Dielectric performance of pyrochlore-type Bi2MgNb2-xTaxO9 ceramics: The effects of tantalum doping

The solid solutions based on the pyrochlore-type system Bi₂MgNb_2-xTa_xO₉ were formed in the compositional range х = 0–2.0 (Bi_1·6Mg_0·8Nb_1.6-tTa_tO_7.2, t = 0–1.6). The Rietveld method was used to refine the structure for Bi₂MgNb_2-xTa_xO₉ (x = 0, 1.0, 2.0). The increasing tantalum content led to the slight decrease in the cubic unit cell parameters from 10.56934 (4) Å for x = 0 and 10.54607 (3) Å for x = 2 (sp.gr. Fd-3m:2). At the same time, tantalum additions suppressed grain growth in the pyrochlore ceramics during sintering and made it possible to obtain materials with an average grain size of 1–2 μm (Bi_1·6Mg_0·8Ta_1·6O_7.2). The increase in the Ta⁵⁺ concentration led to the decrease in the dielectric permeability from 104 (Bi_1·6Mg_0·8Nb_1·6O_7.2) to 20 (Bi_1·6Mg_0·8Ta_1·6O_7.2) at room temperature, while the dielectric loss tangent remained lower than 0.002, which is due to the small grain size and the high porosity of the samples. An increase in temperature has practically no effect on the values of the dielectric permittivity in the entire frequency range. The samples have weak through conductivity. The activation energies of electrical conductivity varied in the range of 0.84–1.00 eV, and the less tantalum, the lower the activation energy. The electrical properties of the samples at 200 Hz to 1 MHz are described by the simplest parallel scheme.     

TRAJECTORY CONTROL OF THE OBSERVATION PROCESS OF A MOBILE DIGITAL DIRECTION FINDER IN THE TOPOLOGY OF A ROAD NETWORK

Journal of Computer and Systems Sciences International - The solution of the problem of determining the trajectory control of the observation process of a mobile digital direction finder in the...     

Validation of scientific topic models using graph analysis and corpus metadata

Probabilistic topic modeling algorithms like Latent Dirichlet Allocation (LDA) have become powerful tools for the analysis of large collections of documents (such as papers, projects, or funding applications) in science, technology an innovation (STI) policy design and monitoring. However, selecting an appropriate and stable topic model for a specific application (by adjusting the hyperparameters of the algorithm) is not a trivial problem. Common validation metrics like coherence or perplexity, which are focused on the quality of topics, are not a good fit in applications where the quality of the document similarity relations inferred from the topic model is especially relevant. Relying on graph analysis techniques, the aim of our work is to state a new methodology for the selection of hyperparameters which is specifically oriented to optimize the similarity metrics emanating from the topic model. In order to do this, we propose two graph metrics: the first measures the variability of the similarity graphs that result from different runs of the algorithm for a fixed value of the hyperparameters, while the second metric measures the alignment between the graph derived from the LDA model and another obtained using metadata available for the corresponding corpus. Through experiments on various corpora related to STI, it is shown that the proposed metrics provide relevant indicators to select the number of topics and build persistent topic models that are consistent with the metadata. Their use, which can be extended to other topic models beyond LDA, could facilitate the systematic adoption of this kind of techniques in STI policy analysis and design.

     

Modernization of Air Supply Unit for Oxidation Towers Used in Bitumen Production

Chemical and Petroleum Engineering - The hydrodynamics of oxidation towers used for bitumen production were studied using a model tower having transparent walls. Experiments were carried out in two...     

Modeling the Destruction of an Anisotropic Composite Barrier in Interaction with Slender Strikers at an Angle

Journal of Engineering Physics and Thermophysics - A numerical investigation has been made into the interaction of slender (5–20 calibers) steel cylinder strikers with orthotropic compost...     

Increasing the photocatalytic and fungicide activities of Ag3PO4 microcrystals under visible-light irradiation

The present study reports for the first time the performance of silver phosphate (Ag₃PO₄) microcrystals as photocatalyst (degradation of Rodamine B-RhB) and antifungal agent (against Candida albicans–C. albicans) under visible-light irradiation (455 nm). Ag₃PO₄ microcrystals were synthesized by a simple co-precipitation (CP) method at room temperature. The structural and electronic properties of the as-synthetized Ag₃PO₄ have been investigated before and after 4 cycles of RhB degradation under visible light using X-ray diffraction (XRD), micro-Raman spectroscopy, UV–Vis spectrophotometer and field emission scanning electron microscopy (FE-SEM) images. The antifungal activity was analyzed in planktonic cells and 48h-biofilm of C. albicans by colony forming units (CFU) counting, confocal laser and FE-SE microscopies. Statistical analysis was carried out using SPSS software. Morphological and structural modifications of Ag₃PO₄ were observed upon recycling. After 4 recycles, the material maintained its photodegradation property; an eightfold increase in the efficiency of Ag₃PO₄ was observed in planktonic cells and a two fold increase in biofilm when irradiated under visible light. Thus, higher antifungal effectiveness against C. albicans was obtained when associated with visible-light irradiation.     

Hydraulic reactivity and cement formation of baghdadite

In this study, the hydraulic reactivity and cement formation of baghdadite (Ca₃ZrSi₂O₉) was investigated. The material was synthesized by sintering a mixture of CaCO₃, SiO₂, and ZrO₂ and then mechanically activated using a planetary mill. This leads to a decrease in particle and crystallite size and a partial amorphization of baghdadite as shown by X-ray powder diffraction (XRD) and laser diffraction measurements. Baghdadite cements were formed by the addition of water at a powder to liquid ratio of 2.0 g/ml. Maximum compressive strengths were found to be ~2 MPa after 3-day setting for a 24-h ground material. Inductively coupled plasma mass spectrometry (ICP-MS) measurements showed an incongruent dissolution profile of set cements with a preferred dissolution of calcium and only marginal release of zirconium ions. Cement formation occurs under alkaline conditions, whereas the unground raw powder leads to a pH of 11.9 during setting, while prolonged grinding increased pH values to approximately 12.3.     