Surface Activation of Diamond Particles in the Process of Chemical Coppering

The effect of the composition of sensitizing–activating solutions on the activation efficiency and the chemical coppering of diamond powders is studied. The results demonstrate that stabilizing additives improve the stability of the solutions, influence the average coppering rate, and play a key role in determining the morphology and quality of the resultant coatings. The most effective stabilizing additive is synthamid-10, which ensures the deposition of high-quality copper coatings.     

High-strain-rate superplasticity of nanocrystalline aluminum alloy 1570

The structure and mechanical properties of nanocrystalline aluminum alloy 1570 obtained by means of severe plastic deformation have been studied. Being tested in a temperature range from 300 to 400°C, the alloy exhibits high-strain-rate superplasticity. At 400°C, the superplasticity is manifested in a very broad range of strain rates, extending from 5 × 10^?3 to 1 s^?1.     

Towards new indicators for the prediction of solid waste anaerobic digestion properties.

The biochemical composition can be seen as a good indicator of both the biodegradability and the methane potential of a given waste. The work presented here is an attempt to elaborate a typology of wastes and to compare it to the anaerobic degradation characteristics. The first data indicate that there is a link between the ligno-cellulosic content of the waste and the biodegradability. When dealing with application to anaerobic digestion processes, having a tool to predict the ability of the waste to be degraded could be of the greatest interest for preventing failures, estimating biogas production, methane content, or for the management of co-digestion processes.     

Financial Analysis and Marketing Strategy

A combination of concept (the product portfolio and the product life cycle) and empirical research (the PIMS study) can aid in clarifying the key issues involved in the selection of a firm's core strategies. Strategy control is multistage: periodic re-evaluation of strategy alternatives by use of the marketing audit; an analytical framework for control of chosen strategies by breaking down components and reporting their performance variances; and 'marketing segment' analysis for control of the detailed marketing plan.?     

Corrosion Behavior of 316LN and 316 Stainless Steels During Long-term Exposure to Aerated 0.5 M NaCl Using Electrochemical Noise Technique

In the present work 316LN as well as 316 stainless steel (SS) coupons each of dimensions (0.025 × 0.018 × 0.006 m³) in well-polished condition were used as two nominal electrodes which were immersed in the aerated solution of 0.5 M NaCl. Correlated current and potential electrochemical noise (EN) signals were collected at 1 Hz sampling frequency for 1 h daily over a period of 30 days. The detrended EN data were used to calculate the noise resistance (R _N) as well as the spectral noise resistance at zero frequency (R _SN^o) values and other statistical parameters. To study the nature of pits and distribution of their diameters as well as depths, extensive observations of the pitted and the blank specimens were carried out using Confocal Laser Scanning Microscopy (CLSM). The current and the potential records of the two alloys showed distinct differences in their corrosion behavior. It was observed that within less than 4 h of immersion, 316SS showed signals indicative of unstable pitting and onset of stable pitting was noticed after 48 h of exposure. However, until about 24 h, 316LN showed just the random signals and unstable pitting was observed after 28 h. The signals clearly indicated continuous growth of the stable pits in 316SS as against the repassivation of the unstable pits in 316LN after 7 days exposure. It was observed that R _N values showed a continuous decrease in the case of 316SS, but were quite stable in the case of 316LN over the exposure period. Concurrent to these observations it was observed that 316SS specimen was extensively pitted. The frequency distributions of pit diameters as well pit depths were observed to be highest at 10-20 μm and 5-10 μm, respectively. However, pits with as large as 70-80 μm diameter and as deep as 20-25 μm too were observed. No pits were observed in case of 316LN even after 30 days of exposure, an observation that corroborates well with the stable R _N values. Thus, in the present investigation, the long-term tests using EN technique coupled with CLSM studies conclusively prove that many unstable pits initiated in 316SS turn into stable ones resulting in insidious localized corrosion attack whereas the unstable pits initiated in 316LN get passivated in the simulated coastal environment.     

Filled Fibrous Sorbents Modified with Transition Metal Ferro- and Ferricyanides for Recovery of Americium and Rare-Earth Metals

Filled fibrous sorbents modified with transition metal ferro- and ferricyanides capable to recover americium(III) and rare-earth metals(III) from nitric acid solutions were prepared. The most complete and rapid recovery is attained on complex-forming and cation-exchange sorbents (as filled fibrous materials) saturated with nickel ions. The sorbents are characterized by good kinetic properties and can be used for recovery of the above metals.     

The Effects of H2O, CO and CO2 on the H2 Permeance and Surface Characteristics of 1 mm Thick Pd80wt%Cu Membranes

The hydrogen permeance of 1 mm-thick Pd_80wt%Cu foils was measured in the presence of equimolar mixtures of H₂ with CO, CO₂ or H₂O over the temperature and total pressure ranges of 623–1,173 K and 0.62–2.86 MPa, respectively. In all cases, permeance losses at 623 and 738 K were very modest. At higher temperatures, more significant decreases in membrane permeance were observed with the highest reduction of about 50% occurring when macroscopic carbon deposition occurred on the membrane surface during H₂–CO exposure at 908 K. The more worrisome effects of exposure to these gases, however, were the micron-scale surface defects observed at 908 and 1,038 K. Although the 1 mm thick disk membranes retained their mechanical integrity, such defects could cause catastrophic failure of ultra-thin, Pd–Cu membranes (1–5 μm thick) deposited on porous substrates.     

Factors of large graphite crucible life

Production methods used to prepare graphite crucibles with high operating properties are considered: use as a filler of good graphitizing acicular coke, vibration molding of the original coke mix, use of production cycles for impregnation with medium temperature coal-tar pitch — firing, firing of compacted billets in metal containers, graphitization of fired billets in graphite cylinders. The last two production methods make it possible to reduce the temperature drop throughout the volume of a billet during heat treatment, and as a consequence to reduce crack development to a minimum as a result of reducing thermal stresses. All of the production methods recommended may be entirely accomplished in existing electrode plants and may be used to increase markedly the quality crucible graphite. It is possible to achieve a quality for these materials at the best world level. Translated from Novye Ogneupory, No. 8, pp. 28–33, August 2008.