Synthesis of LiFePO4 with fine particle by co-precipitation method

LiFePO₄ is a potential candidate for the cathode material of the lithium secondary batteries. A co-precipitation method was adopted to prepare LiFePO₄ because it is simple and cheap. Nitrogen gas was needed to prevent oxidation of Fe²⁺ in the aqueous solution. The co-precipitated precursor shows the high reactivity with the reductive gas, and the single phase of LiFePO₄ is successfully synthesized with the aid of carbon under less reductive conditions. LiFePO₄ fine powder prepared by co-precipitation method shows high rate capability, impressive specific capacity and cycle property.     

Physical modeling of gas/liquid mass transfer in a gas stirred ladle

The absorption of gas through the plume eye and of an injected gas in a steelmaking ladle process was investigated, using a physical model of CO₂ absorption into a NaOH solution. The results show that the inert gas escaping through the plume eye is ineffective in protecting the bath from the atmosphere, and placing an oil layer (simulated slag) decreases the absorption rate significantly. Increasing the flow rate of the inert gas not only exposes more of the liquid surface to the CO₂ atmosphere, but also increases the mass transfer coefficient at the surface. The overall mass transfer between an injected CO₂ gas and NaOH solution includes the mass transfer through the surface of the bath as well as the mass transfer in the bubble dispersion zone. The difference between the mass transfer in the bubble dispersion zone and the overall mass transfer was found to be significant for relatively low gas flow rates. The mass transfer coefficient of CO₂ in the bubble dispersion zone was estimated using available information regarding the bubble size and velocity. Mass transfer coefficient estimated for the constant bubble frequency regime shows a dependence on gas flow rate. However, if a constant characteristic size of bubbles is assumed as an alternative approach, the mass transfer coefficient is independent of the gas flow rate.     

A 0.6–2.7 GHz Semidynamic Frequency Divide-by-3 Utilizing Wideband RC Polyphase Filter in 0.18 $mu$m CMOS

A wideband complementary metal oxide semiconductor (CMOS) semidynamic frequency divide-by-3 covering more than two octave bandwidths is presented. The wideband operation without requiring a quadrature signal source is realized by employing a three-stage RC polyphase filter. The transfer function analysis on Type-II two- and three-stage polyphase filters is performed to provide analytic solutions of the peak phase error and peak attenuation. Implemented in 0.18 mum CMOS, the divide-by-3 operates over the input frequency range between 0.6 and 2.7 GHz while dissipating 15 mA from a 1.8 V supply.     

Production and structural features of a water-soluble polysaccharide from a mutant strain of Agrobacterium sp.

We have developed a mutant strain derived from Agrobacterium sp. ATCC 31750, which produces a water-soluble polysaccharide having potential utility to the food, feed, pharmaceutical and cosmetic industries. A high concentration of product (15 g/L) is obtained by 48 h cultivation of the mutant strain under optimized fermentation conditions. The water-soluble polysaccharide obtained from cultures of the mutant strain beta82 has Glc:Man:Gal in approximate molar ratios of 5.8:6.7:1.0. The molecular weight of the polysaccharide was determined to be approximately 1000 kDa by HPSEC analysis. Linkage analysis contained 3-Glcp, 3-Manp, terminal Glcp and terminal Manp, as well as a small proportion of 3- and 3,4-Galp, and 4,6-Manp residues. Based on analyses using FT-IR and ¹³C NMR spectrometers, most glycosidic bonds joining these sugar residues are of the α-type, and acetyl groups are apparently attached to the polymer chain at random.     

Effects of surfactant/silica and silica/cerium ratios on the characteristics of mesoporous Ce-MCM-41

Using the surfactant CTMABr (cetyltrimethyl ammonium bromide) and cerium(IV) sulfate, mesoporous Ce-MCM-41 molecular sieves were produced under a hydrothermal condition with various surfactant/silica (surfactant/Si) and silica/cerium (Si/Ce) ratios. Changes to the structural traits caused by changing the molar ratios of both surfactant/Si and Si/Ce were investigated. XRD (X-ray diffraction), FT-IR (fourier transform infrared spectroscopy), and SEM (scanning electro microscopy) were used for the characterization of prepared mesoporous samples. Among the tested molar ratios, surfactant/Si ratio of 0.5 and 0.2 showed highest values of d_1 0 0 and intensity, respectively, for the Si-MCM-41. XRD analysis also identified a quintessential hexagonal structure of Ce-MCM-41 for the Si/Ce molar ratio higher than 40 (maintaining the surfactant/Si ratio at 0.2). When cerium content was increased to have the Si/Ce molar ratio of 20, the hexagonal structure of Ce-MCM-41 was collapsed due to the structural stress of substituted cerium. FT-IR results confirmed calcination of Ce-MCM-41 and the incorporation of Ce⁴⁺ ions of cerium sulfate into the silica surface with proper removal of the surfactant. Rod-like shape with rounded edges of the prepared Ce-MCM-41 samples was identified by SEM. These results suggest surfactant/Si ratio of 0.2 and Si/Ce ratio of 40 for the production of Ce-MCM-41 with the highest level of crystallinity.     

Dye adsorption characteristics of alginate/polyaspartate hydrogels

This study examined the removal of some basic dyes, such as Methylene Blue, Malachite Green and Methyl Orange, using alginate or alginate/polyaspartate composite gel beads. The adsorption of dyes from aqueous solutions at 25 °C was examined using a batch sorption technique. The effects of CaCl₂ and the dye concentration on the adsorption were examined. Type-S adsorption isotherms were obtained, which is characteristic of a weak solute–solid interaction. The ionic interaction between the dye molecule and gel matrix appears to be responsible for the efficient adsorption of cationic dyes in this system. These results suggest that an alginate/polyaspartate gel can be used as an effective sorbent for water pollutants such as dyes, and the immobilization of these organic contaminants in the hydrogels from wastewater can solve one of the most important environmental problems in the related industry.     

The relationship between photo-catalytic performance and optical property over Si-incorporated TiO2

This study focuses on the relationship between photo-catalytic performance and optical property over Si-incorporated TiO₂. The Si-incorporated TiO₂ particles exhibited a pure structure of anatase having a particle size of less than 20 nm and surface area of more than 190 m²/g. The absorbance did not shift to a higher wavelength in spite of the incorporation of the Si ions, but the intensity of the photoluminescence (PL) curve was the smallest in the case of the 2.0 mol% Si-TiO₂, which was related to the recombination between the excited electrons and holes. Based on these results, the photodecomposition of methyl orange in the liquid reaction was enhanced over the 2.0 mol% Si-incorporated TiO₂ compared with that over pure TiO₂: Methyl orange at 10.0 ppm was completely decomposed after 100 min when 1.0 g of the 2.0 mol% Si-incorporated TiO₂ was used.     

Noise–Power Optimization of Incremental Data Converters

Incremental data converters (IDCs) are useful in instrumentation and measurement applications, where low-frequency analog signals need to be converted into digital form with high accuracy and low power dissipation. They are particularly well suited for applications where a single analog-digital converter is multiplexed between many channels. This paper proposes an exact design methodology for IDCs, which optimizes the signal-to-noise ratio of the converter under practical design constraints. The process also allows the designer to apportion the noise budget in an arbitrary manner between thermal and quantization noise. The design process is illustrated by an example which describes the optimization of a third-order multiplexed IDC.