Cumulant calculations of thermodynamic quantities for the Hubbard and the emery model

The calculations of the first paper suggesting phase separation in the Hubbard model [2] are performed under modern computer facilties for the one and three-band Hubbard model. High-temperature approximations for specific heat and static correlation functions are obtained. The latter show, at these high temperatures, no tendency to phase separate in the same way as in the cited paper because our spin parallel nearest-neighbor charge correlation function is negative for all doping values. The spin antiparallel correlation function has positive and negative values for different doping regimes.Extension of this work to higher levels of iterations and to other correlation functions is in progress.     

Residual stresses and transformation toughening in MoSi2 composites reinforced with partially stabilized zirconia

The results of study of the effects of yttria stabilization (0–6 mol.%) on the room-temperature fracture behavior and toughening mechanisms in zirconia-reinforced MoSi₂ are presented in this paper. Transformation toughening is shown to occur only in composites reinforced with zirconia particles stabilized with 2 mol.% yttria. However, the fracture toughness levels are comparable in the other composites with yttria levels between 0 and 6 mol.%. Toughening in the other composites is attributed to the combined effects of residual stress, microcrack shielding/anti-shielding and/or crack deflection. A rigorous micromechanics-based model is presented for the estimation of residual stress levels in brittle materials reinforced with phases that can transform during cooling or under stress. The model is applied successfully to the rationalization of the observed fracture and toughening phenomena.     

Effect of type of processing on the microstructural features and mechanical properties of Al-Cu/SiC metal matrix composites

In this study, an aluminum based metallic matrix (Al-2wt.% Cu) was reinforced with SiC particulates using a conventional casting technique and a new disintegrated melt deposition technique. Microstructural characterization studies conducted on the samples taken from disintegrated melt deposition technique revealed a more uniform distribution of SiC particulates and good interfacial integrity between SiC particulates and metallic matrix when compared to the conventionally cast composite samples. Results of ambient temperature mechanical tests demonstrate an increase in 0.2% YS and ultimate tensile strength of samples taken from disintegrated melt deposition technique when compared with the unreinforced and conventionally cast composite samples. The results of microstructural characterization and mechanical testing were finally rationalized in terms of the nature of processing technique employed to reinforce Al-2wt.% Cu metallic matrix with SiC particulates.     

Importance of out-of-plane dispersion of the excitation spectrum of superconducting bilayers with Josephson coupling

We study the effect of Josephson coupling between adjacent superconducting layers on the BCS energy spectrum. We find that the interference between the gap functions of two layers can lead to vanishing condensation energy for perpendicular momenta corresponding to the formation of standing waves. We therefore predict a conventional energy spectrum for large interlayer spacings, if the gap of the single layers has no nodes, and in all cases a gapless spectrum for small spacings. Within the experimental error, our numerical results account for the low-temperature dependence of the penetration depth reported in Nd_1.85Ce_0.15CuO₄ and YBa₂Cu₃O_6.9.     

Superconductivity in nearly single-phase Bi-Pb-Sr-Ca-Cu-O samples with different nominal compositions

The preparation conditions, phase composition, and superconducting properties of Bi-Pb-Sr-Ca-Cu oxide materials from different nominal compositions have been investigated. Nearly single-phase samples from Bi₂Pb_0.4Sr₂Ca₃Cu₄O _y , as well as from the proposed compositions Bi_1.8Pb_0.4Sr₂Ca₃Cu₄O _y and Bi_1.8Pb_0.4Sr₂Ca_2.5Cu_3.5O _y were obtained by a solid-state reaction in air. Samples with the third nominal composition showed the best superconducting properties (T _on=111 K and zero resistance atT ₀=103 K). A possible mechanism for the 2223 phase formation in the three investigated compositions has been discussed.     

Selective catalytic reduction of NOx by hydrocarbons on Pt/Al2O3 catalysts at low temperatures without the formation of N2O

The selective reduction of nitrogen oxides by hydrocarbons on a Pt catalyst has been investigated. Some variations are observed between different reductants. However, the most significant result is the observation that no N₂O is observed as a by-product when toluene is used as a reductant.     

Reactivity of steam in exhaust gas catalysis III. Steam and oxygen/steam conversions of propane on a Pd/Al2O3 catalyst

A 1% Pd catalyst (38% dispersion) was prepared by impregnating a γ-alumina with palladium acetylacetonate dissolved in acetone. The behaviour of this catalyst in oxidation and steam reforming (SR) of propane was investigated. Temperature-programmed reactions of C₃H₈ with O₂ or with O₂ + H₂O were carried out with different stoichiometric ratios S(S =[O₂]/5[C₃H₈]). The conversion profiles of C₃H₈ for the reaction carried out in substoichiometry of O₂ (S < 1) showed two discrete domains of conversion: oxidation at temperatures below 350°C and SR at temperatures above 350°C. The presence of steam in the inlet gases is not necessary for SR to occur: there is sufficient water produced in the oxidation to form H₂ and carbon oxides by this reaction. Contrary to what was observed with Pt, an apparent deactivation between 310 and 385°C could be observed with Pd in oxidation. This is due to a reduction of PdO_x into Pd⁰, which is much less active than the oxide in propane oxidation. Steam added to the reactants inhibits oxidation while it prevents the reduction of PdO_x into Pd⁰. Compared to Pt and to Rh, Pd has a higher thermal resistance: no deactivation occurred after treatment up to 700°C and limited deactivation after treatment up to 900°C, provided that the catalyst is maintained in an oxygen-rich atmosphere during the cooling.     

Erbium-doped silicon and porous silicon for optoelectronics

Silicon forms the backbone of the microelectronics industry, and possibly, of the optoelectronics industry, hitherto dominated by III/V materials. One of the remaining goals is to build an optical source in silicon. Erbium exhibits luminescent 1.54 μm intra-4f transitions in both silicon and porous silicon. This paper reviews the work which has been carried out in this field and discusses some possible additional applications of erbium-doped silicon in optoelectronics, such as a novel on-chip temperature sensor.     

Oxygen absorption kinetics in YBa2Cu3Ox

The oxygen absorption process in highly aligned YBa₂Cu₃O_x samples in air and in pure oxygen was studied at several constant temperatures. The process can be expressed in two steps, a chemical reaction controlled step and a diffusion controlled step. The kinetic equations are as follows respectively:

(1 − a_t) ln(1 − a_t) + a_t = k_Dt

The activation energy was calculated using an Arrhenius equation. The technical conditions of heat treatment for oxygen absorption of highly aligned YBa₂Cu₃O_x crystals are discussed.