Effects of silicone oil and polymeric modifiers on the mechanical properties of highly filled LLDPE

The effects of coupling agents, silicone oil, and three types of polymeric modifiers on the mechanical properties of linear low density polyethylene (LLDPE) composites highly filled with aluminium hydroxide [Al(OH)₃] were studied. Polymeric modifiers that contain polar groups, such as silane‐grafted polyethylene (Si‐g‐PE) and acrylic‐acid‐grafted ethylene‐vinyl acetate copolymer (AA‐g‐EVA), improve the mechanical properties dramatically, while nonpolar modifiers improve them to some extent. When Al(OH)₃ was treated using a titanate coupling agent, the silicone oil increased the impact strength and elongation at break of the LLDPE/Al(OH)₃ composites. Introduction of a polymeric modifier containing polar groups destroys the beneficial effects of silicone oil on film mechanical properties, while the introduction of a nonpolar elastomeric polymeric modifier retains the high impact strength and elongation at break. SEM analyses provide the indirect evidence of the encapsulation of silicone oil around the filler. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 83: 121–128, 2002     

Study of UAV tracking based on CNN in noisy environment

Multimedia Tools and Applications - Recently, there are lots of tracking methods proposed to improve the performance of visual tracking in videos with challenging situations, such as background...     

Robust Control of Networked System and Its Application

International Journal of Control, Automation and Systems - In this paper, the stability issue of networked system with dynamical topology in intelligent vehicle is studied. The systems are...     

Dynamic buffering performance of the honeycomb paperboard filled with polyurethane

A new kind of composite buffering material was made by filling the voids of honeycomb paperboard with polyurethane. Drop tests were performed to evaluate the dynamic energy absorption capacity of the material. Based on the tests results, we analyzed the mechanical behaviors of the material under different conditions and obtained the inherent influencing laws of some factors on the material＇s dynamic buffering performance. It was shown that the dynamic buffering performance varied directly with impact velocity, and inversely with the void diameter, thickness and buffeting area of the composite material.     

焊缝射线照相中的缺陷影像位移

焊缝射线照相中，在底片上得到的只是一张平面投影图，除中心透照法外，其它透照法所得到的缺陷影像会沿焊缝方向相对于实际位置产生不同程度的位移。有些标准如JB4730-2005和GB3323—2005对K值有严格要求，位移量还不是很大，但另一些标准，如SY4056-1993，GB／T12605-1990和美国API标准中对K值没有要求，     

用含Pb、As、Sn地方生铁砂型铸造生产D型石墨铸铁的研究

基于Ph、As、Sn等元素有增大铁液过冷倾向的作用，利用含Ph、As、Sn的地方生铁，采用合金化和砂型铸造可以获得D型石墨铸铁，对其工艺方案进行了研究。用正交试验法设计试验方案，得到最佳工艺方案为：在亚共晶成分（WB％：3．2C，2．1si）的铁液中加入适量的铝（0．6％）和钛（0．8％），可以得到含有100％D型石墨的铸铁，其抗拉强度最高可达276MPa。     

圆锯片的有限元模态分析

针对金属冷热锯机锯片在锯切轧件过程中出现的振动问题 ,利用 MSC/ NASTRAN有限元软件 ,计算分析了各种参数对锯片模态的影响。从而为锯片的设计及其制造工艺的确定提供了可靠的参考依据 ,为最终解决生产中的实际问题发挥了重要作用     

Ni-Cr-Fe-Si-B合金涂层及铝青铜基体熔合区组织的研究

采用钨极氩弧焊方法在铝青铜基体上施焊了Ni—Cr-Fe-Si—B合金涂层，并运用金相显微镜、扫描电子显微镜及能谱分析了喷涂层、熔合区及热影响区的组织形貌和成分分布。结果表明，喷焊时，在涂层与基体界面两侧各组元均发生了明显的扩散，Cu、Ni组元间可相互取代，基体融合区组织的基本组成仍为α (α γ2)，但同时也形成了Cu2FeAl7、NiAl3等新相，且融合区组织细小，涂层与基体间为冶金态结合。     

一种新型气硬冷芯盒树脂砂工艺试验及其在生产中的应用

原砂加入2．5％水溶性酚醛树脂，固化剂为甲酸甲脂，加入量占树脂的30％～40％。先把甲酸甲脂在气体发生器中气化，然后再与40％的压缩空气混合，吹气硬化制芯，最高抗拉强度1．2MPa，抗压强度0．32MPa，发气量12mL／g。生产浇注试验表明：砂芯表面光洁，轮廓清晰，尺寸精确，铸件缺陷少，无毒或低毒，和一般冷硬树脂砂比较，成本降低30％。