重钢高线轧机生产工艺设计

在原有国产高线轧机基础上,经改进,如采用新型闭口式轧机,超高速机架,顶交无扭精轧机组等。为重钢高线车间进行了设计,终轧保证速度达到８０ｍ／ｓ,使我国高线轧机国产化达到了新阶段。     

大型风电球墨铸铁件的生产实践

以轮毂为例,介绍对大型风力发电机球墨铸铁件生产工艺进行的试验研究。通过优化铸型工艺,采用适当的浇注系统和低温石墨化退火工艺,选择合理的化学成分,控制球化处理与孕育处理,可生产出各项性能指标合格的风电铸件。     

新型缓蚀剂TG500在高CO2和Cl-环境中的缓蚀行为

在高温高压高CO2和Cl^-环境中，用静态高温高压模拟试验方法对不同浓度的TGS00新型咪唑啉季铵盐缓蚀剂进行了缓蚀效率测试．结果表明，TGS00缓蚀效率随加入量增加而增加，浓度增加到0．3g／L后，缓蚀速率提高不明显．同时研究N80套管钢表面的腐蚀产物，缓蚀剂浓度较低时，以均匀腐蚀为主，加入量提高到0．3g／L时，除局部少量点蚀外，无其它明显腐蚀特征．     

铝合金板材时效组织的高分辨分析

本文通过X射线衍射、扫描电镜、高分辨透射电镜,分析了6009铝合金时效组织,球形Mg2Si是其主要强化相。在电解低钛铝合金中,球形Mg2Si分布更为弥散、均匀。对高分辨像通过傅立叶变换和反傅立叶变换,得到了调幅分解组织的晶格像。结果表明:电解低钛铝合金其力学性能和组织优于熔配加钛铝合金;电解低钛铝合金中Mg和Si原子在铝基体的(200)面上偏聚,形成明显的调幅分解组织。     

PTA装置中冷凝器壳体腐蚀原因分析及防护对策

对仪征化纤化工厂PTA装置中反应器第一冷凝器E-112 壳体腐蚀状况进行了分析.结果表明，高温高压冷凝液的冲刷是造成E-112壳体腐蚀穿孔的 主要原因，并提出相应防护对策.     

MICROSTRUCTURE OF RAPIDLY SOLIDIFIED TiAl ALLOY POWDER

The rapidly solidified powder of Ti-34Al-2Mn alloy was obtained by means of ultrasonicgas atomisation (USGA) technique.The tupical size of the powder is 27 μm.X-ray diffractionresults show that the powder consists of major α_2-phase and minor γ-phase.Under opticalmicroscope both equiaxed and dendritical microstructure features were observed on RS pow-der sections.After annealing at 900 ℃/for 2 h in vacuum,most of α_2-phase transforms intoγ-phase,resulting in refinement of structure.     

APPLICATION OF MOLECULAR ORBITAL THEORY TO ANALYSIS OF PHASE STABILITY FOR ALLOYS

The critical _d vahues ( _ ) of the γ/(γ+σ).γ/(γ+μ) and γ/(γ+γ') phase boundaries insome ternar alloy phase diagrams at various temperatures are calculated by averaging the _d values of sererai selected characteristic points at the phase boundaries.Approxmateequations for the temperature dependence of the critical _d of γ/(γ+σ).γ/(γ+μ) andγ/(γ+γ') phase boundaries are established.The accuracy of the analysis is discussed in detail.It is found for the first time that the average value of the bondorder _ at the phase boundaries ts also approximatelr a constant and therefore a criticalaverage bond order _ like - can be introduced for the analysts of phase stability     

EFFECT OF FINE GRINDING ACTIVATION ON LEACHING BEHAVIOUR OF SCHEELITE CONCENTRATE

The influence of mechanical activation on the leaching behaviour of scheelite was studied bymeans of fine grinding in an attritor and subsequently HCl leaching in presence of PO_4~(3-).Results showed that after fine grinding in the attritor,the reaction rate of scheelitewith HCl-Na_3PO_4 solution was remarkably increased,the extraction of W increased fromabout 8 to 99%.The IR spectra and X-ray diffraction analysis indicated that in addition toan enlargement of surface area the fine grinding action had made also changes of fine struc-ture and reactivity of solid surface,hence the leaching process of scheelite can be carried outunder mild leaching conditions.     

DISACCOMMODATION OF INITIAL SUSCEPTIBILITY IN AMORPHOUS Fe_(90-x)Ni_xZr_(10) ALLOYS

The disaccommodation(DA)measurements of initial susceptibility were performed inamorphous Fe_(90-x)Ni_xZr_(10)(x=10,20,30)alloys.The DA was measured for two differentamorphous states:as-quenched and pretreated at 537 K for 45 min.For all the as-quenched samples,in the isochronal spectra of DA a well defined relaxation peak around350 K is accompanied by a samll but distinct peak near the Curie temperature ofFe_(90)Zr_(10) phase(T_c=230 K).The reversibility and annealing effect on DA are analyzedwithin the framework of two-level model.The fits of the theory to the experimentaldata of reversible relaxation processes gave a spectrum,of activation energies and pre-exponential factor.     

双滑移取向Cu单晶的循环形变行为──Ⅱ．滑移带和形变带SCIEI

用光学显微镜和扫描电镜研究了双滑移取向（［０３４］，［１１７］）Ｃｕ单晶循环饱和后的表面形貌，塑性分切应变幅（γｐｌ）低于１０^（－３）时，［０３４］晶体表面上要为主滑移系的驻留滑移带（ＰＳＢｓ）占据，次滑移只在边缘区域启动，其ＰＳＢｓ细窄（＜１μｍ），体积百分数在１％以下．γｐｌ＞１０^（－３）时，次滑移开始在试样的中部启动，同时，表面出现二种贯穿晶体的宏观形变带（ＤＢＩ，ＤＢＩＩ），滑移带在形变带内集中．［１１７］晶体在γｐｌ＝４．４×１０^（－４）时，双滑移现象已十分明显．γｐｌ＞１０^（－３）时，表面也形成与前者相似的形变带．ＤＢＩ的惯习面与主滑移面平行（［０３４］晶体）或接近（［１１７］晶体），ＤＢＩＩ的惯习面则与前者垂直，文章讨论了形变带形成的可能原因．