The stability of monochlorotriazinyl reactive dyes on cellulose films in aqueous alkaline solutions containing peroxide bleaching agents

The stability of seven reactive (one difluoromonochloropyrimidinyl and six monochlorotriazinyl) dyes on cellulose immersed in sodium peroxoborate (PB) solution (UK–TO solution) containing tetraacetylethylenediamine (TAED) was examined using cellulosic films at 60 °C. The extent of dye loss that occurred from the dyed cellulosic films which were immersed in the UK–TO solution without detergent correlated closely to the ratings obtained using the BS 1006 UK–TO wash test. The dye loss that occurred from the dyed cellophane films was attributed to three contributions, namely, alkaline hydrolysis of dye–fibre bonds, oxidative fading of the dye chromophore by peroxides and cellulose degradation accelerated by PB and TAED. The alkaline hydrolysis of the dye–fibre bond and the extent of cellulose degradation in the UK–TO solution were the main contributions to the dye loss; dye oxidation was a minor factor in the dye loss mechanism. The physical bonding of the dye molecules reinforced the covalent dye–fibre bond stability towards the UK–TO solution.     

Fabrication of fluorine-terminated diamond-like carbon thin film using a hyperthermal atomic fluorine beam

Surface modification of diamond-like carbon (DLC) film was performed using a hyperthermal atomic fluorine beam on the purpose of production of hydrophobic surface by maintaining the high hardness of DLC film. By the irradiation of atomic fluorine beam of a 1.0 × 10²⁰ atoms/cm², the contact angle of a water drop against the DLC surface increased from 73° to 111°. The formation of CF₃, CF₂ and CF bonding on the modified DLC surface was confirmed from the measurements of X-ray photoelectron spectra and near-edge X-ray absorption fine structure spectra. Irradiation of hyperthermal atomic fluorine beam was concluded to produce insulator fluorine-terminated DLC film, which has high F content on the surface, by the taking of the use of neutral atomic beam as a fluorine source.     

Self‐consistent electrical parameter extraction from bias dependent spectral response measurements of III‐V multi‐junction solar cells

Spectral response of multi‐junction solar cell is complicated because of the interplay between external measurement conditions such as bias light intensity, monochromatic light intensity, bias voltage, and intrinsic electrical properties of series interconnected subcells. In this paper, we report an experimental study on the bias voltage‐dependent spectral response (SR) for multi‐junction solar cell. A self‐consistent iteration loop was developed from a nonlinear least square Powell hybrid algorithm that was used for curve fitting the experimental SR versus bias voltage data of each subcell. We demonstrated for the first time that this approach enabled us to derive the electrical parameters such as dark saturation currents (J₀), shunt resistance (R_sh), series resistance (R_s), and spectra response (J_photo) for each subcell of a Ga_0.99In_0.01As/Ge dual junction solar cell with stable convergence. The accuracies of the fitting results were confirmed by the agreement between the J–V curves calculated on the basis of these parameters and the experimental J–V curve of multi‐junction solar cell measured under AM1.5 and 1 sun condition. Copyright © 2013 John Wiley & Sons, Ltd.     

Identification of Neoantigens in Cancer Cells as Targets for Immunotherapy

The clinical benefits of immune checkpoint blockage (ICB) therapy have been widely reported. In patients with cancer, researchers have demonstrated the clinical potential of antitumor cytotoxic T cells that can be reinvigorated or enhanced by ICB. Compared to self-antigens, neoantigens derived from tumor somatic mutations are believed to be ideal immune targets in tumors. Candidate tumor neoantigens can be identified through immunogenomic or immunopeptidomic approaches. Identification of neoantigens has revealed several points of the clinical relevance. For instance, tumor mutation burden (TMB) may be an indicator of immunotherapy. In various cancers, mutation rates accompanying neoantigen loads may be indicative of immunotherapy. Furthermore, mismatch repair-deficient tumors can be eradicated by T cells in ICB treatment. Hence, immunotherapies using vaccines or adoptive T-cell transfer targeting neoantigens are potential innovative strategies. However, significant efforts are required to identify the optimal epitopes. In this review, we summarize the recent progress in the identification of neoantigens and discussed preclinical and clinical studies based on neoantigens. We also discuss the issues remaining to be addressed before clinical applications of these new therapeutic strategies can be materialized.     

