Enhancement of oxide break-up by implantation of fluorine inpoly-Si emitter contacted p+-n shallow junctionformation

In this study, it is demonstrated that the incorporation of fluorine can enhance poly-Si/Si interfacial oxide break-up in the poly-Si emitter contacted p⁺-n shallow junction formation. The annealing temperature for breaking up the poly-Si/Si interfacial oxide has been found to be as low as 900°C. As a result, the junction depth of the BF₂-implanted device is much larger than that of the boron-implanted device     

Surface leakage currents in SiN/sub x/ passivated AlGaN/GaN HFETs

A novel guarded surface leakage test structure is used to isolate the surface and bulk leakage contributions to gate current in AlGaN/GaN HFETs. Passivation with various recipes of SiN/sub x/ always resulted in the commonly observed increase in gate leakage, which was found to be dominated by bulk leakage through the AlGaN. However, high temperature deposited SiN/sub x/ recipes gave a 1-2 orders reduction in surface leakage, whereas low temperature deposition gave an increase. Gate lag measurements were found to correlate closely with the surface leakage component, giving direct evidence that the key device problem of current slump is associated with current flow at the AlGaN surface.     

Study of miscibility enhancement in poly(styrene‐co‐4‐vinylphenol)/poly(ethylene oxide) blends by the spin labelling method

The electron spin resonance (ESR) spectra of end‐group spin labelled poly(ethylene oxide) (SLPEO) using 2,2,6,6‐tetramethyl‐piperdine‐1‐oxyl nitroxide and its blends with poly(styrene‐co‐4‐vinylphenol) (STVPhs) of different hydroxyl contents were recorded over a wide temperature range. For a blend of SLPEO and pure polystyrene (PS), the ESR spectrum was composed of a single motion component, indicating that PS was immiscible with PEO. For blends composed of SLPEO and different‐hydroxyl‐content STVPhs, two spectral components with different motion rates were observed over a certain temperature range. The difference between the motion rates should be attributed to micro‐heterogeneity in the blends, with the faster rate corresponding to a nitroxide radical motion trapped in the PEO‐rich domain and the slower rate corresponding to a nitroxide radical motion trapped in the STVPh‐rich domain. Variations in the values of a number of the ESR parameters (T_a, T_d and T_50G) and the apparent activation energy (E_a) with hydroxyl content in the blends indicated that the miscibility of the blends increased with increasing hydrogen‐bonding density due to specific interactions between the hydroxyl groups in STVPh and the ether oxygens in PEO. Copyright © 2004 Society of Chemical Industry     

Facile synthesis of nitrogen and oxygen co-doped hierarchical porous carbon materials for high performance super capacitors

Journal of Porous Materials - Nitrogen and oxygen co-doped hierarchical porous carbons (NOPCs) is prepared by the pyrolysis of polyethylene glycol-200 (PEG) and triazine carbon forming agent (CFA)...     

无芯胶管的研制、工艺现状和发展建议

20世纪60年代初,我国胶管领域自主开发创新研制了无芯胶管制造技术,并且形成定型技术,一直沿用至今,笔者参与、见证了该产品从试验到投产的全过程。本文对该产品的工艺进行了新旧对比,提出了今后发展的建议。     

Reciprocating flow ion exchange part II: Application to saline water softening

The “hardness” components in sea water can be considerably reduced by means of a new economical fixed bed technique called “Reciprocating Flow Ion Exchange”, when used in conjunction with a closed cycle exchanger-evaporator system. Removal of 87.9% of the calcium and 54.5% of the magnesium in sea water has been obtained with an overall flow rate of 5.0 U. S. g. p. m./sq. ft. Results from bench scale and a 5,000 g. p. d. pilot plant were identical. The virtually continuous cyclic steady-state process requires a small amount of exchanger (0.5 to 2% of the usual ion exchange methods, such as conventional fixed beds or fluidized beds). The effects of variation in operating parameters are discussed.     

Preparation of Titanium Nitride/Alumina Laminate Composites

A preparation route for TiN/Al₂O₃ laminate composites has been described. A water-based process using Al₂O₃ and TiN slurries with solids contents of 40 and 35 vol%, respectively, was used to make TiN and Al₂O₃ tapes. The removal of the binder was monitored by weight-loss measurements in a thermogravimetry unit. Bodies composed of Al₂O₃ and TiN tapes were densified at temperatures of 1400° and 1500°C using the Spark Plasma Sintering^® (SPS) technique. Densities of >98% of the theoretical densities were approached. Crack-free and almost fully densified TiN/Al₂O₃ compacts were prepared by heating the burned-out green bodies to the final sintering temperature (1500°C) at a rate of 100°C/min, and with a holding time of 5–10 min, under a pressure of 75 MPa. The microstructures of the obtained compacts were studied using scanning electron microscopy. Grain sizes in the sintered Al₂O₃ and TiN compacts were similar to those of the precursor powders. Hardness and indentation fracture toughness were measured at room temperature, and the monolithic compacts as well as the laminate composites exhibited anisotropic mechanical behavior; i.e., the cracks propagated much more easily in a direction parallel to the laminas than perpendicular to them.