Gaseous and dissolved concentrations of polychlorinated biphenyls (PCBs) and hexachlorobenzene (HCB) were measured in the ambient air and water of Kaohsiung Harbor lagoon, Taiwan, from December 2003 to January 2005. During the rainy season (April to September), gaseous PCB and HCB concentrations were low due to both scavenging by precipitation and dilution by prevailing southwesterly winds blown from the atmosphere of the South China Sea. In contrast, trace precipitation and prevailing northeasterly winds during the dry season (October to March) resulted in higher gaseous PCB and HCB concentrations. Instantaneous air-water exchange fluxes of PCB homologues and HCB were calculated from 22 pairs of air and water samples from Kaohsiung Harbor lagoon. All net fluxes of PCB homologues and HCB in this study are from water to air (net volatilization). The highest net volatile flux observed was + 172 ng m^− 2 day^− 1 (dichlorobiphenyls) in December, 2003 due to the high wind speed and high dissolved concentration. The PCB homologues and HCB fluxes were significantly governed by dissolved concentrations in Kaohsiung Harbor lagoon. For low molecular weight PCBs (LMW PCBs), their fluxes were also significantly correlated with wind speed. The net PCB and HCB fluxes suggest that the annual sums of 69 PCBs and HCB measured in this study were mainly volatile (57.4 × 10³ and 28.3 × 10³ ng m^− 2 yr^− 1, respectively) and estimated yearly, 1.5 kg and 0.76 kg of PCBs and HCB were emitted from the harbor lagoon surface waters to the ambient atmosphere. The average tPCB flux in this study was about one-tenth of tPCB fluxes seen in New York Harbor and in the Delaware River, which are reported to be greatly impacted by PCBs.     

Effect of iron content on the distribution of zinc between copper and matte

The distribution coefficients of zinc between copper and matte phase containing iron have been measured at 1400°K and 1500°K. In a dilute solution, activity ZnS shows negative deviation from Raoult’s Law. At 1500°K activity of ZnS can be approximated by Tempkin’s model. Distribution coefficient of zinc, L_zn, increased with increasing iron and decreasing zinc contents at both temperatures. Activity coefficient of ZnS for an iron bearing matte may be expressed by log $\gamma _{ZnS(1)} = - \frac{{297}}{T} - 0.153 + 0.65{\text{ }}$ N_FeS for 1400°K < T < 1500°K, 0 < N_ZnS < 0.04 and 0 < N_FeS <     

Findings of the International Road Tunnel Fire Detection Research Project

Fire detection systems play a crucial role in ensuring safe evacuation and firefighting operations in road tunnels, but information on the performance of these systems in tunnels has been limited and guidelines for their application in tunnel environments are not fully developed. Recently, the National Research Council of Canada (NRC) and the Fire Protection Research Foundation completed a 2-year international research project, with the support of private- and public-sector organizations, to determine some of the strengths and weaknesses of the various types of fire detection systems and the factors that can affect their performance in tunnel environments. The project included both laboratory and field fire tests combined with computer modeling studies. Although this research was conducted on road tunnels, the findings should apply to other tunnels, such as those used in subway systems. As part of the project, the NRC conducted two series of tests in the Carleton University-NRC tunnel facility to investigate the performance of detection systems under minimal and longitudinal airflow conditions. In addition, NRC conducted tests in the Carré-Viger Tunnel in Montréal, as well as a computer modeling study. The project studied nine fire detection systems that covered five types of currently available technologies. The performance of the detection systems, including response times and ability to locate and monitor a fire in the tunnel and the effect of the tunnel environment, were evaluated under the same conditions. This article provides an overview of the findings of the project. Fire detectors, fire scenarios and test protocols used in the test program are described. A summary of the research results of the full-scale fire tests conducted in a laboratory tunnel facility and in an operating road tunnel as well as of the computer modeling activities is reported.     

