板材在弯曲过程中存在的最突出的问题是弯曲回弹难以精确控制.弯曲卸载后产生的回弹,使弯曲件的形状和尺寸与模具工作部分的形状和尺寸不符.弯曲件的最后形状与整个变形过程有关,模具几何参数、材料性能参数等都会对回弹产生很大影响.在板材弯曲成形智能化控制系统中,准确确定实时识别和预测模型的输入、输出参数是弯曲智能化控制的成功与否以及回弹控制精度高低的关键.本文采用Ls-dyna软件,对U形件弯曲影响回弹的因素进行了分析,得出了影响回弹规律的主要因素.为U形件弯曲智能化控制神经网络参数识别及预测模型输入、输出参数的选择提供依据.     

球磨对ZrO2（Y2O3）超细粉末性能的影响

以共沉淀法制备煅烧态ＺｒＯ２（Ｙ２Ｏ３）超细粉末为研究对象，研究了球磨对其物理和烧结性能的影响，结果表明，球磨虽可以有效地减小粉末的团聚尺寸，但对粉末一次颗粒尺寸的的影响不大，球磨可以显著增加团聚程度较严重的锻烧态粉末的比表面积，但对团聚程度较轻的粉末，其影响大：球磨还可显著减小粉末的晶粒尺寸，这与粉末在球磨过程中发生了相变有关。此外，对团聚较严重的粉末，球磨可改善其烧结性能，但对团聚程度较轻的粉     

高温W/Re流口复合界面上的扩散层

W/Re流口在高温下使用时,复合界面处会发生反应扩散而形成一个由固溶体(W),双相σ,双相x,固溶体(Re)4个相组成的过渡层。并作出了不同反应扩散时间的浓度分布曲线,及浓度突变形成的双相区,从而确定了各相成份组成。对经反应扩散后的复合界面进行微观观察发现x相、σ相内有许多间隔式微裂纹,据此认为高温下W/Re流口失效原因是使用过程中上述两x,σ相内裂纹扩散,熔体渗入所致。     

Effects of temperature and blank holding force on biaxial forming behavior of aluminum sheet alloys

Biaxial forming behavior is investigated for three aluminum sheet alloys (Al 5182 containing 1% Mn (5182+Mn), Al 5754, and 6111-T4) using a heated die and punch in the warm forming temperature range of 200–350 °C. It is found that, while all three alloys exhibit significant improvement in their formability compared with that at room temperature, the non-heat-treatable alloys 5182 + Mn and 5754 give higher part depths than that of heat-treatable 6111-T4. The formability generally increases with decreasing BHP (BHP), but increasing the forming temperature and/or BHP minimizes the wrinkling tendency and improves the forming performance. The stretchability of the sheet alloys increase with increasing temperature and increasing BHP. For the alloys and forming conditions involved in the current study, the formability, measured in terms of part depth, comes mainly from the drawing of metal into the die cavity, although stretching effects do influence the overall forming behavior. The optimum formability is achieved by setting the die temperature 50 °C higher than the punch temperature to enhance the drawing component. Setting the die temperature higher than the punch temperature also improves the strain distribution in a part in such a manner that postpones necking and fracture by altering the location of greatest thinning.     

Development of microstructure and mechanical properties of a Ni-base single-crystal superalloy by hot-isostatic pressing

Effects of the hot-isostatic pressing (HIP) process on microstructures and mechanical properties of Ni-base single crystal superalloy CMSX-4 were investigated. In the overall heat treatment process, the HIP treatment remarkably induced the healing behavior of micropores and decreased the pore size and porosity of superalloy CMSX-4 compared with normally treated specimens. The microstructure of γ′ phase after the HIP process showed rather a coarsening tendency and could be developed by the partially solution and aging treatment. Consequently, the elimination of cast micropores using the HIP step resulted in the inhibition of crack initiation in microstructure and improved the stress-rupture lives of Ni-base single crystal superalloy by 185%.     

Effects of phosphorus addition on the magnetic properties of sintered Fe-50 wt.% Ni alloys

Phosphorus was added to Fe-50 wt.% Ni in the form of a coated composite powder via an electroless plating process. Addition of phosphorus to Fe-50 wt.% Ni facilitated increases in density and grain size, both of which were beneficial to magnetic performance. Because of the homogeneous distribution of phosphorus in the powder, the optimal phosphorus addition was much lower than for those using Fe₃P as the phosphorus precursor. The optimal phosphorus addition was close to its maximum solubility in Fe-50 wt.% Ni (about 0.5 wt.%), above which precipitation of excessive phosphorus in the form of iron nickel phosphide, (Fe,Ni)₃P, effectively degraded the magnetic properties of Fe-50 wt.% Ni. Without the addition of phosphorus, good magnetic properties could be achieved only when the sintering temperature was high enough (>1200 °C) to result in a high sintered density and large grains in the sintered structure.     

稀盐酸中锰结核还原浸出溶液净化除铁

针对酸性氯化物中黄铁矿还原浸出锰结核的溶液成分特点，选择黄钠铁矾法进行了沉淀分离铁的研究。结果表明温度和晶种以及溶液ｐＨ值是影响铁矾沉淀的重要因素。在ｐＨ２．０左右，溶液温度高于９０℃，足量晶种加入的情形下，１５０ｍｉｎ后可将溶液中的铁含量降至０．１ｇ／Ｌ。沉矾过程的表观活化能为９４．６６ｋＪ／ｍｏｌ。黄铁矿氧化生成的硫酸根随铁一同沉淀，从而消除了ＳＯ２－４在氯化物体系中的积累。     

EFFECT OF STRENGTH ON CORROSION FATIGUE BEHAVIOUR OF LOW ALLOY STEELS IN ARTIFICIAL SEAWATER

本文应用断裂力学及电化学等方法,研究了通过不同回火温度处理具有不同强度水平的34CrNi3Mo和40CrNiMo钢在人造海水中的腐蚀疲劳(CF)和应力腐蚀开裂(SCC)行为。试验结果表明,钢的强度对CF和SCC行为有着强烈的作用。随着钢屈服强度σ_s的提高,钢在海水中的SCC敏感性增大,腐蚀疲劳裂纹扩展速率dα/dN剧增。低合金钢在海水环境中的CF行为与SCC行为密切相关,而在CF条件下可促进钢的SCC敏感性。     

Numerically optimal design for the system with coupled complex transport phenomena-application to the Submerged Entry<Emphasis Type="Italic">Nozzle</Emphasis> in continuous slab caster

This study presents a simple and robust algorithm for the optimal design of the system with coupled complex transport phenomena: the transport phenomena comprise fluid flow, heat and mass transfer. The (1+1)-Evolution Strategy method is adopted as the optimization method. In order to analyze the transport phenomena in the complex geometry generated during the optimization procedure, thefinite volume method with a boundary fitted curvilinear coordinate system is used. To confirm the validity of the present method, the optimal design for the inner shape of the simplified two-dimensionalSubmerged Entry Nozzle in the continuous slab caster is conducted. It is shown that the resulting design of the nozzle is consistent with the purpose and constraints of the design.     

现代化中厚板热处理机组及其使用效果

介绍了引进的辐射加热无氧化辊式热处理炉及连续辊式淬火机，有效地解决了钢板的表面质量问题，取得了满意的效果．