高柔韧性聚氨酯丙烯酸酯的合成及应用

选用不同结构的多元醇作骨架，合成一系列高性能的聚氨酯丙烯酸树脂，并通过对聚氨酯丙烯酸树脂性能的对比研究，发现以聚丁二烯二元醇为骨架的聚氨酯丙烯酸酯树脂具有极佳的柔韧性和优异的低温耐曲折性。     

Gel formation in diimide‐hydrogenated polymers

The hydrogenation of diene‐based polymers via diimide is a very attractive alternative to the conventional catalytic hydrogenation route based on gaseous molecular hydrogen. However, serious crosslinking always accompanies it and limits the end‐use properties of the polymers. Gel formation in polymers that are hydrogenated via diimide has been investigated in detail through an inspection of all the chemical reactions involved in the process. The results indicate that hydrogen peroxide decomposition, some reactions related to oxygen, and the redox reaction between hydrogen peroxide and hydrazine are capable of generating radicals. However, radicals generated in the aqueous phase do not appear to initiate the crosslinking of diene‐based polymers in the latex form. It is proposed that the primary radicals giving rise to crosslinking are generated in the polymer phase in situ, and the step responsible for generating these organic radicals is possibly the diimide disproportionation reaction. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 96: 1122–1125, 2005     

Soap‐free emulsion copolymerization of perfluoroalkyl acrylates in the presence of a reactive surfactant

Soap‐free emulsion copolymerization of perfluoroalkyl acrylate (FA)/methyl methacrylate (MMA)/n‐butyl acrylate (n‐BA) was carried out in the presence of sodium 2‐acrylamide‐2‐methyl propanesulfonate (AMPSNa) as a reactive surfactant and potassium persulfate (KPS) as an initiator. An analysis of the effects of concentration of AMPSNa, KPS, FA as well as polymerization temperature on the kinetic features (rate of polymerization) and colloidal characteristics (mean particle diameter, particle disperse index, particle numbers, and surface charge density) was followed. NMR, FTIR, AFM, and fluorine‐selective electrode analysis were used to characterize the composition and morphology of the FA copolymers. Both AFM analysis and contact angle measurements strongly implied that the fluorinated segments migrated to the outmost surface and created films with lower surface energy. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 2438–2444, 2007     

Fabrication and amplification of Rhodamine B‐doped step‐index polymer optical fiber

A step‐index polymer optical fiber (SI POF) containing Rhodamine B in poly(methyl methacrylate) (PMMA) has been fabricated by a preform technique. Fluorescence of different fiber lengths were observed and discussed. A high gain (23 dB) for a SI POF with 60‐cm length, 400‐μm diameter was obtained. The Rhodamine B content of the doped SI POF is 5 ppm‐wt. The signal wavelength providing the highest gain for a 60 cm SI POF is around 630 nm, and the optimum fiber length is about 60 cm at 10 kW launched pump power. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 93: 681–685, 2004     

Decolorisation and mineralisation of CI Reactive Black 8 by the Fenton and ultrasound/Fenton methods

The effects of pH, ferrous ion and hydrogen peroxide dosage on the decolorisation and mineralisation of CI Reactive Black 8 by the Fenton process with/without ultrasonic irradiation were investigated. It was verified that the presence of ultrasonic irradiation did not enhance the decolorisation of CI Reactive Black 8 significantly by Fenton's reagents, but it enhanced the chemical oxygen demand removal efficiency. The enhancement was more pronounced for lower (<0.89 mm) or higher (>1.78 mm) ferrous ion dosage. The optimal pH for chemical oxygen demand removal was 3.0. Chemical oxygen demand removal efficiency increased with the increasing H₂O₂ dosage and reached the highest level at 5.88 mm, but further increase in H₂O₂ dosage would not increase removal efficiency significantly.     

HIPS-g-PMMA的合成及其在HIPS/PVC共混体系中的增容作用

采用自由基引发的溶液聚合法合成了高抗冲聚苯乙烯接枝聚甲基丙烯酸甲酯(HIPS-g-PMMA)增容剂，考察了引发剂用量、反应温度及反应时间对增容剂的接枝率及支链摩尔质量的影响；同时对增容剂对HIPS／PVC共混体系的增容效果作了考察。结果表明：最佳反应条件是反应温度80℃，反应时间4h，引发剂用量以0．2～0．25g为宜；增容剂HIPS-g-PMMA对HIPS／PVC共混体系表现出较好的增容效果，共混物的拉伸强度、屈服强度及断裂伸长率明显增加，冲击强度增大，电镜照片显示两相界面变得更加模糊。     

集成电路密封用高纯邻甲酚醛环氧树脂的制备

ECN树脂中的可水解氯含量是决定树脂质量的—个重要指标。本文研究了反应温度、ECH/OCN配比、反应时间和碱用量等因素的影响,取得了规律性的认识,并获得最佳配方,制备出高纯度的ECN树脂系列产品。     

改性5A分子筛对水中As(Ⅴ)的吸附作用研究

改性5A分子筛是一种高效吸附材料。实验用5A分子筛作为载体,制备了该吸附剂,并表征了其基本性质。结果表明,改性5A分子筛对As(Ⅴ)具有很高的吸附率和选择性;室温下,pH=7时,改性5A分子筛吸附As(Ⅴ)的吸附等温线符合Langmuir型和Freundlich型。     

论港口危险货物运输装卸作业安全问题

危险货物作业安全越来越受到人们的关注，从危险货物的分类谈起，分析了危险货物港口运输装卸作业中易引发事故的诸因素和安全作业中应特别注意的几个问题，强调从业单位、从业人员的资质、法律意识和业务素质，制定危险货物事故应急预案等。提出了加强港口危险货物安全管理的有关建议：开展危险源与事故隐患的多层次监控；推进港航危险货物企业建立安全质量标准化体系；创建“抓小放大”的安全管理机制。     

Dynamic equivalent method of interconnected power systems with consideration of motor loads

The existing equivalent methods usually only deal with static load models and neglect the dynamic characteristics of loads such as induction motors.This paper presents a dynamic equivalent method which considers motor dynamics.At first,the clustering criterion of motor loads is given.The motors with similar dynamic characteristics are classified into one group.Then,reduction of motors in the same group is carried out.Finally,parameters of the equivalent motor are calculated and the equivalent system is thus...