Formation Processes of β-C2S by the Decomposition of Hydrothermally Prepared C-S-H with Ca(OH)2

A mixture of CaO and silicic acid prepared with a Ca/Si ratio of 2.0 was hydrothermally synthesized at 80° to 200°C, and the thermal decomposition behavior of the products (C-S-H with Ca(OH)₂) was analyzed using XRD, ²⁹Si MAS NMR, and the trimethylsililation method (TMS). It was found that the main silicate anion structure of C-S-H was a mixture of a dimer and a single-chain polymer (larger than Si₅O₁₆) and that polymerization advanced with an increase of the synthesizing temperature. On heating, the products decomposed to form β-C₂S. It was found that the decomposition was gradual and that the-higher the temperature of hydrothermal synthesis, the lower was the temperature of the decomposition into β-C₂S. Although the decomposition proceeded to form a monomer (β-C₂S) from the polymer and dimer, this dimer was resistant to heat and did not decompose unless heated to above 400°C.     

Change in Oxygen Content of Y2O3-Nd2O3-Doped Silicon Nitride During Firing

The oxygen content of silicon nitride with 1 mol% Y₂O₃—Nd₂O₃ additive was measured after firing to determine the compositional change during gas-pressure sintering. Oxygen content decreases from 2.5 to 0.94 wt% during firing for 4 h at 1900°C and 10-MPa pressure in N₂. This decrease in oxygen results from the release of SiO gas generated by a thermaldecomposition reaction between Si₃N₄ and SiO₂. The resultant sintered silicon nitride material contains less than 1 wt% oxygen.     

Effects of calcining conditions of kaolinite on pore structures of mesoporous materials prepared by the selective leaching of calcined kaolinite

This paper describes the effects of calcining conditions of kaolinite on pore structures of the porous materials obtained from the selective leaching of calcined kaolinite using KOH solution. Mesoporous -Al₂O₃ was the predominant crystalline phase in the samples calcined in the temperature range between 950°C and 1050°C for 24 h. The mean specific surface area of these samples was approximately 250 m² · g^–1 and the mean total pore volume was approximately 0.8 ml · g^–1. The pore size distribution curves of these samples showed a sharp peak at around 2–3 nm pore radius. This peak was sharper for the sample calcined at 1000°C for 24 h. On the other hand, the pore sizes of the sample calcined at 1100°C for 24 h increased abruptly to 10–20 nm and this change corresponded to the formation of mullite in the sample. The pore sizes of the samples calcined at 1100°C varied with calcining time. The specific surface area and total pore volume decreased, the longer the calcining time of the samples, and this was correlated with an increase in the amount of mullite in the samples.     

Resistance to wear and cavitation erosion of bearing alloys

Sliding wear and vibratory cavitation erosion tests in paraffin oil were carried out on bearing alloys, i.e. tin-based and lead-based white metals, Cu-Pb alloy and leaded bronze. In lubricated wear under mild conditions the surface is worn smooth and a slight difference exists between the wear resistances of the four alloys. In cavitation erosion an eroded surface which is much rougher than the worn surface is formed. Cavitation erosion is affected strongly by the composition and crystal structure of the alloy and thus the erosion resistances of the four alloys differ greatly, the ranking of resistance being lead-based white metal < Cu-Pb alloy < tin-based white metal < leaded bronze. The surface damage, which is caused by the joint action of cavitation erosion and wear, was also investigated by rubbing the eroded surfaces which had been exposed to cavitation erosion for various times. This damage becomes larger with increasing cavitation damage. The resistance to this damage differs much more in the four alloys tested and tends to correlate with the results of the erosion tests rather than those of the wear tests. Therefore, it is clear that the cavitation erosion resistance should be considered in the selection of bearing materials.