A 62-ns 16-Mb CMOS EPROM with voltage stress relaxation technique

To meet the increasing demand for higher-density and faster EPROMs, a 16-Mb CMOS EPROM has been developed based on 0.6-μm N-well CMOS technology. In scaled EPROMs, it is important to guarantee device reliability under high-voltage operation during programming. By employing internal programming-voltage reduction and new stress relaxation circuits, it is possible to keep an external programming voltage V_pp of 12.5 V. The device achieves a 62-ns access time with a 12-mA operating current. A sense-line equalization and data-out latching scheme, made possible by address transition detection (ATD), and a bit-line bias circuit with two types of depletion load led to the fast access time with high noise immunity. This 16-Mb EPROM has pin compatibility with a standard 16-Mb mask-programmable ROM (MROM) and is operative in either word-wide or byte-wide READ mode. Cell size and chip size are 2.2 μm×1.75 μm and 7.18 mm×17.39 mm, respectively     

Organic field-effect transistors based on J-aggregate thin films of a bisazomethine dye

We report on the fabrication and the characterization of p-type organic field-effect transistors based on vapor-deposited J-aggregate bisazomethine dye thin films. The absorption spectra of this non-ionic organic semiconductor in the solid state show a strong influence of the film thickness on the J-aggregate formation. However, the electrical characteristics of the devices demonstrate that the hole transport properties do not vary significantly in films thicker than 100 nm. This is due to the fact that the J-aggregates are formed in this material at the surface of the crystalline grains and do not influence the semiconductor/gate dielectric interface and the charge transport properties of the devices. Hole field-effect mobilities as high as 2.4 × 10^?4 cm² V^?1 s^?1 were obtained and could be slightly improved by a solvent vapor treatment due to changes in the film crystallinity. Overall, this study demonstrates that J-aggregate bisazomethine dye thin films are good candidates for the realization of organic electronic devices.     

Rainfall propagation impairments for medium elevation angle satellite‐to‐earth 12 GHz in the tropics

Rain attenuation is the dominant propagation impairment for satellite communication systems operating at frequencies above about 10 GHz. The rainfall path attenuation at 12.255 GHz measured at Universiti Sains Malaysia (USM) for 4 years (2 January to 5 December) is presented. This paper presents an empirical analysis of rain rate and rain attenuation cumulative distribution functions obtained using 1‐min integrated rainfall data and comparison of the measured data with data obtained from well‐established rain model attenuation predictions. Copyright © 2008 John Wiley & Sons, Ltd.     

Optical 40-gb/s 3R regenerator with a combination of the SPM and XAM effects for all-optical networks

An all-optical 3R regenerator with a combination of self-phase modulation (SPM) and cross-absorption modulation (XAM) effects is proposed and investigated. Principle performances of the proposed all-optical 3R regenerator were experimentally investigated at a signal bit rate of 40 Gb/s. The all-optical 3R regenerator, which is located at the midpoint of a 1080-km transmission line, successfully provided an approximately 3-dB improvement of the Q-factor both just after regeneration and after totally 1080-km transmission. The chromatic dispersion tolerance of the proposed 3R regenerator was also investigated and successfully enhanced to about twice as wide by introducing a predistortion block configuration including a highly nonlinear fiber (HNLF). It was confirmed that the proposed all-optical 3R regenerator can become one of the strong candidates for the actual deployment of the all-optical network.     

Uncooled 25 Gbit/s direct modulation of semi-insulating buried-heterostructure 1.3 μm AlGaInAs quantum-well DFB lasers

Uncooled 25 Gbit/s direct modulation of 1.3 mum DFB lasers is demonstrated. The 150 mum-long semi-insulating buried-heterostructure AIGalnAs quantum-well DFB lasers show clear eye-openings with dynamic extinction ratio of 5 dB up to 70degC. 13 km singlemode-fibre transmission experiments using the devices show low power penalty within 1.3 dB between 25 and 70degC. These characteristics are the first achievement by 1.3 mum directly modulated lasers.     

