Mg-1．5Mn-1．5Y-3Sn合金显微组织及力学性能研究

采用挤压结合固溶时效方法,对铸态Mg-1．5Mn-1．5Y-3Sn合金进行了处理。利用扫描电镜、X射线衍射仪及显微硬度计等,研究该本合金在不同的热处理工艺下的显微组织及力学性能。试验结果表明,在铸态下,本合金的显微组织由α-Mg基体、大量颗粒状的第二相Mg2Sn、少量的针状YMg—Sn相组成。经过挤压和固溶后,微观组织中出现纤维状条纹,获得最佳力学性能的时效时间是66h（〈180℃）。拉伸试验表明,最大延伸率8为7％,抗拉强度约为230MPa。断口分析发现,合金的断裂方式主要为准解理断裂。     

Preparation and Properties of a New Mediumdensity and High-strength Ceramic Proppant

Based on the needs of the market,a new 52 MPa medium-density and high-strength ceramic proppant was prepared by adopting third grade bauxite and clay as raw materials and using the solid phase sintering method,and the effect of the firing temperature on the microstructure,phase composition and mechanical properties of the ceramic proppant was studied. The broken resistance mechanism of this ceramic proppant was also discussed. The results show that the main phases of the prepared ceramic proppant are mullite and corundum; the broken rates are 3. 92% and 7. 21% under 52 MPa and69 MPa,respectively.     

马坑铁矿地下水流场变化特征与疏干防治对策

福建马坑铁矿属水文地质条件复杂的顶板直接岩溶充水矿床,开采以来不断发生的岩溶水涌（突）水灾害严重制约着矿区安全生产。地下水流场的形态是矿区水文地质条件的综合反映,利用不同时期的岩溶水动态观测数据,绘制并分析了矿区多个时段岩溶水的流场形态,总结发现随着矿区岩溶水不断疏干,矿区岩溶水系统补给、径流与排泄更多受断层破碎带的控制,同时也因岩溶发育及岩性的不同而有所差异,地下水流场形态变化在空间上不仅没有很好的一致性,也明显地制约着矿区岩溶水的全面疏干。针对矿区流场形态变化的主控因素,提出了具有针对性的疏干防治对策。     

土工击实试验方法的研究

击实试验是建筑物地基、道路地基、室内地坪及场地平整等施工和验收的重要依据。笔者基于工作中积累的实际操作经验,介绍了击实试验的方法及其要点,对其进行了研究,以期获得对施工有指导意义的数据。     

半绝缘砷化镓单晶中的晶体缺陷

通过化学腐蚀、金相显微观察、透射电子显微镜、扫描电镜和X射线异常透射形貌等技术,研究了半绝缘砷化镓单晶中的位错和微缺陷.实验发现用常规液封直拉法制备出的直径大于或等于75 mm的半绝缘砷化镓单晶在晶体周边区域,一般都有由高密度位错的运动和反应而形成的蜂窝状网络结构,并且位错和微缺陷之间,有着强烈的相互作用,位错吸附微缺陷,微缺陷缀饰位错.     

晶态合金Fe_(79)Si_7B_(14)、Fe_(83)Si_4B_(10)C_3结构弛豫的穆斯堡尔效应研究

本文应用示差热分析和穆斯堡尔谱学方法,对非晶态合金Fe_(79)Si_7B_(14)和Fe_(83)Si_4B_(10)C_3的结构弛豫过程进行了实验研究,认为其结构弛豫过程包括拓扑短程序弛豫、化学短程序弛豫和基体金属相形核长大三种形式的结构变化。     

Mossbauer Effect of Rapidly Quenched Al-Fe-V-Si-Mm Alloys

ＭｏｓｓｂａｕｅｒＥｆｆｅｃｔｏｆＲａｐｉｄｌｙＱｕｅｎｃｈｅｄＡｌ－Ｆｅ－Ｖ－Ｓｉ－ＭｍＡｌｌｏｙｓＷａｎｇＪｉａｎｑｉａｎｇ（王建强），ＣｈａｏＹｕｅｓｈｅｎｇ（晁月盛），ＺｅｎｇＭｅｉｇｕａｎｇ（曾梅光），ＺｈａｎｇＢａｏｊｉｎ（张宝金），Ｃｈ...     

混合烧结高散热导电胶的封装应用及性能

为满足中大尺寸背面裸硅芯片的封装应用及其高散热需求,开发了一种新型混合烧结高散热导电胶,该新型导电胶以有机二元酸表面活化的银粉颗粒、丙烯酸树脂和其他有机添加剂为原料混合制备而成.采用新型导电胶将6 mm×6 mm裸硅芯片粘接到方形扁平无引脚封装键合(QFNWB)产品上,并进行了导电胶黏度测量、X射线无损检测、导电胶和芯片粘接的破坏性推力测试、导热系数测试和可靠性试验.研究结果表明,该导电胶触变指数为7.2,烘烤后无明显气孔产生,6 mm×6 mm裸硅芯片粘接的破坏性推力为343 N,导热系数高达15 W/(m·K).与常规导电胶相比,其导热性能优异,且解决了烧结银导电胶无法应用于中大尺寸背面裸硅芯片的问题,满足产品的高散热和高可靠性要求.     

一种基于分块压缩感知的鲁棒图像散列算法

图像散列算法是一种把数字图像映射为一个基于内容的简短二进制比特串的技术,它具有鲁棒性、安全性、紧凑性和单向性等特点,已被广泛应用于图像鉴别与图像识别领域中。本文提出一种基于分块压缩感知的鲁棒图像散列算法,其设计利用了压缩感知采样阶段的计算保密及线性运算的特点。该算 法通过对图像进行分块,利用压缩感知理论在密钥的控制下将图像块随机投影为一个测量值向量序列,并把每个测量值向量量化为一个比特,得到一个长度可由分块策略调整的二进制散列值。实验结果表明,本文算法在鲁棒性、安全性和运算速度等方面具有良好的性能。     

Solution‐Growth Strategy for Large‐Scale “CuGaO2 Nanoplate/ZnS Microsphere” Heterostructure Arrays with Enhanced UV Adsorption and Optoelectronic Properties

Intrinsically p‐type conductivity and a wide bandgap of ≈3.6 V endow inorganic delafossite CuGaO₂ with great promise for fabricating high‐performance UV photodetectors. Nevertheless, CuGaO₂‐based optoelectronic devices hindered because the intrinsic direct transitions are symmetry forbidden in CuGaO₂. This study reports a large‐area synthesis of “CuGaO₂ nanoplate/ZnS microsphere” heterostructure arrays using a facile solution‐based strategy associated with an oil/water interfacial self‐assembly approach. It is found that a large number of ZnS microspheres with a polycrystalline structure grow on the top surface of CuGaO₂ hexagonal platelets through Ostwald ripening mechanism, forming high‐density p–n heterojunctions. A parabolic dependence between the size of ZnS microsphere and the growth time is confirmed in this growth. The UV light adsorption of the heterostructure CuGaO₂/ZnS thin film is two times higher than that of the pristine CuGaO₂ thin film. Furthermore, the as‐designed “CuGaO₂ nanoplate/ZnS microsphere” heterostructure arrays exhibit enhanced photoresponse properties. This work offers a new insight into the rational design of optoelectronic devices from the synergetic effect of p‐type 2D nanoplates as well as n‐type nanostructures such as ZnS, ZnO, CdS, and CdO.