Synthesis and electronic property of platinum nanowire and nanoparticle in mesoporous silica template

Platinum nanowires and nanoparticles were selectively synthesized in mesoporous silicas FSM-16 and HMM-1. The nanowires are 3 nm in diameter and several hundred nm to μm in length with high crystallinity. Pt nanowires and nanoparticles can be isolated by dissolving silica matrix with HF. The Pt wires extracted from organosilica HMM-1 have a nanonecklace structure, while the wires from siliceous FSM-16 have a nanorod structure. The extracted Pt nanoparticles (3 nm in size) on HOPG show the Coulomb staircase phenomena in STM/STS analysis. The mechanism for formation of the Pt nanowires is based on the migration of Pt ions in the mesoporous channels.     

Effects of support and additive on oxidation state and activity of Pt catalyst in propane combustion

The effects of support and additive on the oxidation state and catalytic activity of Pt catalyst in the low temperature propane combustion were systematically investigated on Pt/MgO, Pt/Al₂O₃ and Pt/SiO₂–Al₂O₃. The catalytic activity varied much with both support materials and additives. The catalyst on the more acidic support showed higher activity, and the catalytic activity on every support materials increased as the electronegativity of additives increased, while some additives decreased the activity. The oxidation state of platinum, estimated by white line intensity of Pt L_III-edge XANES spectrum, also varied with the support and additives, and additives with higher electronegativity greatly prevented the platinum from its oxidation under oxidising atmosphere. Among almost all the catalysts with various supports and various additives, a clear relationship was observed between the oxidation state of platinum and the catalytic activity; the more metallic platinum showed higher activity. Thus, it was concluded that the total electrophilic/electrophobic property derived from those of the support and additive controls the oxidation state of platinum, which intensively affects the catalytic activity; i.e. higher electrophilic property provides less oxidised platinum, resulting in high catalytic activity. The mechanism of this effect was also discussed on the basis of thermochemical data, and it was proposed that the electrophobic materials promote the noble metal oxidation since the noble metal oxo-anion such as PtO^δ− is more stabilised with electrophobic cation.     

Junction properties of polypyrrole containing a small amount of poly(ethylene oxide) with indium

A method to generate a porous region near the surface of a polymer is suggested. In this method the region near the surface is swollen by immersing the polymer for a short time in a solvent. Subsequently, the polymer is introduced in a nonsolvent (for the polymer) that is, however, miscible with the solvent. The formation of the porous region is a result of (1) the swelling accompanied by the disentanglement of the surface molecular chains, and the dissolution of some of them during the immersion in the solvent, and (2) the rapid extraction of the solvent from the swollen region by the nonsolvent. The porous surface provides a matrix into which a second incompatible monomer can be polymerized so that the two otherwise incompatible polymers can adhere to one another.     

Fabrication of Nonadditive Mica Ceramics by Hot Isostatic Processing

Powder compacts of synthetic mica (fluorphlogopite) encapsulated in a boro–silicate glass tube were isostatically hot–pressed in a Roy–Tuttle–type pressure vessel. Synthetic mica was sintered to a density of 2.60 g/cm³ (91.2% of theoretical density) without additives under 98 MPa of water at 800°C for 45 min.     

Extraction and implementation of muscle synergies in neuro-mechanical control of upper limb movement

This work faces the redundancy problem, a central concern in robotics, in a particular force-producing task by using muscle synergies to simplify the control. We extracted muscle synergies from human electromyograph signals and interpreted the physical meaning of the identified muscle synergies. Based on the human analysis results, we hypothesized a novel control framework that can explain the mechanism of the human motor control. The framework was tested in controlling a pneumatic-driven robotic arm to perform a reaching task. This control method, which uses only two synergies as manipulated variables for driving antagonistic pneumatic artificial muscles to generate desired movements, would be useful to deal with the redundancy problem; thus, suggesting a simple but efficient control for human-like robots to work safely and compliantly with humans.     

Partial oxidation of ethane to synthesis gas over Co-loaded catalysts

Attention has been increasingly paid to the partial oxidation of lower alkanes to synthesis gas, due to its intrinsic energy saving process. We studied the partial oxidation of ethane (POE) on Co loaded on various supports. The POE performance varied as follows: Y₂O₃, CeO₂, ZrO₂, La₂O₃  SiO₂, Al₂O₃, TiO₂ > MgO. Comparing Y₂O₃ and CeO₂, the carbon deposition during the POE was negligible on CeO₂ and therefore CeO₂ was the most preferable support. By changing space velocity and O₂ partial pressure, reaction mechanism of POE was studied and it was revealed that two-step mechanism was prevailing; combustion of ethane to H₂O and CO₂ and subsequent reforming of ethane with H₂O and CO₂ to synthesis gas. Co/CeO₂ catalyst exhibited high and stable catalytic activity for 10 h; high ethane conversion of 18% (maximum ethane conversion 20% at O₂/C₂H₆ = 0.2) with H₂ and CO selectivities of 93 and 84%, respectively.     

Evaluation for distance learning scheme on distributed multiple server system

A distributed multiple server system is designed and implemented with Web-DB based services for distance learning as well as emergency communication. The system has employed multiple servers located in a distributed campus network environment. Each server of the system has multi-core processors. With so-called “server virtualization” technology, some programs are executed in parallel (on the virtual servers) so that such a system can efficiently perform several functions. For example, two or more application services can be performed simultaneously as “cloud services” on the whole system. The system can provide distance learning scheme for educational tool, at the same time it can also support Web-based surveillance facilities for emergency contact. With qualitative and quantitative approach, trial evaluation of system has been performed in some classrooms of distributed campus. And users can obtain some good results from the above evaluation.     

Low-temperature selective reduction of NO with propene over alkaline-exchanged mordenites

Partially protonated alkaline mordenites showed higher activity per acid amount below 573 K than acidic zeolites for the selective reduction of NO with C₃H₆ in the presence of O₂, which can be related to a high concentration of NO₃ ^- species in the zeolite channels. This revised version was published online in July 2006 with corrections to the Cover Date.     

Sintering Kinetics at Isothermal Shrinkage: II, Effect of Y2O3 Concentration on the Initial Sintering Stage of Fine Zirconia Powder

The shrinkage behavior of fine zirconia powders containing 2.9 and 7.8 mol% Y₂O₃ was investigated to clarify the effect of Y₂O₃ concentration on the initial sintering stage. The shrinkage of powder compact was measured under both conditions of constant rates of heating (CRH) and constant temperatures. CRH measurements revealed that when the Y₂O₃ concentration of fine zirconia powder increased, the starting temperature of shrinkage shifted to a high temperature. Isothermal shrinkage measurements revealed that the increase in Y₂O₃ concentration causes the shrinkage rate to decrease. The values of activation energy ( Q ) and frequency-factor term (β₀) of diffusion at initial sintering were estimated by applying the sintering-rate equation to the isothermal shrinkage data. When the Y₂O₃ concentration increases, both Q and β₀ of diffusion increase. It is, therefore, concluded that the increase in Y₂O₃ concentration of fine zirconia powder decreases the shrinkage rate because of increasing Q of diffusion at the initial stage of sintering.