Failure analysis of aluminum cable steel reinforced (ACSR) conductor of the transmission line crossing the Paraná River

The failure of the conductor of the 460 kV overhead transmission line located along the crossing of the Paraná River was investigated. As a result of this failure, a blackout took place in the southern states of Brazil in January of 2002, reaching approximately 67 million inhabitants. Investigation of the external aluminium layer of the ACSR conductor near the fracture showed typical static deformation marks and dynamic fretting wear tangential marks, both associated with the presence of Al₂O₃ debris. Additionally, encrusted silicon particles were observed on the external surface of the strands. The internal Al layer showed elliptical deformation marks also associated with Al₂O₃ debris. Both Al₂O₃ and Si particles are efficient abrasive material, which associated with slight relative motion of metallic surfaces (clamp/strand and strand/strand) can promote fretting wear. Two types of fracture surface of the Al strands were identified: 45° and quasi-normal surfaces, the former being the predominant type. Delamination and particle detachment were the mechanisms of superficial degradation observed on the Al strands, indicating that the rupture of the strands occurred under a gross slip fretting regime induced by sub-conductor oscillation. Inspection of the internal surface of as-cast Al–10%Si spacer clamps revealed different stages of intense circumferential wear caused by the preferential cracking and particle detachment of the eutectic constituent of the as-cast microstructure. This intense wear reduces the clamping contact pressure, which allows higher displacement amplitude and leads to the critical fretting regime. Finally, a few suggestions are discussed to minimise the occurrence of future failures.     

Coarse filters for shape matching

This article describes the coarse shape filters that support the 3D, Internet-based search engine ShapeSifter, which aims to locate parts already in production that have a shape similar to a desired new part. The search engine analyzes the target model's shape characteristics and performs a similarity match on the database's contents. Our main challenge is identifying shape metrics that produce effective characterizations of 3D models for similarity comparison. We focus on using three novel convex hull-based indices to carry out a preliminary coarse filtering of candidates prior to more detailed analysis. We also describe the crucial role played by two databases of benchmark objects. Unlike other shape-matching systems, we chose ShapeSifter's architecture (multistep query), 3D representation (triangulated mesh), and implementation (Java3D) to allow deployment online once it matures     

Shallow Linear Action Graphs and their Embeddings

Action calculi, which generalise process calculi such as Petri nets, π-calculusand ambient calculus, have been presented in terms of action graphs. We here offer linear action graphs as a primitive basis for action calculi. This paper presents the category of embeddings of undirected linear action graphs without nesting, using a novel form of graphical reasoning which simplifies some otherwise complex manipulations in regular algebra. The results are adapted in a few lines to directed graphs. This work is part of a long-term search for a uniform behavioural theory for process calculi. Received October 2000 / Accepted in revised form April 2001     

Network topology and the theory of rubber elasticity

The earliest investigations on rubber elasticity, commencing in the 19th century, were necessarily limited to phenomenological interpretations. The realisation that polymers consist of very long molecular chains. commencing c. 1930, gave impetus to the molecular theory of rubber elasticity (1932-). according to which the high deformability of an elastomer, and the elastic force generated by deformation, stem from the configurations accessible to long molecular chains. Theories of rubber elasticity put forward from 1934-1946 relied on the assumption that the junctions of the rubber network undergo displacements that are affine in macroscopic strain. The theory of James and Guth (1947) dispensed with this premise, and demonstrated instead that the mean positions of the junctions of a ‘phantom’ network consisting of Gaussian chains devoid of material properties are affine in the strain. The vital significance of the distinction between the actual distribution of chain vectors in a network and their distribution if the junctions would be fixed at their mean positions went unnoticed for nearly 30 years. Experimental investigations, commencing with the incisive work of Gee in 1946. revealed large departures from the relationship of stress to strain predicted by the theories cited. This discrepancy prompted extensive studies, theoretical and experimental, during succeeding years. Inquiry into the fundamentals of polymer networks, formed for example by interlinking very long polymer molecules, exposed the need to take account of network imperfections, typically consisting of chains attached at only one end to a network junction. Various means were advocated to make corrections for these imperfections. The cycle rank ζ of the network has been shown (1976) to be the fundamental measure of its connectivity, regardless of the junction functionality and pattern of imperfections. Often overlooked is the copious interpenetration of the chains comprising typical elastomeric networks. Theories that attempt to represent such networks on a lattice are incompatible with this universal feature. Moreover, the dense interpenetration of chains may limit the ability of junctions in real networks to accommodate the fluctuations envisaged in the theory of phantom networks. It was suggested in 1975 that departures from the form predicted for the elastic equation of state are due to constraints on the fluctuations of junctions whose effect diminishes with deformation and with dilation. Formulation of a self-consistent theory based on this suggestion required recognition of the non-affine connection between the chain vector distribution function and the macroscopic strain in a real network, which may partake of characteristics of a phantom network in some degree. Implementation of the idea was achieved through postulation of domains of constraint affecting the equilibrium distribution of fluctuations of network junctions from their mean positions. This led in due course to a theory that accounts for the relationship of stress to strain virtually throughout the ranges of strain accessible to measurement. The theory establishes connections between structure and elastic properties. This is achieved with utmost frugality in arbitrary parameters.     

Structural acrylic adhesives for the sheet steel fabrication industries

Recent developments in rubber-toughened structural acrylic adhesives now offer sheet steel fabricators the opportunity to replace conventional metal fastening techniques such as spot welding with lower cost, durable, more versatile structural adhesive bonding. These developments, in particular much improved ability to bond oily/waxy surfaces common to the motor car industry and improved retention of fracture toughness after exposure to paint stoving temperatures, are discussed in this paper.     

Eliminating memory for fragmentation within partitionable SIMD/SPMDmachines

Efficient data layout is an important aspect of the compilation process. A model for the creation of perfect memory maps for large-scale parallel machines capable of user-controlled partitionable single-instruction-multiple data/single-program-multiple data (SIMD/SPMD) operation is developed. The term perfect implies that no memory fragmentation occurs and ensures that the memory map size is kept to a minimum. A major constraint on solving this problem is based on the single program nature of both the SIMD and SPMD modes of parallelism. It is assumed that all processors within the same submachine used identical addresses to access corresponding data items in each of their local memories. Necessary and sufficient conditions are derived for being able to create perfect memory maps, and results are applied to several partitionable interconnection networks     

Statistical tests of the IBM PC pseudorandom number generator

The widespread use of IBM personal computers in biomedical research and medical practice is evidenced by a variety of journal articles. Many of the application programs are written in the BASIC language, they model a stochastic process, and they depend on the Microsoft random number generator. Unfortunately, the Microsoft generator has exhibited a number of flaws including, for some seeds, a lack of uniformity of generated sequences of numbers, and serial correlation within such sequences. This paper provides evidence of these problems for several seeds, and provides suggestions for acceptable seeds which ensure that the generated sequences of numbers pass two fundamental statistical tests for randomness.