Breakdown Trade-Off Relation of Mechanical Properties via Micro-alloying in Mg–Mn Alloys

The impact of micro-alloying on tensile behavior at strain rates in various ranges is examined using five types of extruded Mg-0.3 at. pct Mn–0.1 at. pct X ternary alloys, where X is selected as a common element, Al, Li, Sn, Y or Zn. Microstructural observations reveal that the average grain size of these extruded alloys is between 1 and 3 μm, and these micro-alloying elements segregate at grain boundaries. In room temperature tensile and compression tests, these results show that the mechanical properties and deformation behavior are influenced by the micro-alloying element, even as a small addition of 0.1 at. pct. Mg–Mn–Y and Mg–Mn-Zn alloys show higher strength and smaller strain rate sensitivity (m-value) among the present alloys, owing to the rate-controlling mechanism as dislocation slip. On the other hand, the Mg–Mn–Li alloy exhibits the largest elongation to failure in tension and the highest strain rate sensitivity, associated with high contribution of grain boundary sliding to deformation. These differences are due to the grain boundary segregation of the micro-alloying elements. Compared to the common Mg alloys, the present ternary alloys also show a trade-off relationship between strength and ductility, which is similar to that of the well-known Mg alloys; however, these properties of the Mg–Mn system ternary alloys could be controlled via the type of micro-alloying elements with a chemical content of 0.1 at. pct.

     

An XPS study of passive films on Nickel and alloy 600 in acids

Compositions of surface films formed on nickel and Alloy 600 in I M HCI, 0.5 M H₂SO₄ and I/3 M H₃PO₁ solutions were investigated as a function of polarization potential. The main constituent of surface films formed on Ni in 0.5 M H₂SO₄ or 1/3 M H₃PO₄ solution was hydrated nickel oxyhydroxide, in which the ratio of O₂ to OH⁻ increased when passivation occurred. The surface films formed on Ni and Alloy 600 at lower potentials in 0.5 M H₂SO₄ solution contain S² ions other than SOP_4²⁻ ions, whereas S²⁻ ions were not incorporated in the passive film. Passivation of Alloy 600 took place by the formation of hydrated chromium oxyhydroxide. Pitting led to no substantial change in the average composition of the film.     

Importance of initial surface film in the degradation of stainless steels by atmospheric exposure

The surface compositions of stainless steels types 304, 316, 430, and 444 combined with four types of surface finishes, 2B finish, hairline polishing, mirror polishing, and bright annealing, were measured by ICP-AES, EPMA, and XPS before exposure. The surface finish that most enriched the chromic species in the surface film was mirror polishing, followed by bright annealing, 2B finish, and hairline polishing. The order of corrosion-resistance was type 444, type 316, type 304, and type 430. The surface compositions were correlated with the rating number and pitting depth after exposure to atmospheric environments. The rating number had a high positive correlation with the concentration of Cr in the surface film, and had a slight correlation with the near-surface composition measured by EPMA at 12 kV, but did not show any correlation with bulk composition within the composition range covered in the present work. This same trend was observed for pitting depth. It was concluded that the cationic concentration of Cr in the surface film before atmospheric exposure is the prime factor in controlling the resistance of stainless steels to atmospheric corrosion.     

Laser-Sintered Barium Titanate

Laser sintering of alkoxy-derived ultrafine BaTiO₃ powders was investigated. The temperature increases of the sample with laser irradiation were measured with a thermocouple. It was found that laser irradiation could generate enough heat to sinter ceramics. A slurry was prepared by mixing an alkoxy-derived BaTiO₃ powder, binder additives, solvent, and plasticizer. The slurry was tape cast and dried to give a green sheet. The green sheet was laser sintered and was then characterized by SEM, XRD, and density measurements. The effect of burnout before laser irradiation and the characteristic microstructure of laser-sintered BaTiO₃ are described.     

Effect of the Chiral Center Position of an Optically Active Terminal Group on the Induction of Optical Activity in Polysilanes

Summary Polysilanes with an optically active alkoxy group, i.e., (S)-(+)-2-butoxy, (R)-(-)-2-butoxy, (S)-(-)-2-methyl-1-butoxy, and (S)-(+)-3,7-dimethyl-1-octoxy, at the terminal positions, the chiral carbon centers of which were located at the α, β, and γ positions relative to the oxygen, respectively, were prepared, and the effect of the position of chiral center of the terminal optically active group on the induction of optical activity in polysilanes was investigated. The circular dichroism (CD) spectra of these polymers showed positive Cotton signals around 340 nm at temperatures below -20 °C, but the intensities were small, indicating that the optically active groups at the terminal positions have some ability, albeit small, to induce optical activity to the polysilanes. Further, the optically active (S)-(+)-2-butoxy and (R)-(-)-2-butoxy groups did not control the helical sense direction of the polymers, despite the different chiral stimuli from the 2-butoxy groups introduced to the terminal positions. To control the helical structure of polysilanes by the use of optically active terminal groups, appropriate optically active groups are required.     

