Investigations in the compaction and sintering of large ceramic parts

In this study, a large ceramic part was successfully compacted and sintered using uniaxial die compaction technique. The effects of die design, compaction pressure, lubrication, sintering procedure and part orientation in the oven on the P/M part quality were investigated and the preferred process conditions were discussed and concluded. The main quality issues encountered were cracking and distortion. A finite element model for the powder compaction process was also developed and validated. Based on the model, the relationship between the cracking location and the density distribution predicted from finite element analysis (FEA) was discussed.     

Increasing profit by improving gas handling systems

The availability of a smelter’s gas handling systems is crucial to the profitability of the plant. In new projects, the best technical and economic result is achieved if the gas handling systems are integrated into the process. This integration requires close cooperation between the smelter process designer and the gas handling designer. In modernization projects, environmentally, economically, and technically feasible solutions can be found, and smelter productivity can be increased when imagination and new technology are applied.     

Micro-end-milling of single-crystal silicon

Ductile-regime machining of silicon using micro-end-mill is almost impossible because of the brittle properties of silicon, crystal orientation effects, edge radius of the cutter and the hardness of tool materials. Micro-end-milling can potentially be used to create desired three dimensional (3D) free form surface features using the ductile machining technology for single-crystal silicon. There is still a lack of fundamental understanding of micro-end-milling of single-crystal silicon using diamond-coated tool, specifically basic understanding of material removal mechanism, cutting forces and machined surface integrity in micro-scale machining of silicon. In this paper, further research to understand the chip formation mechanism was conducted. An analysis was performed to discover how the chips are removed during the milling process. Brittle and ductile cutting regimes corresponding to machined surfaces and chips are discussed. Experiments have shown that single-crystal silicon can be ductile machined using micro-end-milling process. Forces generated when micro-end-milling single-crystal silicon are used to determine the performance of the milling process. Experimental results show that the dependence of the cutting force on the uncut chip thickness can be well described by a polynomial function order n. As cutting regime becomes more brittle, the cutting force has more complex function.     

The preparation of tantalum powder using a MR-EMR combination process

In the conventional metallothermic reduction (MR) process used to obtain tantalum powder in batch-type operation, it is difficult to control the morphology and location of the tantalum deposits. In contrast, an electronically mediated reaction (EMR) process is capable of overcoming this difficulty. It has the advantage of being a continuous process, but has the disadvantage of a poor reduction yield. A process known as the MR-EMR combination process is able to overcome the shortcomings of the MR and EMR processes. In this study, an MR-EMR combination process is applied to the production of tantalum powder via sodium reduction of K₂TaF₇. In the MR-EMR combination process, the total charge passed through an external circuit and the average particle size (FSSS) increase as the reduction temperature increases. In addition, the proportion of fine particles (−325 mesh) decreases as the reduction temperature increasess. The tantalum yield improved from 65 to 74% as the reduction temperature increased. Taking into account the charge, impurities, morphology, particle size and yield, a reduction temperature of 1123 K was found to be optimum for the MR-EMR combination process.     

Microstructure and mechanical property of irradiated Zr−2.5Nb pressure tube in Wolsong unit-1

With the aim of assessing the degradation of Zr−2.5Nb pressure tubes operating in the Wolsong unit-1 nuclear power plant, characterization tests are being conducted on irradiated Zr−2.5Nb tubes removed after 10-year operation. The examined tube had been exposed to temperatures ranging from 264 to 306°C and a neutron fluence of 8.9×10²¹ n/cm² (E>1 MeV) at the maximum. Tensile tests were carried out at temperatures ranging from RT to 300°C. The density of a-type and c-type dislocations was examined on the irradiated Zr-2.5Nb tube using a transmission electron microscope. Neutron irradiation up to 8.9×10²¹ n/cm² (E>1 MeV) yielded an increase in a-type dislocation density of the Zr−2.5Nb pressure tube to 7.5×10¹⁴ m⁻², which was highest at the inlet of the tube exposed to the low temperature of 275°C. In contranst, the c-component dislocation density did not change with irradiation, keeping an initial dislocation density of 0.8×10¹⁴ m⁻² over the whole length of the tube. As expected, the neutron irradiation increased mechanical strength by about 17–26% in the transverse direction and by 34–39% in the longitudinal direction compared to that of the unirradiated tube at 300°C. The change in the mechanical properties with irradiation is discussed in association with the microstructural change as a function of temperature and neutron fluence.     

