Hydroxyapatite/tricalcium silicate composites cement derived from novel two-step sol-gel process with good biocompatibility and applications as bone cement and potential coating materials

Tricalcium silicate (C₃S) and hydroxyapatite (HAp) composites were fabricated through the sol-gel process. The aim of this research is to improve the biocompatibility of C₃S through HAp addition and study the potential of using this as coating materials. The composites (HAp/C₃S) were characterised by Fourier transform infrared spectrometry, thermal gravity-differential thermal analysis and X-ray diffraction. The working and setting times of cement pastes were tested using Gillmore needle. Mechanical properties were examined by nanoindentation and material testing system. In vitro biocompatibility of the materials were studied by cell attachment and viability of L929 and MG-63 cells. HAp/C₃S as a coating material on gelatin film were measured with the surface roughness and imaged by scanning electron microscope. With the addition of HAp, no undesirable free CaO was detected with the synthesis by the sol-gel preparation. The pH values of HAp added groups were between 7.54 and 8.76, which were much lower than pure C₃S group (pH?=?11.75). For in vitro studies, the presence of HAp could effectively enhance the cell attachment and viability of both L929 and MG-63 cells grown in the extract or directly on the composites. However, the mechanical properties of the composites were impaired as compared to pure C₃S. Lastly, HAp/C₃S cement could be evenly coated on gelatin film. HAp is successfully demonstrated to improve C₃S biocompatibility with this new composites HAp/C₃S. C-75 (75% C₃S and 25% HAp), in particular, has good biocompatibility, relatively high compressive strength and can be uniformly coated onto gelatin film. Thus, C-75 is a promising material for further investigation as a coating on other biopolymers.     

Preparation and characterization of mullite whisker reinforced ceramics made from coal fly ash

Ceramics with mullite whiskers were prepared from coal fly ash and Al₂O₃ raw materials, with AlF₃ used as an additive. The phase structures and microstructures of the ceramics were identified via X-ray diffraction and scanning electron microscopy, respectively. The results show that pickling of coal fly ash is an effective method for enhancing the flexural strength of ceramics. Sintering temperature and AlF₃ addition were also key factors influencing the creation of ideal ceramics. The ceramic made from pickled coal fly ash, 6?wt% AlF₃, and sintered at 1200?°C, exhibited the highest flexural strength of 59.1?MPa, and had a bulk density of 1.32?g/cm³ and porosity of 26.8%. The results show that ceramic materials made under these conditions are ideal candidates for manufacturing ceramic proppants for the exploitation of unconventional oil and gas resources.     

Electrospun microporous gelatin–polycaprolactone blend tubular scaffold as a potential vascular biomaterial

The work reported involved the fabrication of an electrospun tubular conduit of a gelatin and polycaprolactone (PCL) blend as an adventitia‐equivalent construct. Gelatin was included as the matrix for increased biocompatibility with the addition of PCL for durability. This is contrary to most of the literature available for biomaterials based on blends of gelatin and PCL where PCL is the major matrix. The work includes the assiduous selection of key electrospinning parameters to obtain smooth bead‐free fibres with a narrow distribution of pore size and fibre diameter. Few reports elucidate the optimization of all electrospinning parameters to fabricate tubular conduits with a focus on obtaining homogeneous pores and fibres. This stepwise investigation would be unique for the fabrication of gelatin–PCL electrospun tubular constructs. The fabricated microfibrous gelatin–PCL constructs had pores of size ca 50–100 μm reportedly conducive for cell infiltration. The measured value of surface roughness of 57.99 ± 17.4 nm is reported to be favourable for protein adhesion and cell adhesion. The elastic modulus was observed to be similar to that of the tunica adventitia of the native artery. Preliminary in vitro and in vivo biocompatibility tests suggest safe applicability as a biomaterial. Minimal cytotoxicity was observed using MTT assay. Subcutaneous implantation of the scaffold demonstrated acute inflammation which decreased by day 15. The findings of this study could enable the fabrication of smooth bead‐free microfibrous gelatin–PCL tubular construct as viable biomaterial which can be included in a bilayer or a trilayer scaffold for vascular tissue engineering. © 2019 Society of Chemical Industry     