HVEM study of crack-tip dislocations in Si crystals prepared by FIB and twin-blade cutting method

Crack-tip dislocations in silicon crystals have been examined by using high-voltage electron microscopy. Cracks were introduced by the Vickers indentation method at room temperature and the indented specimens were annealed at high temperatures to induce dislocations around crack tips under the presence of residual stress due to the indentation. A selected area around a crack tip was thinned by a focused ion beam (FIB) technique. Specimens were thinned in advance by a twin-blade cutting (TBC) method, which is a simple cutting process for saving FIB machine time. A combination of FIB and TBC can be a useful thinning procedure for the efficient preparation of transmission electron microscopy specimens. Characteristic dislocation structures were observed around the tip of a crack, aiding the elucidation of dislocation processes, which is essential to increase the fracture toughness of materials.     

Information geometry of turbo and low-density parity-check codes

Since the proposal of turbo codes in 1993, many studies have appeared on this simple and new type of codes which give a powerful and practical performance of error correction. Although experimental results strongly support the efficacy of turbo codes, further theoretical analysis is necessary, which is not straightforward. It is pointed out that the iterative decoding algorithm of turbo codes shares essentially similar ideas with low-density parity-check (LDPC) codes, with Pearl's belief propagation algorithm applied to a cyclic belief diagram, and with the Bethe approximation in statistical physics. Therefore, the analysis of the turbo decoding algorithm will reveal the mystery of those similar iterative methods. In this paper, we recapture and extend the geometrical framework initiated by Richardson to the information geometrical framework of dual affine connections, focusing on both of the turbo and LDPC decoding algorithms. The framework helps our intuitive understanding of the algorithms and opens a new prospect of further analysis. We reveal some properties of these codes in the proposed framework, including the stability and error analysis. Based on the error analysis, we finally propose a correction term for improving the approximation.     

Topic allocation method on edge servers for latency-sensitive notification service

The importance of real-time notification has been growing for social services and Intelligent Transporting System (ITS). As an advanced version of Pub/Sub systems, publish-process-subscribe systems, where published messages are spooled and processed on edge servers, have been proposed to achieve data-driven intelligent notifications. In this paper, we present a system that allows a topic to be managed on multiple edge servers so that messages are processed near the publishers, even when publishers spread over a wide area. Duplicating messages on geographically distributed servers could enable immediate notification to neighboring subscribers. However, the duplicated message spool may cause exhaustion of resources. We prepare a formal model of our publish-process-subscribe system and formulate the topic allocation as an optimization problem under the resource constraints of edge servers. As the optimization problem is NP-hard, we propose heuristics leveraging the locality and the pub/sub relationships observed between clients to use the edge server resources efficiently. Our performance evaluation shows that our method reduces the delay to deliver notifications and the effectiveness of the strategy exploiting the relationships between clients.     

Oxygen doped Ge crystals Czochralski-grown from the B2O3-fully-covered melt

Local vibrations of oxygen in Ge crystals grown from a melt fully covered by B₂O₃ were evaluated by Fourier-transform infrared spectroscopy. Ge single crystals containing oxygen were grown by the Czochralski method under various growth conditions. Oxygen concentrations in the crystals were determined to be in the range between 8.5 × 10¹⁵ and 5.5 × 10¹⁷ cm⁻³ from the infrared absorption at 855 cm⁻¹ originating in local vibration of Ge-O_i-Ge quasi-molecules. Absorption peaks relating to GeO_x, SiO_x and Si-O_i-Si were not detected in the as-grown crystals. The calibration coefficient for determining oxygen concentration in Ge crystals from the absorption peak intensity at 1264 cm⁻¹ was estimated to be 1.15 × 10¹⁹ cm⁻².     

Fabrication of (Pb,La)(Zr,Ti)O/sub 3/ thin-film arrayed waveguide grating

The design and fabrication of an 8-ch, 500 GHz-spacing arrayed waveguide grating on (Pb,La)(Zr,Ti)O₃ has been successfully achieved for the first time. An insertion loss of 22.1 dB, including a 10 dB coupling loss, and an adjacent crosstalk of -23.1 dB have been obtained. The device is expected to be monolithically integrated into high-speed optical switches to form integrated chips such as a reconfigurable add-drop multiplexer