Facile modifications of polyimide via chloromethylation: II. Synthesis and characterization of thermocurable transparent polyimide having methylene acrylate side groups

From chloromethylated polyimide, a useful starting material for modification of aromatic polyimides, a thermocurable transparent polyimide having acrylate side groups was prepared. In the presence of 1,8‐diazabicyclo[5,4,0]undec‐7‐ene, chloromethylated polyimide was esterified with acrylic acid to synthesize poly(imide methylene acrylate). The polymer was soluble in organic solvent, which makes it possible to prepare a planar film by spin coating. The polymer film became insoluble after thermal treatment at 230 °C for 30 min. Optical transparency of the film at 400 nm (for 1 µm thickness) was higher than 98 % and not affected by further heating at 230 °C for 250 min. Adhesion properties measured by the ASTM D3359‐B method ranged from 4B to 5B. Preliminary results of planarization testing showed a high degree of planarization (DOP) value (>0.53). These properties demonstrate that poly(imide methylene acrylate) could be utilized as a thermocurable transparent material in fabricating display devices such as TFT‐LCD. Copyright © 2004 Society of Chemical Industry     

Properties of poly(ethylene terephthalate)–poly(ethylene naphthalene 2,6‐dicarboxylate) blends with montmorillonite clay

The production and properties of blends of poly(ethylene terephthalate) (PET) and poly(ethylene naphthalene 2,6‐dicarboxylate) (PEN) with three modified clays are reported. Octadecylammonium chloride and maleic anhydride (MAH) are used to modify the surface of the montmorillonite–Na⁺ clay particles (clay–Na⁺) to produce clay–C18 and clay–MAH, respectively, before they are mixed with the PET/PEN system. The transesterification degree, hydrophobicity and the effect of the clays on the mechanical, rheological and thermal properties are analysed. The PET–PEN/clay–C18 system does not show any improvements in the mechanical properties, which is attributed to poor exfoliation. On the other hand, in the PET–PEN/clay–MAH blends, the modified clay restricts crystallization of the matrix, as evidenced in the low value of the crystallization enthalpy. The process‐induced PET–PEN transesterification reaction is affected by the clay particles. Clay–C18 induces the largest proportion of naphthalate–ethylene–terephthalate (NET) blocks, as opposed to clay–Na⁺ which renders the lowest proportion. The clay readily incorporates in the bulk polymer, but receding contact‐angle measurements reveal a small influence of the particles on the surface properties of the sample. The clay–Na⁺ blend shows a predominant solid‐like behaviour, as evidenced by the magnitude of the storage modulus in the low‐frequency range, which reflects a high entanglement density and a substantial degree of polymer–particle interactions. Copyright © 2005 Society of Chemical Industry     

Morphology and properties of poly[2‐methoxy‐5‐(2′‐ethyl‐hexyloxy)‐para‐phenylene vinylene]/silica nanoparticle hybrid films

Poly[2‐methoxy‐5‐(2′‐ethyl‐hexyloxy)‐para‐phenylene vinylene] (MEH‐PPV)/silica nanoparticle hybrid films were prepared and characterised. Three kinds of materials were compared: parent MEH‐PPV, MEH‐PPV/silica (hybrid A films), and MEH‐PPV/coupling agent MSMA/silica (hybrid B films), in which MSMA is 3‐(trimethoxysilyl) propyl methacrylate. It was found that the hybrid B films could significantly prevent macrophase separation, as evidenced by scanning electron and fluorescence microscopy. Furthermore, the thermal characteristics of the hybrid films were largely improved in comparison with the parent MEH‐PPV. The UV‐visible absorption spectra suggested that the incorporation of MSMA‐modified silica into MEH‐PPV could confine the polymer chain between nanoparticles and thus increase the conjugation length. The photoluminescence (PL) studies also indicated enhancement of the PL intensity and quantum efficiency by incorporating just 2 wt% of MSMA‐modified silica into MEH‐PPV. However, hybrid A films did not show such enhancement of optoelectronic properties as the hybrid B films. The present study suggests the importance of the interface between the luminescent organic polymers and the inorganic silica on morphology and optoelectronic properties. Copyright © 2004 Society of Chemical Industry     

Properties of nanoporous organosilicate hybrid thin films with a bimodal pore size distribution

