Superplastic behavior of Al-Cu-Li based alloy

The superplastic behavior was studied in an Al-4Cu-ILi-0.4Mg-0.4Ag-0.1Zr alloy. The alloys were manufactured both by＂ a conventional rolling route and a thermo-mechanical treatment route. The superplastic properties were evaluated as a function of temperature, strain rate, and processing history. Prior to thermo-mechanical processing, the alloys have elevated-temperature ductilities of 94% to 130%, strain rate sensitivities of about 0.25, and activation energies corresponding to lattice diffusion. After thermo-mechanical processing, the alloys have ductilities of 200% to 630%, strain rate sensitivity of about 0.42, and activation energies corresponding to grain boundary diffusion or a mixture of grain boundary diffusion and lattice diffusion. Skipping rapid recrystallization annealing can supply a higher value of elongation-to-failure.     

Numerical simulation of deep cryogenic treatment electrode tip temperature for spot welding aluminum alloy

Deep cryogenic treatment technology of electrodes is put forward to improve electrode life of resistance spot welding of aluminum alloy LF2.Deep cryogenic treatment makes electrode life for spot welding aluminum alloy improve.The specific resistivity of the deep cryogenic treatment electrodes is tested and experimental results show that specific resistivity is decreased sharply.The temperature field and the influence of deep cryogenic treatment on the electrode tip temperature during spot welding aluminium alloy is studied by numerical simulation method with the software ANSYS.The axisymmetric finite element model of mechanical,thermal and electrical coupled analysis of spot welding process is developed.The numerical simulation results show that the influence of deep cryogenic treatment on electrode tip temperature is very large.     

稀土La细化再生铝硅合金中β-Fe相的机理研究

研究了再生副牌ZL102合金中稀土La的加入量和β-Fe相平均长度的关系，分析了La在合金和β-Fe相中的分布情况。结果表明，La在熔体中形成了稳定金属间化合物，凝固时促进了β-Fe相形核，同时La在β-Fe相表面富集，阻碍了β-Fe相长大。因此，加入稀土La能很好地细化再生铝合金中的β-Fe相。     

基于ProCAST的消失模铸造工艺的数值模拟研究

运用ProAST软件对链轮铸钢件的消失模铸造工艺进行了充型和凝固过程的数值模拟评价,分析了缺陷产生的原因,对铸造工艺进行了优化,并结合实际生产情况,给出了影响消失模铸造的六大基本因素。     

非晶态Fe_(90-x)Si_xZr_(10)合金的磁矩,Curie温度和自旋波激发SCIEI

非晶态Fe_(90-x)Si_xZr_(10)(x=0,4,7,10)合金是用单辊急冷方法制备的,用提拉样品磁强计测量了样品的磁化曲线和热磁曲线。发现每个磁性原子的平均磁矩μ和Curie温度T_c随Si含量的增加而增加,与相应的非晶态FeSiB合金相比,非晶态FeSiZr合金的μ和T_c明显偏低,认为这一反常现象是Fe-Fe原子间的反铁磁耦合的存在所致。低温下样品的磁化强度与温度的关系较好地符合Bloch T^(3/2)定律,得到自旋波劲度系数D从x=0时的0.37meV·um^2增加到x=10时的0.538meV·um^2,计算出交换相互作用范围都是在最近邻原子间的距离。     

连铸工艺参数对自润滑高耐磨铝硅合金磨损特性的影响

采用正交试验法研究温度梯度、浇注温度和牵引速度三个因素对自润滑高耐磨铝硅合耐磨性能的影响。结果表明,温度梯度、浇注温度是影响耐磨性能的显著因素。在高温度梯度,较低浇注温度连铸工艺下制备此合金,可以获得耐磨性能和减摩性(低摩擦系数)兼顾的优越综合性能。其摩擦系数仅为0.135,磨损量为380.6mg。     

碳对马氏体钢显微组织和力学性能的影响

通过固定其它元素的含量，调整碳含量的方式，研究了碳含量对马氏体钢显微组织和力学性能的影响。结果表明，随碳含量增加，马氏体钢的硬度和抗拉强度提高，但冲击韧度下降。     

碳对马氏体钢显微组织和力学性能的影响

通过固定其它元素的含量,调整碳含量的方式,研究了碳含量对马氏体钢显微组织和力学性能的影响。结果表明,随碳含量增加,马氏体钢的硬度和抗拉强度提高,但冲击韧度下降。     

我国再生铝硅合金冶金质量现状分析

本文介绍了我国再生铝生产工艺流程,全面分析了我国铝再生的冶金质量现状和不足之处,指出了净化变质是制约我国再生铝生产发展的主要障碍,认为要使我国再生铝生产上新台阶,就必须加大技改力度,加大新工艺新设备的投入。     

压应力对Cr-Mo钢连续冷却贝氏体相变的影响

采用Gleeble-1500热模拟试验机测量了Cr-Mo钢在1-90℃／s的冷却速度下奥氏体连续冷却过程中的温度．膨胀曲线，用origin软件进行数据处理，获得了实验钢的CCT曲线；同时测量了施加轴向载荷为0、40MPa、80MPa和120MPa的压应力时奥氏体连续冷却过程中的温度．膨胀曲线，冷却速度分别为50℃／s、70℃／s和90℃／s。利用杠杆定律，根据不同温度下的膨胀量计算得到贝氏体相变动力学曲线，研究了压应力对贝氏体相变动力学和贝氏体相变温度的影响。结果表明，在以冷却速度为50℃／s和70℃／s连续冷却时，压应力抑制前期阶段的贝氏体相变，促进后期阶段的贝氏体相变；在以冷却速度为90℃／s连续冷却时，压应力对整个贝氏体相变过程都有促进作用，特别是应力较大时；压应力使贝氏体相变开始温度Bs升高，贝氏体相变终了温度Bf降低。