Norovirus and MS2 inactivation kinetics of UV-A and UV-B with and without TiO2

Germicidal ultraviolet, such as 254-nm UV-C, is a common method of disinfection of pathogenic enteric viruses. However, the disinfection efficacies of UV-A or -B in terms of inactivating waterborne viruses such as norovirus have not been characterized. We evaluated the inactivation kinetics of MS2 bacteriophage and murine norovirus (MNV), a surrogate of human norovirus (NoV), by UV-A and -B. In addition to UV disinfection, we further investigated whether the presence of TiO₂ could enhance the virus inactivation kinetics of UV-A and -B. Both MS2 and MNV were highly resistant to UV-A. However, the addition of TiO₂ enhanced the efficacy of UV-A for inactivating these viruses. UV-A dose of 1379 mJ/cm² resulted in a 4 log₁₀ reduction. In comparison, UV-B alone effectively inactivated both MS2 and MNV, as evidenced by the 4 log₁₀ reduction by 367 mJ/cm² of UV-B. The addition of TiO₂ increased the inactivation of MS2; however, it did not significantly increase the efficacy of UV-B disinfection for inactivating MNV. When these treatments were applied to field water such as groundwater, the results were generally consistent with the laboratory findings. Our results clearly indicated that UV-B is useful for the disinfection of waterborne norovirus. However, MNV was quite resistant to UV-A, and UV-A effectively inactivated the tested viruses only when used in combination with TiO₂.     

Biodegradation of phenol by Synechocystis sp. in media including triacontanol hormone

Phenol removal levels of Synechocystis sp. were investigated in BG11 media with 10 mg/L triacontanol (TRIA) and without it to test whether the hormone could increase the removal efficiency by increasing biomass. The assays were performed to determine the effect of light on degradation, in media with 119.0–492.8 mg/L phenol under light and dark conditions. At increasing phenol concentrations, the degradation ranged between 98.5 and 100% regardless of a dark or a light condition. Experiments were carried out under light to determine the optimum pH for effective degradation. Optimum pH was found to be 6.5 at 200 mg/L phenol with or without TRIA. Phenol degradation was investigated in the 120.2–826.9 mg/L range. Although 377.4 mg/L phenol was completely degraded in hormone controls within 120 h, degradation was increased by TRIA, and the process was completed in 96 h. These data suggest that Synechocystis sp. has potential for use in the treatment of wastewaters containing phenol.     

Selective CO oxidation in the presence of hydrogen over supported Pt catalysts promoted with transition metals

Selective CO oxidation in the presence of excess hydrogen was studied over supported Pt catalysts promoted with various transition metal compounds such as Cr, Mn, Fe, Co, Ni, Cu, Zn, and Zr. CO chemisorption, XRD, TPR, and TPO were conducted to characterize active catalysts. Among them, Pt-Ni/γ-Al₂O₃ showed high CO conversions over wide reaction temperatures. For supported Pt-Ni catalysts, Alumina was superior to TiO₂ and ZrO₂ as a support. The catalytic activity at low temperatures increased with increasing the molar ratio of Ni/Pt. This accompanied the TPR peak shift to lower temperatures. The optimum molar ratio between Ni and Pt was determined to be 5. This Pt-Ni/γ A1₂O₃ showed no decrease in CO conversion and CO₂ selectivity for the selective CO oxidation in the presence of 2 vol% H₂O and 20 vol% CO₂. The bimetallic phase of Pt-Ni seems to give rise to stable activity with high CO₂ selectivity in selective oxidation of CO in H₂-rich stream.     

Fabrication of SiO2-ZrO2 composite fiber mats via electrospinning

(1 − x)SiO₂-(x)ZrO₂ (x = 0.1, 0.2) composite fiber mats were prepared by electrospinning their sol-gel precursors of zirconium acetate and tetraethyl orthosilicate (TEOS) without using a polymer binder. The electrospun composite fibers were characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM), fourier transform infrared spectroscopy (FT-IR) and mercury porosimetry. The composite fibers having a tetragonal crystalline ZrO₂ were obtained by calcining the electrospun composite fibers at high temperatures. The results show that the structure and crystallization of ZrO₂ in the composite fibers can be controlled by sintering temperature, while the porosity and morphology of the fiber mats did not depend on the sintering temperature.     

