Metalorganic chemical vapor deposition of silver thin films for future interconnects by direct liquid injection system

Deposition of Ag films by direct liquid injection-metal organic chemical vapor deposition (DLI-MOCVD) was chosen because this preparation method allows precise control of precursor flow and prevents early decomposition of the precursor as compared to the bubbler-delivery. Silver(I)-2,2-dimethyl-6,6,7,7,8,8,8-heptafluoro-3,5-octanedionato-triethylphosphine [Ag(fod)(PEt₃)] as the precursor for Ag CVD was studied, which is liquid at 30 °C. Ag films were grown on different substrates of SiO₂/Si and TiN/Si. Argon and nitrogen/hydrogen carrier gas was used in a cold wall reactor at a pressure of 50–500 Pa with deposition temperature ranging between 220 °C and 350 °C. Ag films deposited on a TiN/Si diffusion barrier layer have favorable properties over films deposited on SiO₂/Si substrate. At lower temperature (220 °C), film growth is essentially reaction-limited on SiO₂ substrate. Significant dependence of the surface morphology on the deposition conditions exists in our experiments. According to XPS analysis pure Ag films are deposited by DLI-MOCVD at 250 °C by using argon as carrier gas.     

State of polarization changes: Classification and measurement

We propose a standardization procedure that provides a convenient, quantitative and reproducible laboratory-based method for measuring the state of polarization (SOP) fluctuations produced by polarization varying devices. This method is based on the SOP distributions generated by commercial polarization scramblers. We show that these devices generate distributions of the maximum change of the SOP (in a given sample time) that follow Rayleigh statistics, which scale linearly with scrambling frequency and the sample time. We use this procedure to measure the SOP fluctuations in a short length of coiled fiber subject to mechanical perturbations.     

Oligo(ethylene oxide) side‐chain steric screening effects on conductimetric properties of grafted poly(4‐vinylpyridinium) salts in aqueous solutions

A set of poly[N‐oligo(ethylene oxide)yl 4‐vinylpyridinium tosylate] (P4VOEOOTs) has been prepared by spontaneous polymerization of 4‐vinylpyridine. This method gives a grafted polyelectrolyte having a positive charge on every backbone pyridinic moiety. The P4VP15Ts, P4VP164Ts, P4VP350Ts and P4VP750Ts aqueous solution conductivities were determined in the concentration range from 6 × 10^?4 to 10^?2 M at 25 °C. The variation of the conductivity versus concentration of the investigated system exhibits typical polyelectrolyte behaviour. The polyelectrolyte mobility was found to be dependent on the oligo(ethylene oxide) (OEO) side‐chain length. Manning's rod‐like model fails to describe these results. A simple steric effect is proposed to explain the influence of the OEO length. Copyright © 2003 Society of Chemical Industry     

Effects of surface charge, micro-bubble size and particle size on removal efficiency of electro-flotation.

Flotation is a water treatment alternative to sedimentation, and uses small bubbles to remove low-density particles from potable water and wastewater. The effect of zeta potential, bubble size and particle size on removal efficiency of the electro-flotation process was investigated because previous model-simulations indicated that these attributes are critical for high collision efficiency between micro-bubbles and particles. Solutions containing Al3+ as the metal ion were subjected to various conditions. The zeta potentials of bubbles and particles were similar under identical conditions, and their charges were influenced by metal ion concentration and pH. Maximum removal efficiency was 98 and 12% in the presence and absence of flocculation, respectively. Removal efficiency was higher when particle size was similar to bubble size. These results agree with modelling simulations and indicate that collision efficiency is greater when the zeta potential of one is negative and that of the other is positive and when their sizes are similar.     

