Achieving enhanced ductility in a dilute magnesium alloy through severe plastic deformation

Experiments were conducted to evaluate the utility of a new processing procedure developed for Mg-based alloys in which samples are subjected to a two-step processing route of extrusion followed by equal-channel angular pressing (designated as EX-ECAP). The experiments were conducted using a Mg-0.6 wt pct Zr alloy and, for comparison purposes, samples of pure Mg. It is shown that the potential for successfully using ECAP increases in both materials when adopting the EX-ECAP procedure. For the Mg-Zr alloy, the use of EX-ECAP produces a grain size of ∼1.4 μm when the pressing is undertaken at 573 K. By contrast, using EX-ECAP with pure Mg at 573 K produces a grain size of ∼26 μm. Tensile testing of the Mg-Zr alloy at 523 and 573 K after processing by EX-ECAP revealed the occurrence of significantly enhanced ductilities with maximum elongations of ∼300 to 400 pct.     

Structural analysis of Ti-Fe thin films prepared by pulsed laser deposition

Titanium iron oxide (Ti-Fe-O) thin films have been successfully deposited by pulsed laser deposition (PLD). Experiments were carried out by using some targets. One was a Ti-50 at.% Fe-sintered target, while the others were Ti and Fe plates with various surface area ratio [S_R=S_Fe/(S_Fe+S_Ti)] from 30 to 70%. The thin films were analyzed by X-ray diffractometry, Rutherford backscattering spectroscopy (RBS) and transmission electron microscopy (TEM). From XRD analysis, the main phase in the thin films deposited at S_R=30 and 50% was β-Ti (Fe). By increasing S_R to 70%, the main phase of the thin film changed to TiFe. By phase diagram, composition of TiFe must be between Ti-47.5-50.3 at.% Fe at a temperature of 1085 °C. However, the composition of the thin film deposited at S_R=70% was found to be Ti_0.15Fe_0.62O_0.23. Thus, the composition of Fe in the thin film was much greater than the solubility limit. This fact suggests two possibilities. One is that the thin films, which we have deposited, were in a metastable state. The other is that metal oxides of amorphous state could be contained in the thin film.     

Biochemical characterisation of an aminopeptidase with highest preference for lysine from Japanese flounder skeletal muscle

An aminopeptidase was purified from Japanese flounder skeletal muscle to homogeneity by ammonium sulphate fractionation and three chromatographies. The enzyme was approximately 100 kDa with isoelectric point of 5.7 as estimated by two-dimensional polyacrylamide gel electrophoresis. Its optimum temperature and pH were 45 °C and 7.5, respectively. According to peptide mass fingerprinting study, the enzyme revealed high identity to a puromycin-sensitive aminopeptidase. It had a broad specificity toward aminopeptidase substrates and preferred to hydrolyse Lys-MCA with k_cat/K_m of 8.1 × 10⁶ M^?1 s^?1, and the activation energy (E_a) of 72.5 kJ M^?1. Metal-chelating agents effectively inhibited the enzyme activity, and Zn²⁺, Mn²⁺ and Co²⁺ significantly restored the apoenzymatic activity dialysed by EDTA, whilst inhibitors to other proteinases did not show much effect. Furthermore, bestatin strongly inhibited its activity. These results indicate that the purified enzyme is a metalloaminopeptidase which would possibly contribute to free amino acids increase in fish muscle.     

Fabrication of BSCF-based mixed oxide ionic-electronic conducting multi-layered membrane by sequential electrophoretic deposition process

The Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3-δ (BSCF)-based multi-layered oxygen separation membrane was fabricated by the sequential electrophoretic deposition (EPD) process. A thin porous/dense bi-layer of BSCF was formed on a thick porous support of BSCF. The porous support prepared by a sacrificial template method using BSCF powder mixed with wheat starch (30 wt%) as a pore-forming agent, followed by uniaxial pressing and low-temperature sintering, was directly used as an EPD electrode. A thin BSCF layer was first formed on the porous support, and then a thin BSCF + PMMA (polymethyl methacrylate) layer was sequentially formed on the thin BSCF layer using a bimodal suspension of BSCF and PMMA. A 30-μm thin porous/dense bi-layer of BSCF of which the total thickness was obtained by optimizing the processes of EPD and subsequent co-sintering. The oxygen separation performance of 3.7 ml (STP) min^?1 cm^?2 at 860 °C was achieved for the BSCF-based multi-layered oxygen separation membrane.     