Studies on the nuclear magnetic resonance spectra of olefinic protons of conjugated fatty acid methyl esters

The NMR spectra of olefinic protons in the four representative conjugated fatty acid methyl esters, methylcis-9,trans-11-octadecadienoate, methyltrans-9,trans-11-octadecadienoate, methyl α eleostearate, and methyl β eleostearate, were studied. The chemical shift of each olefinic proton in these compounds was determined by considering their intramolecular environment. Coupling constants were also obtained as the results of spectral analysis.     

Highly Transparent Lu-α-SiAlON

Novel Lu-α-SiAlON ceramics were produced by hot pressing mixtures of Si₃N₄, Lu₂O₃, AlN, and Al₂O₃ at 1950°C for 2 h in a nitrogen atmosphere. The resultant SiAlON was fully dense and possessed a uniform, equiaxed microstructure with a grain size of ∼1 μm, which resulted in a high hardness of >19 GPa. In addition to high hardness, the sample showed very high optical transparency in the visible light region, with >70% transmission at higher wavelengths. This high transparency was attributed to the uniform, dense microstructure and lack of residual grain-boundary phase.     

Fate of the chlorine and fluorine in a sub-bituminous coal during pyrolysis and gasification

The fate of the chlorine and fluorine present in a sub-bituminous coal from Indonesia during pyrolysis and gasification has been studied with fixed and entrained bed reactors. The rate profile for HCl evolved in the temperature programmed pyrolysis exhibits the main and shoulder peaks at 480 and 600 °C, respectively. Model experiments and subsequent Cl 2p XPS measurements show that HCl reacts with metal impurities and carbon active sites at 500 °C to be retained as inorganic and organic chlorine forms, from which HCl evolves again at elevated temperatures. It is suggested that the HCl observed in the coal pyrolysis may originate from the above-mentioned chlorine functionalities formed by secondary reactions involving the nascent char. In the CO₂ gasification of the 900 °C char at 1000 °C and 2.5 MPa, any measurable amounts of HCl and HF could not be detected even at a high conversion of 75 wt% (daf), suggesting the accumulation of these halogens in the residual char. When the coal is injected into an O₂-blown, entrained bed gasifier at 1200-1400 °C under 2.6 MPa, the partial oxidation proceeds to a larger extent at a higher O₂/coal ratio, whereas the chlorine and fluorine are enriched in the remaining char, and the extent of the enrichment at the latter stage of gasification is larger with the fluorine. The XPS measurements of the chars reveal the presence of the broad F 1 s peak, which can cover a wide range of binding energies attributable to inorganic and organic fluorine. The halogen enrichment during gasification is discussed in terms of secondary reactions of HCl and HF with char.     

Fracture Energies of Tape-Cast Silicon Nitride with β-Si3N4 Seed Addition

The fracture energies of the tape-cast silicon nitride with and without 3 wt% rod-like β-Si₃N₄ seed addition were investigated by a chevron-notched-beam technique. The material was doped with Lu₂O₃–SiO₂ as sintering additives for giving rigid grain boundaries and good heat resistance. The seeded and tape-cast silicon nitride has anisotropic microstructure, where the fibrous grains grown from seeds were preferentially aligned parallel to the casting direction. When a stress was applied parallel to the fibrous grain alignment direction, the strength measured at 1500°C was 738 MPa, which was almost the same as room temperature strength 739 MPa. The fracture energy of the tape-cast Si₃N₄ without seed addition was 109 and 454 J/m² at room temperature and 1500°C, respectively. On the contrary, the fracture energy of the seeded and tape-cast Si₃N₄ was 301 and 781 J/m² at room temperature and 1500°C, respectively, when a stress was applied parallel to the fibrous gain alignment. The large fracture energies were attributable primarily to the unidirectional alignment fibrous Si₃N₄ grains.     

Physical properties of silk fibers treated with ethylene glycol diglycidyl ether by the pad/batch method

This paper deals with the epoxide treatment of silk fabrics by the pad/batch method. The optimum reaction conditions, i.e., NaOH concentration, and reaction temperature were 2.5 g/L and 30°C, respectively. A weight gain of 8.5% was attained at a reaction time of 6 h. This value slightly increased to 10% after 24 h. The reactivity of tyrosine and basic amino acid residues was dependent on the reaction time and did not significantly differ from the results of epoxide-treated silk fiber by the conventional method in tetrachloroethylene. The moisture regain slightly decreased at 4% weight gain and then increased with the epoxide content, exceeding the value of the untreated control. The crease recovery of the epoxide-treated silk fabrics measured in the wet state was significantly improved, whereas that in the dry state was almost unchanged. The rate of photoyellowing of the epoxide-treated silk fabrics by the pad/batch method was reduced significantly compared with that of the untreated control. Among the mechanical properties, elongation at break and tensile modulus remained unchanged, whereas the tensile strength slightly increased following the epoxide reaction. The thermal properties were evaluated by DSC and TGA and on the basis of the dynamic viscoelastic measurements. The DSC curve of the epoxide-treated sample showed a slight increase of the decomposition temperature of silk fibroin. The rate of weight loss determined by TGA remained unchanged regardless of the chemical modification, whereas the peak of loss modulus became broader and shifted to lower temperature. The X-ray diffractograms showed that the crystalline structure of silk fibers was not affected by the reaction with epoxides. © 1993 John Wiley & Sons, Inc.