差分跳频通信系统的特点及性能

文章介绍了一种新型的短波跳频通信技术——差分跳频,分析了差分跳频技术区别于常规跳频技术的主要特点。针对按序列检测的信号接收方法,对差分跳频通信系统在AWGN信道下的性能进行了理论分析,同时做出相应的计算机仿真,证实了差分跳频通信技术和按序列检测方法的结合,使通信系统在AWGN信道下的性能得到了比较显著的提升。     

Synthesis and characterization of biocompatible hydroxyapatite coated ferrite

Ferrite particles coated with biocompatible phases can be used for hyperthermia treatment of cancer. We have synthesized substituted calcium hexaferrite, which is not stable on its own but is stabilized with small substitution of La. Hexaferrite of chemical composition (CaO)_0.75(La₂0₃)_0.20(Fe₂O₃)₆ was prepared using citrate gel method. Hydroxyapatite was prepared by precipitating it from aqueous solution of Ca(NO₃)₂ and (NH₄)₂HPO₄ maintaining pH above 11. Four different methods were used for coating of hydroxyapatite on ferrite particles. SEM with EDX and X-ray diffraction analysis shows clear evidence of coating of hydroxyapatite on ferrite particles. These coated ferrite particles exhibited coercive field up to 2 kOe, which could be made useful for hysteresis heating in hyperthermia. Studies by culturing BHK-21 cells and WBC over the samples show evidence of biocompatibility. SEM micrographs and cell counts give clear indication of cell growth on the surface of the sample. Finally coated ferrite particle was implanted in Kasaulli mouse to test its biocompatibility. The magnetic properties and biocompatibility studies show that these hydroxyapatite coated ferrites could be useful for hyperthermia.     

A 1.5-V 45-mW direct-conversion WCDMA receiver IC in 0.13-/spl mu/m CMOS

A 2-GHz direct-conversion receiver for wide-band code division multiple access (WCDMA) is presented. It includes two low-noise amplifiers (LNAs), an I/Q demodulator, and two sixth-order baseband channel select filters with programmable gain. Quadrature local oscillator (LO) signals are generated on chip in a frequency divider flip-flop. An external interstage filter between the LNAs rejects transmitter leakage to relax demodulator linearity requirements. A low-voltage demodulator topology improves linearity as well as demodulator output pole accuracy. The active-RC baseband filter uses a programmable servo loop for offset compensation and provides an adjacent channel rejection of 39 dB. Programmable gain over 71-dB range in 1-dB steps is merged with the filter to maximize dynamic range. An automatic on-chip frequency calibration scheme provides better than 1.5% corner frequency accuracy. The receiver is integrated in a 0.13-/spl mu/m CMOS process with metal-insulator-metal (MIM) capacitors. Measured receiver performance includes a 6.5-dB noise figure, IIP2 of +27 dBm, and IIP3 of -8.6 dBm. Power consumption is 45 mW.     

Synthesis of amphiphilic magnetic microspheres by dispersion copolymerization of styrene and poly(ethylene oxide) macromonomer

Amphiphilic magnetic microspheres ranging in diameter from 5 to 100 µm were prepared by dispersion copolymerization of styrene and poly(ethylene oxide) vinylbenzyl (PEO‐VB) macromonomer (MPEO) in the presence of Fe₃O₄ magnetic fluid. The effects of various polymerization parameters on the average particle size were systematically investigated. The average particle size was found to increase with increasing styrene concentration and initiator concentration. It also increased with decreasing stabilizer concentration and molecular weight of MPEO. The content of the hydroxyl groups localized in the microspheres ranged from 0.01 to 0.2 mmol g^?1. © 2003 Society of Chemical Industry     

Effect of film thickness on hydrogen content in a-Si : H

The hydrogen content, its depth distribution, and its bonding configuration have been studied in hydrogenated amorphous silicon prepared by plasma-enhanced chemical vapor deposition with hydrogen-diluted silane. Nuclear reaction analysis and infrared spectroscopy were used to determine the total amount of hydrogen and its bonded component, respectively. It has been established that the total concentration of hydrogen does not depend on the film thickness, and has a uniform depth profile. The concentration of bonded hydrogen changes with the film thickness within the measurement accuracy. The data obtained suggest the presence of molecular (non-bonded) hydrogen, uniformly distributed in concentration across the film thickness.     

Lateral ion implant straggle and mask proximity effect

Lateral scattering of retrograde well implants is shown to have an effect on the threshold voltage of nearby devices. The threshold voltage of both NMOSFETs and PMOSFETs increases in magnitude for conventional retrograde wells, but for triple-well isolated NMOSFETs the threshold voltage decreases for narrow devices near the edge of the well. Electrical data, SIMS, and SUPREM4 simulations are shown that elucidate the phenomenon.