Core–shell NTC materials with low thermal constant and high resistivity for wide-temperature thermistor ceramics

Core–shell structures have been proposed to improve the electrical properties of negative-temperature coefficient (NTC) thermistor ceramics. In this work, Al₂O₃-modified Co_1.5Mn_1.2Ni_0.3O₄ NTC thermistor ceramics with adjustable electrical properties were prepared through citrate-chelation followed by conventional sintering. Co_1.5Mn_1.2Ni_0.3O₄ powder was coated with a thin Al₂O₃ shell layer to form a core–shell structure. Resistivity (ρ) increased rapidly with increasing thickness of the Al₂O₃ layer, and the thermal constant (B) varied moderately between 3706 and 3846 K. In particular, Co_1.5Mn_1.2Ni_0.3O₄@Al₂O₃ ceramic with 0.08 wt% Al₂O₃ showed the increase of ρ double, and the change in its B was less than 140 K. The Co_1.5Mn_1.2Ni_0.3O₄@Al₂O₃ NTC ceramics showed high stability, and their grain size was relatively uniform due to the protection offered by the shell. The aging coefficient of the ceramic was less than 0.2% after aging for 500 hours at 125°C. Taken together, the results indicate that as-prepared Co_1.5Mn_1.2Ni_0.3O₄@Al₂O₃ NTC ceramics with a core–shell structure may be promising candidates for application as wide-temperature NTC thermistor ceramics.     

Dual Inhibition of Pyruvate Dehydrogenase Complex and Respiratory Chain Complex Induces Apoptosis by a Mitochondria-Targeted Fluorescent Organic Arsenical in vitro and in vivo

Based on the potential therapeutic value in targeting mitochondria and the fluorophore tracing ability, a fluorescent mitochondria-targeted organic arsenical PDT-PAO-F16 was fabricated, which not only visualized the cellular distribution, but also exerted anti-cancer activity in vitro and in vivo via targeting pyruvate dehydrogenase complex (PDHC) and respiratory chain complexes in mitochondria. In details, PDT-PAO-F16 mainly accumulated into mitochondria within hours and suppressed the activity of PDHC resulting in the inhibition of ATP synthesis and thermogenesis disorder. Moreover, the suppression of respiratory chain complex I and IV accelerated the mitochondrial dysfunction leading to caspase family-dependent apoptosis. In vivo, the acute promyelocytic leukemia was greatly alleviated in the PDT-PAO-F16 treated group in APL mice model. Our results demonstrated the organic arsenical precursor with fluorescence imaging and target-anticancer efficacy is a promising anticancer drug.     

Flotation Behavior,Collector Adsorption Mechanism of Quartz and Feldspar-Quartz Systems Using PEA as a Novel Green Collector

Silicon - A novel green cationic surfactant Poly (propylene glycol) bis (2-aminopropyl ether) (PEA) with multiple amine groups was utilized as a collector for flotation separation of quartz from...     

A公司C产品研发项目范围管理研究

通过分析A公司在研发项目范围管理中所存在问题,提出研发项目范围管理的方法及其在C产品的应用实例,通过运用研发项目范围管理的工具和方法,改善产品开发流程,从而缩短新产品开发周期,提高响应市场的速度,并提高企业研发项目的管理能力。     

Mineralization of Para-Chlorobenzoic Acid in Water by Cobalt-Incorporated MCM-41 Catalyzed Ozonation

Cobalt-incorporated MCM-41(Co-MCM-41) was used as a heterogeneous catalyst for the ozonation of para-chlorobenzoic acid (p-CBA) in aqueous solution. Cobalt oxide supported on MCM-41(Co/MCM-41) was synthesized for comparison. Their textural properties were elucidated by various characterization techniques to understand the relationship between surface texture and catalytic activity. TOC removal at 60 min reached 91% with Co-MCM-41, 83% with Co/MCM-41 and only 52% with ozone alone, respectively. Observations from diffuse reflection spectroscopy demonstrated that different metal phases were formed in these cobalt-modified molecular sieves samples. Radical scavenger experiments indicated the formation of hydroxyl radicals that were responsible for the effective degradation of p-CBA. An integrated approach to the catalytic mechanism was proposed by considering the variation of pH in the course of ozonation as well as its subsequent influence on the dissociation of targeted compounds and surface charge of the catalyst. In the reusability experiments, the reused Co-MCM-41 was able to regain the same catalytic capability as the fresh one within 5 cycles. X-ray photoelectron spectroscopy results indicated that a part of Co²⁺ was oxidized to Co³⁺ after oxidation reaction.     

微型步进马达线架组自动卷线设备设计

微型步进马达线圈组卷线上下料基本靠手动作业,效率低下,同时因工人技术水平的不同造成产品品质不稳定的问题多发.为此专门设计了微型步进马达线圈组自动卷线及上下料设备.通过结合现阶段的先进工业技术,采用振动盘分离区分进料,多机构并联三菱PLC及威纶人机界面触摸屏研发了此微型步进马达线圈组自动上下料及卷线设备.通过该设备实现了微型步进马达因工人不足导致产能减少和品质多发问题,减少企业成本,提升产品品质.     

Oxygen transport,thermal and electrochemical properties of NdBa0.5Sr0.5Co2O5+δ cathode for SOFCs

In this study, the crystal structure, thermal, oxygen transport, electrical conductivity and electrochemical properties of the perovskite NdBa_0.5Sr_0.5Co₂O_5+δ (NBSC55) are investigated. In the temperature range of 250 °C–350 °C, the weight loss upon heating was due to a partial loss of lattice oxygen and along with a reduction of Co⁴⁺ to Co³⁺. The tend of weight-loss slows down as temperature increased above 350 °C indicating a reduction of Co³⁺ to Co²⁺ during this stage. The oxygen migration is dominated by surface exchange process at high temperature range (650-800 °C); however, the bulk diffusion process prevails at low temperature range (500–600 °C). For long-term testing, the polarization resistance of NBSC55 increases gradually form 3.13 Ω cm² for 2 h to 3.34 Ω cm² for 96 h at 600 °C and an increasing-rate for polarization resistance is around 0.22% h^?1. The power density of the single cell with NBSC55 cathode reached 341 mW cm^?2 at 800 °C.