Low dielectric poly[methylsilsesquioxane‐ran‐trifluoropropylsilsesquioxane‐ran‐(2,4,6,8‐tetramethyl‐2,4,6,8‐tetraethylenecyclotetrasiloxane)silsesquioxane]s {P[M‐ran‐TFP‐ran‐(TCS)]SSQs} having various compositions were synthesized using trifluoropropyl trimethoxysilane, methyl trimethoxysilane and 2,4,6,8‐tetramethyl‐2,4,6,8‐tetra(trimethoxysilylethyl)cyclotetrasiloxane. The chemical composition of the polymers and the content of SiOH end‐groups were controlled by adjusting the reaction conditions, and they were characterized by ¹H‐NMR. The thermally decomposable trifluoropropyl groups on the P[M‐ran‐TFP‐ran‐(TCS)]SSQ backbone and heptakis(2,3,6‐tri‐O‐methyl)‐β‐cyclodextrin (CD) were employed as pore generators. The dielectric constants of the porous CD/P[M‐ran‐TFP‐ran‐(TCS)]SSQ films were in the range 2.0–2.7 (at 100 kHz) depending on the concentration of the porogens, and showed no change over 4 days under aqueous conditions. The pore size of the films showed a bimodal distribution, with diameters of ca 0.5–1.0 nm for those originating from the trifluoropropyl groups and 1.7 nm from the CD. The elastic modulus and hardness of the 30 vol% CD‐blended film with a dielectric constant of 2.26 were 2.40 and 0.38 GPa, respectively, as determined by a nanoindenter. Copyright © 2005 Society of Chemical Industry     

Preparation of flexible polyhedral particles via concentrated emulsion templating polymerization

This paper presents recent efforts on the preparation of flexible polyhedral particles via concentrated emulsion templating polymerization in which the hydrophilic monomer (acrylamide) and hydrophobic monomer (butyl acrylate) are polymerized simultaneously in the continuous and dispersed phase, respectively. Such templating polymerization has been enhanced in our systems owing to the introduction of acrylamide monomer and their higher polymerization rate in continuous phase as compared with butyl acrylate in dispersed phase. Diffusion between the different phases was also inhibited. Furthermore, the stability of the concentrated emulsion and the molecular weight of the produced poly(butyl acrylate) were found to be significantly affected by the amount of redox initiator. The morphology of the particles could be controlled by varying the volume fraction of the dispersed phase and the polyhedral particles were achieved at higher volume fraction. Copyright © 2005 Society of Chemical Industry     

Ring‐opening polymerization of D,L‐lactide by rare earth 2,6‐dimethylaryloxide

Ring‐opening polymerization of D,L ‐lactide (LA) has been successfully carried out by using rare earth 2,6‐dimethylaryloxide (Ln(ODMP)₃) as single component catalyst or initiator for the first time. The effects of different rare earth elements, solvents, monomers and catalyst concentration as well as polymerization temperature and time on the polymerization were investigated. The results show that La(ODMP)₃ exhibits higher activity to prepare poly(D,L ‐lactide) (PLA) with a viscosity molecular weight of 4.5 × 10⁴ g mol^?1 and the conversion of 97 % at 100 °C in 45 min. The catalytic activity of Ln(ODMP)₃ has following sequence: La > Nd > Sm > Gd > Er > Y. A kinetic study has indicated that the polymerization is first order with respect to both monomer and catalyst concentration. The apparent activation energy of the polymerization of LA with La(ODMP)₃ is 69.6 kJ mol^?1. The analyses of polymer ends indicate that the LA polymerization proceeds according to ‘coordination–insertion’ mechanism with selective cleavage of the acyl–oxygen bond of the monomer. Copyright © 2004 Society of Chemical Industry     

Optimal transfer trees and distinguishing trees for testing observable nondeterministic finite-state machines

The fault-state detection approach for blackbox testing consists of two phases. The first is to bring the system under test (SUT) from its initial state to a targeted state t and the second is to check various specified properties of the SUT at t. This paper investigates the first phase for testing systems specified as observable nondeterministic finite-state machines with probabilistic and weighted transitions. This phase involves two steps. The first step transfers the SUT to some state t' and the second step identifies whether t' is indeed the targeted state t or not. State transfer is achieved by moving the SUT along one of the paths of a transfer tree (TT) and state identification is realized by using diagnosis trees (DT). A theoretical foundation for the existence and characterization of TT and DT with minimum weighted height or minimum average weight is presented. Algorithms for their computation are proposed.     

Note on ‘Construction of Double Sampling s‐Control Charts for Agile Manufacturing’

He and Grigoryan (Quality and Reliability Engineering International 2002; 18 :343–355) formulated the design of a double‐sampling (DS) s control chart as an optimization problem and solved it with a genetic algorithm. They concluded that the DS s control charts can be a more economically preferable alternative in detecting small shifts than traditional s control charts. We explain that, since they only considered the average sample size when the process is in control, their conclusion is questionable. Copyright © 2006 John Wiley & Sons, Ltd.