Spatiotemporal Magnetocaloric Microenvironment for Guiding the Fate of Biodegradable Polymer Implants

The degradation behavior of implants is significantly important for bone repair. However, it is still unprocurable to spatiotemporally regulate the degradation of the implants to match bone ingrowth. In this paper, a magneto-controlled biodegradation model is established to explore the degradation behavior of magnetic scaffolds in a magnetothermal microenvironment generated by an alternating magnetic field (AMF). The results demonstrate that the scaffolds can be heated by magnetic nanoparticles (NPs) under AMF, which dramatically accelerated scaffold degradation. Especially, magnetic NPs modified by oleic acid with a better interface compatibility exhibit a greater heating efficiency to further facilitate the degradation. Furthermore, the molecular dynamics simulations reveal that the enhanced motion correlation between magnetic NPs and polymer matrix can accelerate the energy transfer. As a proof-of-concept, the feasibility of magneto-controlled degradation for implants is demonstrated, and an optimizing strategy for better heating efficiency of nanomaterials is provided, which may have great instructive significance for clinical medicine.     

Toughness and R-curve behaviour of laminated Si3N4/SiCw ceramics

Laminated Si₃N₄/SiC_w ceramics were successfully prepared by tape casting and hot-pressing. Its mechanical properties were measured and the impact resistance was discussed. The toughness of the laminated Si₃N₄/SiC_w ceramics was 13.5 MPa m^1/2, which was almost 1.6 times that of Si₃N₄/SiC_w composite ceramics, namely 8.5 MPa m^1/2. Moreover, the indentation strength of laminated Si₃N₄/SiC_w ceramics was not sensitive to increasing indentation loads and exhibited a rising R-curve behaviour, indicating that the laminated Si₃N₄/SiC_w ceramics had excellent impact resistance. The improved toughness and impact resistance of laminated Si₃N₄/SiC_w ceramics was attributed to the residual stress caused by a thermal expansion coefficient mismatch between the different layers, resulting in crack deflection and bridging of SiC whiskers in the interface layer, thus consuming a large amount of fracture work.     

Synthesis of nanopowders with low agglomeration by elaborating Φ values for producing Gd2O3-MgO nanocomposites with extremely fine grain sizes and high mid-infrared transparency

Refining ceramic microstructures to the nanometric range to minimize light scattering provides an interesting methodology for developing novel optical ceramic materials. In this work, we reported the fabrication and properties of a new nanocomposite optical ceramic of Gd₂O₃-MgO. The citric acid sol-gel combustion method was adopted to fabricate Gd₂O₃-MgO nanocomposites with fine-grain sizes, dense microstructures and homogeneous phase domains. Nanopowders with low agglomeration and improved sinterability can be obtained by elaborating Φ values. Further refining of the microstructure of the nanocomposites was achieved by elaborating the hot-pressing conditions. The sample sintered at 65 MPa and 1300 °C showed a quite high hardness value of 14.3 ± 0.2 GPa, a high transmittance of 80.3 %–84.7 % over the 3?6 μm wavelength range, due mainly to its extremely fine-grain size of Gd₂O₃ and MgO (93 and 78 nm, respectively) and high density.     

儿童用品TBT通报数据可视化预警研究

探索采用数据可视化技术分析儿童用品TBT通报数据,以可视化图形图像呈现通报热点并揭示趋势信息,提出对策与建议,助力为儿童用品产业升级、TBT预警数据分析和信息传播工作提供新思路,提高中小企业的国外市场准入机会。     

复杂难选铁矿石悬浮磁化焙烧-高效分选技术

针对传统铁矿石磁化焙烧技术与装备存在焙烧产品质量差、产能低、能耗高和环境污染严重等问题，创造性提出了一种“预热-蓄热还原-再氧化”悬浮磁化焙烧新工艺。该工艺具有原料适应性广、焙烧产品质量均匀、回收率高、生产能耗低、无污染等特点，适合处理赤铁矿、褐铁矿、菱铁矿及其混合型难选铁矿石。通过多年的潜心基础研究与技术攻关，形成了非均质矿石颗粒悬浮态流动控制、蓄热式高效低温还原、铁物相精准调控与余热同步回收等一系列关键技术，建成了500kg/h复杂难选铁矿石悬浮磁化焙烧-高效分选半工业试验平台。     

急性炎性疾病患者乳酸林格氏液液体动力学

目的:探索炎性疾病患者的乳酸林格氏液（Ringer's lactate,RL）液体动力学特征以及炎性生物标记物是否可以作为协变量影响RL分布和排泄。方法:本研究为前瞻性队列研究。选择40例美国麻醉医师分级（ASA）I-II级，腹腔镜下择期胆囊切除术（胆囊炎组，n=20）或者腹腔镜下急诊阑尾切除术（阑尾炎组，n=20）。所有患者麻醉诱导前开始输注RL，按15 mL/kg，35 min内输毕。采用酶联免疫（enzyme-linked immunosorbent assay,ELISA）方法测定血浆炎症（TNF-α,IL-10和CRP）或者内皮损伤生物标记物（syndecan-1,SDC-1）；利用血红蛋白（Hb）稀释-时间曲线和尿量，使用Phoenix软件，采用非线性混合效应模型分析计算RL液体动力学参数和协变量的影响。结果:与胆囊炎组相比，阑尾炎组RL从组织间隙到血浆的转运速率常数（k21）显著降低（14×10-3min-1 versus 35×10-3min-1;P=0.012）。阑尾炎组C反应蛋白（CRP）升高［中位数38.1(1.8-143.6) μg/mL versus 1.3(0.1-159.0) μg/mL;P<0.001］；与清醒状态相比，麻醉期间（输液开始后30～45 min），液体从中央室中到外周室的转运速率常数（k12）显著增加（57×10-3min-1 versus 32×10-3min-1；P<0.01）。清除速率常数（k10）降低90%（0.6×10-3min-1 versus 5.3×10-3min-1;P<0.001）。无论在清醒状态还是麻醉状态下低血压均能降低液体清除；炎症或者内膜损伤的生物标记物不能作为显著影响RL液体动力学参数的协变量。结论:阑尾炎或者胆囊炎患者术前输入液体后“炎症反应的生物标记物”不是RL的液体动力学的协变量，但是两组患者中，全身麻醉期间输入液体的清除率下降。     

Cathode plasma electrolytic deposition of Al2O3 coatings doped with SiC particles

Semiconductor particles doped Al₂O₃ coatings were prepared by cathode plasma electrolytic deposition in Al(NO₃)₃ electrolyte dispersed with SiC micro- and nano-particles (average particle sizes of 0.5–1.7?µm and 40?nm respectively). The effects of the concentrations and particle sizes of the SiC on the microstructures and tribological performances of the composite coatings were studied. In comparison with the case of dispersing with SiC microparticles, the dispersion of SiC nanoparticles in the coatings was more uniform. When the concentration of SiC nanoparticles was 5?g/L, the surface roughness of the composite coating was reduced by 63%, compared with that of the unmodified coating. Friction results demonstrated that the addition of 5?g/L SiC nanoparticles reduced the friction coefficient from 0.60 to 0.38 and decreased the wear volume under dry friction. The current density and bath voltage were measured to analyze the effects of SiC particles on the deposition process. The results showed that the SiC particles could alter the electrical behavior of the coatings during the deposition process, weaken the bombardment of the plasma, and improve the structures of the coatings.