Isolation of antimicrobial agent from the marine algae Cystoseira hakodatensis

Cystoseira hakodatensis is an unutilised brown algae belonging to family Sargassaceae. A crude methanol extract from the algae showed inhibitory effects on the growths of Bacillus cereus and Bacillus licheniformis. To isolate the major antimicrobial agent, a sequential active‐guided isolation procedure was applied: liquid–liquid extraction, column chromatography and bio‐autography. A marked antimicrobial agent (active α) was isolated in hydrophobic fraction and was determined to phenolics without carbohydrates and proteins by phytochemical test. Regarding the antimicrobial potential, the isolated active α showed better inhibitory effects against B. cereus and B. licheniformis at 2 and 4 times of lower concentrations (62.5 and 31.3 μg mL^?1) in comparison with epigallocatechin gallate. These results showed that C. hakodatensis is a potential source of antimicrobial agent capable of preventing the growth of the two bacteria.     

125I粒子条联合胆道支架植入治疗恶性梗阻性黄疸22例疗效分析

【摘要】　 　目的 研究和探讨125I粒子条联合胆道支架植入治疗恶性梗阻性黄疸的临床疗效。方法 2011年6月—2013年9月收治恶性梗阻性黄疸患者40例。行胆道支架植入术治疗患者18例，为对照组；采用125I粒子条联合胆道支架植入患者22例，为观察组。两组均采用经皮肝穿刺胆道引流（PTCD）并胆道支架植入。结果 观察组与对照组的平均胆道开通时间分别为（8.7 ± 0.7）和（6.2 ± 0.4）个月，两组比较差异有统计学意义（P < 0.05）。观察组与对照组术后平均生存时间分别为（11.4 ± 0.8）和（8.7 ± 0.5）个月，生存时间的差异有统计学意义（P < 0.05）。术后近期疗效及并发症两组之间的比较无明显差异（P > 0.05），但是远期疗效有显著差异（P < 0.05）。结论 与对照组相比，观察组的术后生存时间及胆道开通时间明显延长，对于125I粒子条联合支架治疗恶性梗阻性黄疸值得进一步临床研究。
     

高光谱激光雷达谱位合一的角度效应分析

高光谱激光雷达以其谱位合一的技术优势为实现超三维精准遥感观测提供了可行途径,因此成为当前激光雷达与高光谱遥感领域共同大力推进的前沿发展方向。目前已有多型原型系统研发出来并得到了原理性验证,然而针对其数据处理核心环节问题的基础技术仍较为欠缺。典型问题之一是不同波段回波信号受激光入射角度的影响,该角度效应限制了高光谱激光雷达实现高性能遥感。以芬兰空间信息研究所高光谱激光雷达原型系统扫描桦树树干为例探讨了该角度效应,发现了不同激光波段对不同入射角度的回波强度响应模式,推导出了角度效应的基本规律及其精细尺度的统计规律,为后续该方向的系统研发、数据处理及信息提取等提供了可借鉴的底层机理与技术基础。     

碳酸盐岩岩溶储层多井评价方法及地质应用

多井评价是建立在单井精细解释对比分析基础上的预测储层及含油气性平面分布规律的技术方法,而常规测井资料无法区分碳酸盐岩岩溶储层,因而利用多井评价结果确定岩溶发育程度在平面上的分布规律就显得十分重要。为此,在岩心标定成像测井的基础上,对四川盆地高石梯—磨溪地区15口井的成像测井岩溶发育特征进行分析,建立了中二叠统茅口组岩溶发育各分带的标准成像图版,利用交会图及直方图分析各分带的常规测井响应特征,在此基础上形成了电成像测井刻度常规测井识别岩溶发育带的新方法。研究结果表明:①高石梯—磨溪地区茅口组岩溶带自上而下可划分为风化壳残积带、垂直渗流岩溶带、水平潜流岩溶带以及受岩溶作用较弱的基岩;②风化壳残积带在成像测井图像显示为"暗—亮—暗"条带状模式,垂直渗流岩溶带为垂直线状与暗色斑状组合模式,水平潜流岩溶带为水平线状—层状与斑状组合模式,基岩整体显示为亮色块状模式偶见线状或斑状特征;③有效储层主要发育在垂直渗流带和水平潜流带的顶部;④该区茅口组岩溶发育主要受裂缝发育控制,而裂缝发育又与断层关系密切。结论认为,该新方法对碳酸盐岩岩溶储层的多井评价具有普遍适用性,为四川盆地中二叠统风险探井的部署提供了技术支撑。