Application results of a prototype ultrasonic liquid film sensor to a 7 MPa steam–water two-phase flow experiment

A prototype ultrasonic liquid film sensor was applied to a high-temperature steam–water two-phase flow experiment. The liquid film sensor was vertically installed in a loop which was connected to HUSTLE, a multi-purpose steam source test facility. The hydraulic diameter of the measurement section was 9.4 mm. The output waveforms of the sensor were acquired with a digital oscilloscope. The fluid temperature and system pressure were kept at 288 °C and 7.2 MPa, respectively, during the experiment. The pulse-echo method was used to calculate the liquid film thickness. The cross-correlation calculation was utilized to determine the time difference between the pulse reflected at the sensor surface and the pulse reflected at the liquid film surface. The time-averaged liquid film thicknesses were less than 0.055 mm in the annular flow condition. The increase of the time-averaged thickness was small with the change of the gas momentum flux. The film thicknesses measured with the sensor were compared with the past experimental results; the former were smaller than one-fourth of the thickness estimated as the mean film thickness. The comparison results suggested that the continuous liquid sublayer thickness was measured with the liquid film sensor.     

Connection‐Strength Estimation of Neuronal Networks by Fitting for Izhikevich Model

Recently, there has been abundant research using multineuron recording, but there are many problems with extracting the features from the obtained spike time series, which are huge in volume and complex. Here we introduce a new method of estimating synaptic connection strengths between neurons by fitting to the Izhikevich model by maximum likelihood estimation. We demonstrate that our method can estimate connection strengths from spike time series given by a simulated neural ensemble and can estimate nonconnectivity between two independent cultured neuronal networks. These results suggest that our method is applicable to network and plasticity analysis of neuronal networks.     

Effects of phosphorus content on generation and growth of cracks in nickel–phosphorus platings owing to thermal cycling

We observed crack generation and structural changes in electroless nickel–phosphorus (Ni–P) plating layers formed on copper-metalized silicon nitride substrates both during thermal cycling from ? 40 to 250 °C and during storage (not cycling) at 250 °C in order to investigate the effect of the phosphorus contents on crack generation and growth in the Ni–P platings. The used platings contained phosphorus at three different contents: 2.1 wt% [Ni–P(low)], 6.5 wt% [Ni–P(med)], and 10.9 wt% [Ni–P(high)]. The generation time and the amount of cracks were strongly dependent on their phosphorus contents. More cracks appeared after thermal cycling than after storage at 250 °C. In Ni–P(low), cracks were generated after 200 thermal cycles, whereas no cracks were observed even after 250 h of storage at 250 °C. In Ni–P(med) and Ni–P(high), both during thermal cycling and storage at 250 °C, cracks formed during or after crystallization of the amorphous layers. These results suggest that the primary factors affecting the generation of cracks in electroless Ni–P platings are crystallization of the Ni–P platings and repeated changes in thermal stress.     

Enantioselective addition Of diketene to aldehydes promoted by chiral schiff base—titanium alkoxide complex. Application to asymmetric synthesis of potential inhibitors of HMG coenzyme reductase

Highly enantioselective addition of diketene to aldehydes was achieved by using novel Schiff base—titanium alkoxide complexes. Up to 92% ee of 5-hydroxy-3-oxoesters was obtained. This procedure provides an efficient method for the asymmetric synthesis of potential inhibitors of HMG coenzyme reductase.     

Research and Development of the Coprecipitation Process for Lanthanum Germanate Oxyapatite

Although lanthanum germanate oxyapatite (La–Ge–O) has shown good potential for use as a solid electrolyte in energy storage applications, its synthesis has been challenging by either solid‐ or solution‐state methods. In this study, a new synthesis of La–Ge–O was developed through a coprecipitation technique, in which a highly concentrated homogeneous aqueous solution of La and Ge was prepared from aqueous ammonium germanate and lanthanum nitrate solutions with the addition of dilute nitric acid. Several precipitates were formed by pH manipulation, including an amorphous material obtained at pH > 3. Compared to the individual precipitation behaviors of the parent compounds, the amorphous precipitate was formed only from the aqueous two‐component mixture, and appeared to contain both metals. This material was transformed into crystalline mixtures upon heating at 1273 K. The crystalline phases were La₂Ge₃O₉ and hexagonal‐type GeO₂ when the precipitate was formed below pH 8, and the La–Ge–O and La₂Ge₂O₇ phases when the precipitate was formed around pH 8. Product formation from the coprecipitate was discussed based on X‐ray diffraction and thermal analyses. The improved availability of La–Ge–O will allow more extensive investigations of its useful properties.