Low-energy ion beam treatment of α-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>(0001) and improvement of photoluminescence of ZnO thin films

A low energy N₂ ^? ion beam impinged on a α-Al₂O₃(0001) single crystal surface in the range of fluence 5×10¹⁵/cm²?1×10¹⁸/cm² at room temperature. After ion bombardment, chemical bonding on the modified sapphire surface was investigated by x-ray photoelectron spectroscopy. Below a fluence of 1×10¹⁵/cm², only a non-bonded N1s peak at the binding energy 398.7 eV was found, but further irradiation up to 2×10¹⁷/cm² induced Al?O?N bonding at around 403 eV. The occurrence of Al?N bonding was identified at ion fluence higher than 5×10¹⁷/cm² at 396.6 eV. II–VI ZnO thin films were grown on an untreated/ion-beam-induced sapphire surface by pulsed laser deposition (PLD) for the investigation of the modified-substrate effect on photoluminescence. The ZnO films grown on modified sapphire containing Al?O?N bonding only, and both Al?O?N and Al?N bonding showed a significant reduction of the peak related to deep-level defects in photoluminescence. These results are explained in terms of the formation of Al?N?O and Al?O?N layers and relaxation of the interfacial strain between Al₂O₃ and ZnO.     

Optimization of casting conditions for heat and abrasion resistant large grey iron castings

Numerical simulation technology was applied for optimizing the casting design and conditions in large cast iron castings for marine engine. By the simulation of mold filling and solidification sequences the problems of the previous casting conditions were analyzed and marked improvements for large cylinder liner parts were derived from these results. Especially the amount and positions of chills were optimized to increase the mechanical properties and to minimize the shrinkage and microporosity in the castings. Ultrasonic testing, penetration testing and mechanical property testing were carried out for the parts with the modified casting conditions. It showed that no defects in the castings were found and the productivity could be distinctly increased. The mechanical properties satisfied also the specification demanded.     

Caustic stress corrosion cracking of alloys 600 and 690 with NaOH concentrations

In order to evaluate the stress corrosion cracking resistance for commercial alloys (C600MA, C600TT, C690TT) and Korean-made alloys (K600MA, K690TT), C-ring tests were performed in a caustic environment of 4, 10, 20, 30, and 50% NaOH solution at 315°C, for 480 h with an applied potential of 125 mV vs. OCP. Different stress corrosion cracking phenomena were observed according to the NaOH concentration. The rate of caustic IGSCC attack did not appear to increase monotonically with caustic concentrations, but peaked at a concentration between 4 and 50% caustic, or approximately 30% NaOH. Intergranular stress corrosion cracking was found for C600MA in 10, 20, and 30% NaOH solutions, while no cracking was observed in the 4 and 50% NaOH solutions. In 30% NaOH solution, transgrnular stress corrosion cracking was detected in C690TT, which may be related with the large amount of plastic strain (150% yield) and the applied potential (125 mV vs. OCP). The overall data clearly indicate that C600MA has the worst SCC resistance while K690TT offers the best resistance. There is also fairly good correlation between the caustic SCC susceptibility and some metallurgical parameters, particularly the grain size and the yield strength at room temperature. Specifically, materials having larger grain size and lower yield strength exhibited higher caustic SCC resistance.     

Single-view-based 3D facial reconstruction method robust against pose variations

The 3D Morphable Model (3DMM) and the Structure from Motion (SfM) methods are widely used for 3D facial reconstruction from 2D single-view or multiple-view images. However, model-based methods suffer from disadvantages such as high computational costs and vulnerability to local minima and head pose variations. The SfM-based methods require multiple facial images in various poses. To overcome these disadvantages, we propose a single-view-based 3D facial reconstruction method that is person-specific and robust to pose variations. Our proposed method combines the simplified 3DMM and the SfM methods. First, 2D initial frontal Facial Feature Points (FFPs) are estimated from a preliminary 3D facial image that is reconstructed by the simplified 3DMM. Second, a bilateral symmetric facial image and its corresponding FFPs are obtained from the original side-view image and corresponding FFPs by using the mirroring technique. Finally, a more accurate the 3D facial shape is reconstructed by the SfM using the frontal, original, and bilateral symmetric FFPs. We evaluated the proposed method using facial images in 35 different poses. The reconstructed facial images and the ground-truth 3D facial shapes obtained from the scanner were compared. The proposed method proved more robust to pose variations than 3DMM. The average 3D Root Mean Square Error (RMSE) between the reconstructed and ground-truth 3D faces was less than 2.6 mm when 2D FFPs were manually annotated, and less than 3.5 mm when automatically annotated.