Blue‐light‐emitting poly(arylene ethynylenes) containing alternating sequences of biphenylene or fluorenediyl and p‐phenylene moieties linked through triple bonds

Two new poly(arylene ethynylenes) were synthesized by the reaction of 1,4‐diethynyl‐2.5‐dioctylbenzene either with 4,4′‐diiodo‐3,3′‐dimethyl‐1,1′‐biphenyl or 2,7‐diiodo‐9,9‐dioctylfluorene via the Sonogashira reaction, and their photoluminescence (PL) and electroluminescence (EL) properties were studied. The new poly(arylene ethynylenes) were poly[(3,3′‐dimethyl‐1,1′‐biphenyl‐4,4′‐diyl)‐1,2‐ethynediyl‐(2,5‐dioctyl‐1,4‐phenylene)‐1,2‐ethynediyl] (PPEBE) and poly[(9,9‐dioctylfluorene‐2,7‐diyl)‐1,2‐ethynediyl‐(2,5‐dioctyl‐1,4‐phenylene)‐1,2‐ethynediyl] (PPEFE), both of which were blue‐light emitters. PPEBE not only emitted better blue light than PPEFE, but it also performed better in EL than the latter when the light‐emitting diode devices were constructed with the configuration indium–tin oxide/poly(3,4‐ethylenedioxythiophene) doped with poly(styrenesulfonic acid) (50 nm)/polymer (80 nm)/Ca:Al. The device constructed with PPEBE exhibited an external quantum efficiency of 0.29 cd/A and a maximum brightness of about 560 cd/m², with its EL spectrum showing emitting light maxima at λ = 445 and 472 nm. The device with PPEFE exhibited an efficiency of 0.10 cd/A and a maximum brightness of about 270 cd/m², with its EL spectrum showing an emitting light maximum at λ = 473 nm. Hole mobility (μ_h) and electron mobility (μ_e) of the polymers were determined by the time‐of‐flight method. Both polymers showed faster μ_h values. PPEBE revealed a μ_h of 2.0 × 10^?4 cm²/V·s at an electric field of 1.9 × 10⁵ V/cm and a μ_e of 7.0 × 10^?5 cm²/V·s at an electric field of 1.9 × 10⁵ V/cm. In contrast, the mobilities of the both carriers were slower for PPEFE, and its μ_h (8.0 × 10^?6 cm²/V·s at an electric field of 1.7 × 10⁶ V/cm) was 120 times its μ_e (6.5 × 10^?8 cm²/V·s at an electric field of 8.6 × 10⁵ V/cm). The much better balance in the carriers' mobilities appeared to be the major reason for the better device performance of PPEBE than PPEFE. Their highest occupied molecular orbital (HOMO) and lowest unoccupied molecular orbital (LUMO) levels were also a little different from each other. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 299–306, 2006     

Modification of a carbon/carbon composite with a thermosetting resin precursor as a matrix by the addition of carbon black

Carbon/carbon composites were made through the pyrolysis of stabilized PAN felt and phenolic resin with the addition of 5 or 10 wt % carbon black to the matrix and then heat treatment at 600–2500°C. The effects of adding carbon black to the matrix precursor on the physical properties, microstructure, and mechanical properties of the resultant composites were investigated. Adding carbon black not only reduced the weight loss but also limited the shrinkage of the resultant composites. Adding carbon black also accelerated the formation of carbon basal planes in the matrix. At 2500°C, the crystalline stacking height in the composite with 10 wt % added carbon black was 200% greater than that with no additive. The flexural strength of the composite also increased from 15 to 42 MPa (almost 300%). © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 333–337, 2006