Rapid Reactive Synthesis and Sintering of Submicron TiC/SiC Composites through Spark Plasma Sintering

Submicrometer TiC/SiC composites were fabricated by a rapid reactive sintering process through spark plasma sintering (SPS) technique using the carbon, titanium, and nanosized-SiC powders without any additive. It was found that the composite could be sintered in a relatively short time (8 min at 1480°C) to 97.9% of theoretical density. After sintering, the phase constituents and microstructures of the samples were analyzed by X-ray diffraction techniques and observed by scanning electron microscopy. The effect of nanosized and microsized SiC additives on the microstructure of TiC/SiC composites was investigated.     

在OsO_4催化作用下烯烃的立体选择性氧化反应

四氧化锇是一种贵而毒性大的试剂。本文介绍催化剂量的四氧化锇在立体选择性高的烯烃氧化反应中的应用，为四氧化锇在有机合成中的应用，开辟了新的途径。     

Alternative hydrocarbon solvents for cottonseed extraction

Hexane has been used for decades to extract edible oil from cottonseed. However, due to increased regulations affecting hexane because of the 1990 Clean Air Act and potential health risks, the oil-extraction industry urgently needs alternative hydrocarbon solvents to replace hexane. Five solvents,n-heptane, isohexane, neohexane, cyclohexane, and cylopentane, were compared with commercial hexane using a benchscale extractor. The extractions were done with a solvent to cottonseed flake ratio of 5.5 to 1 (w/w) and a miscella recycle flow rate of 36 mL/min/sq cm (9 gal/min/sq ft) at a temperature of 10 to 45°C below the boiling point of the solvent. After a 10-min single-stage extraction, commercial hexane removed 100% of the oil from the flakes at 55°C; heptane extracted 100% at 75°C and 95.9% at 55°C; isohexane extracted 93.1% at 45°C; while cyclopentane, cyclohexane, and neohexane removed 93.3, 89.4, and 89.6% at 35, 55, and 35°C, respectively. Each solvent removed gossypol from cottonseed flakes at a different rate, with cyclopentane being most and neohexane least effective. Based on the bench-scale extraction results and the availability of these candidate solvents, heptane and isohexane are the alternative hydrocarbon solvents most likely to replace hexane. Presented in part at the AOCS Annual Meeting & Expo, Atlanta, Georgia, May 1994.     

超稠油污水处理技术的研究

以河油田曙I区社84污水处理站含超稠油污水为对象，选用最新研制开发的HL－005高效除油剂，研究了药剂浓度及复合比例对污水的处理效果。结果表明，在现有工艺条件下，使用该药A与C两组分复合先对污水进行预处理,然后A与B两组分复合对预处理后的水质进行净化，在技术上是可行的，完全达到水质净化指标。     

Rheology and Consolidation of Colloidal Alumina-Coated Silicon Nitride Suspensions

In an attempt to improve the colloidal processing of Si₃N₄ ceramics, we studied the rheology and consolidation of colloidal suspensions of Si₃N₄ particles (average particle size 0.7 μm) with small Al₂O₃ particles (average particle size 20 nm). It was found that at pH >7, the viscosity of the mixtures increased and then decreased with an increasing concentration of Al₂O₃. λpotential measurements, optical micrographs, and visible light absorptance measurement suggest that such viscosity behavior is due to clustering of Si₃N₄ particles bridged by the small Al₂O₃ particles. This is also supported by the Derjaquin-Landau-Verwey-Overbeek (DLVO) potential calculations that show the barrier height in the DLVO potential between Al₂O₃ and Si₃N₄ is small. The small barrier height under current experimental conditions stems from the small size of the Al₂O₃ particles. The small barrier height allows the thermal motion of the two kinds of particles to overcome the barrier and attach to each other. The adsorption of small Al₂O₃ particles on Si₃N₄ can occur even when both Al₂O₃ and Si₃N₄ carry the same sign of charges. The adsorption of Al₂O₃ on Si₃N₄ also increases the density of consolidated compacts.     

聚乙烯转光棚膜的加工及应用研究

本文对聚乙烯转光棚膜的加工和光转换剂的作用、配比关系及物理性能进行了讨论。     

液膜法去除水中Cr(Ⅵ)的研究

本文采用液膜去除回收水中Ｃｒ（Ⅵ）。对膜溶剂、载体、稳定剂的种类及用量进行了优选。用优选出的膜配方制成乳液处理含Ｃｒ（Ⅵ）水样，对制膜速度及时间、混合速度及时间、内外水相ｐＨ、膜内比及乳水比等操作条件对Ｃｒ（Ⅵ）去除率的影响进行了研究。     

有限元方法在离心机转鼓强度分析中的应用

在回顾以往转鼓强度分析的基础上 ,指出了目前转鼓有限元应力分析所存在的问题 ,给出了提高计算精度和保证模拟有效性的注意事项 ,并探讨了转鼓强度评定准则     

热含量不变量的SAR图像点特征变化检测

针对区域变化检测受分类器精度影响大、无法探测出内部细微变化这一问题,本文提出了基于热含量不变量的合成孔径雷达（Synthetic aperture radar,SAR）图像点特征变化检测.该方法利用热核特征,具有计算简便、矩阵扰动性小的特点,且有效地降低了噪声的干扰.由热核不变量的统计特性,采用期望极大化（Expectation maximization,EM）算法解决了SAR图像的自动变化检测.同时通过对权的讨论,给出了适用于SAR图像的权函数定义.对单波段单极化SAR与多极化SAR图像,本文算法相比于基于像素和似然比的方法,能够更快速更精确地检测到变化区域.     

铁谱分析技术在齿轮监控中的应用

从磨损机理出发，分析了齿轮传动的工作状况及失效形式，介绍了用铁谱分析技术监控齿轮传动的实施程序及注意事项，总结出判别齿轮磨损种类和磨损程度的方法，并提供了一些实验结果。