process methodologies have been offered to minimize stress development and retention in tape-cast ceramic layers     

Practice characteristics that lead to 21st century learning outcomes

Abstract The key research question for this study was to ask whether or not innovative teaching practices would lead to the development of learning outcomes essential for preparing the younger generation for the challenges of life in the knowledge society of the 21st century, and if so, how are the pedagogical features related to the different learning outcomes. Preliminary analyses of the case study data collected from the SITES M2 Study in Hong Kong reveal that where the development of more significant learning gains were observed, the cases possess characteristics additional to the criteria defined in the Study for selection of innovation. More importantly, it was found that the impact of the pedagogical practices was not determined simply by the aggregation of characteristics of the practices per se , nor on the technologies used, but on whether 'empowerment' permeates the curriculum goal and process. Further, this paper claims that these affective and socio-cognitive learning outcomes are more important as preparation for lifelong learning in the 21st century than 'knowledge management competencies'.