Highly active sites of low spin FeⅡN4species:The identification and the ORR performance

Over recent years,catalytic materials of Fe-N-C species have been recognized being active for oxygen reduction reaction(ORR).However,the identification of active site remains challenging as it generally involves a pyrolysis process and mixed components being obtained.Herein Fe₃C/C and Fe₂N/C samples were synthesized by temperature programmed reduction of Fe precursors in 15%CH₄/H₂and pure NH₃,respectively.By acid leaching of Fe₂N/C sample,only single sites of FeN₄species were presented,providing an ideal model for identification of catalytic functions of the single sites of FeN₄in ORR.A correlation was conducted between the concentration of Fe^ⅡN₄in low spin state by Mossbauer spectra and the kinetic current density at 0.8 V in alkaline media,and such a structure-performance correlation assures the catalytic roles of low spin Fe^ⅡN₄ species as highly active sites for the ORR.     

NH_3-OH体系中共沉淀法同时回收钕铁硼废料中Nd-Pr-Co-Fe

为了避免回收单一钕铁硼废料中有价元素带来的操作复杂和资源浪费等问题,本研究采用共沉淀法共沉淀出钕铁硼废料中的有价元素Me(Nd,Pr,Co,Fe),制备可用于生产再生钕铁硼的原料;根据质量守恒和同时平衡原理,采用MATLAB软件建立Me(Nd,Pr,Co,Fe)-OH--NH3热力学模型,绘制lg[Me]-p H曲线模拟共沉淀工艺,并根据模拟结果确立了共沉淀工艺;模拟和实验的结果表明:根据lg[Me]-p H模拟结果可以确立一步共沉淀法的p H:6~10,Fe3+比Fe2+更易于沉淀完全;在上述条件下获得的共沉淀粉末主相均为Nd,Pr,Co,Fe的化合物,且有价元素的百分比含量均大于99.4%;其中,当p H值在8左右时回收率最高,在该条件下金属元素Me(Nd,Pr,Co,Fe)的沉淀效率分别为:98.7%,99.9%,93.6%,99.9%。该结果也表明共沉淀法工艺不仅高效,而且所制备的共沉淀粉末可以满足制备二次钕铁硼的需要。     

搅拌式风力致热装置启动性能研究

搭建搅拌式风力致热试验台,以自制的2种致热器为研究对象,使其分别在3个不同平均角加速度24.92、14.66、8.04 rad/s2下启动。通过动态扭矩测试仪和数据采集仪测试记录致热器启动阶段的相关数据。结果表明:致热器启动时所需扭矩与角加速度的一次方、转速、叶片半径的二次方成正比,同时得出这些因素之间的关系式;满负荷时,启动扭矩会出现一个峰值,且角加速度越大峰值越大,自然风必须提供峰值以上的扭矩,否则装置无法启动。     

核算前移在冶炼企业优化成本控制中的应用

针对国际黄金价格的走低,黄金冶炼企业如何在激烈的市场竞争中寻求更大的利润空间,优化成本控制显得尤为重要。以某冶炼厂为例,阐述核算前移在优化企业成本控制中的应用,以达到降本增效的目的,实现企业利润的最大化。     

Core–shell NTC materials with low thermal constant and high resistivity for wide-temperature thermistor ceramics

Core–shell structures have been proposed to improve the electrical properties of negative-temperature coefficient (NTC) thermistor ceramics. In this work, Al₂O₃-modified Co_1.5Mn_1.2Ni_0.3O₄ NTC thermistor ceramics with adjustable electrical properties were prepared through citrate-chelation followed by conventional sintering. Co_1.5Mn_1.2Ni_0.3O₄ powder was coated with a thin Al₂O₃ shell layer to form a core–shell structure. Resistivity (ρ) increased rapidly with increasing thickness of the Al₂O₃ layer, and the thermal constant (B) varied moderately between 3706 and 3846 K. In particular, Co_1.5Mn_1.2Ni_0.3O₄@Al₂O₃ ceramic with 0.08 wt% Al₂O₃ showed the increase of ρ double, and the change in its B was less than 140 K. The Co_1.5Mn_1.2Ni_0.3O₄@Al₂O₃ NTC ceramics showed high stability, and their grain size was relatively uniform due to the protection offered by the shell. The aging coefficient of the ceramic was less than 0.2% after aging for 500 hours at 125°C. Taken together, the results indicate that as-prepared Co_1.5Mn_1.2Ni_0.3O₄@Al₂O₃ NTC ceramics with a core–shell structure may be promising candidates for application as wide-temperature NTC thermistor ceramics.     

大口径光学元件装夹转运结构设计及分析

为了实现大口径光学元件的安全装夹、转运,通过光学元件开槽与不开槽两种装夹方式的分析,得出开槽夹紧转运方式将带来微裂纹、应力集中、成本高等缺陷,提出了利用摩擦力克服光学零件的重力和惯性力的低应力装夹转运方案。通过对光学元件低应力夹紧结构设计,并利用有限元分析方法,得到不开槽装夹方式下,光学元件的最大主应力为1.11 MPa,最大切应力为0.73 MPa,远低于光学元件破坏的强度极限,且受力均匀,无应力集中现象。     