In this paper, the droplet transfer in oscillating arc narrow gap gas metal arc ( GMA ) welding was studied. According to the experimental results, the oscillating arc has effect on the droplet transfer mode. The droplet transfer frequency in narrow gap groove is higher than that in bead-on-plate welding. Because of the change of arc location in narrow gap groove, the droplet transfer in oscillating arc narrow gap changes regularly. The droplet transfer frequency near groove sidewall is higher than that at the middle of narrow gap groove. 相似文献
3.
4.
采用光纤激光器开展了碳钢板表面锈蚀层激光清洗研究,通过白光干涉仪、光学显微镜、拉曼光谱仪等研究了激光扫描速度对锈蚀层去除质量的影响。研究表明,当激光扫描速度小于2 000 mm/s时,因光斑搭接率高,热累积效应强,试样表面出现基材熔化重凝现象,同时试样表面发生二次氧化,生成了复杂的铁的氧化物膜层,此时试样表面粗糙度最小。当激光扫描速度增加到3000 mm/s时,试样表面锈蚀层去除干净,露出金属基底本身色泽,基材表面二次氧化减弱。当线速度继续增加时,因光斑搭接率低,锈蚀层吸收的激光能量少,仅有部分锈蚀被去除,试样表面开始出现残留锈蚀层,且随着线速度的增加,残留锈蚀层和试样表面粗糙度增加。通过调节扫描速度可以获得较好的除锈效果,工艺优化后,激光功率为120 W时,除锈效率达到1.5 m2/h。 相似文献
5.
窄间隙焊接因采用窄且深的U型或者I型坡口,在焊接厚板时具有焊接效率高、焊接填充量少及焊接变形少等诸多优势,在大型厚壁高强钢结构制造领域具有很好的应用前景。由于窄间隙焊接中电弧与坡口侧壁几乎平行,造成电弧无法对侧壁直接加热,易出现侧壁未熔合缺陷,严重影响了大型高强钢结构的服役安全。通过对窄间隙焊接技术研究现状的分析整理,综述并比较常用的侧壁熔合控制技术与方案,分析了其优缺点。分析结果表明,目前已经开发了旋转电弧、双电弧、带状电极、复合热源及摆动电弧等多种侧壁熔合控制技术,在一定程度上解决了侧壁未熔合问题,并且在压力容器、厚壁管道等领域获得了应用。最后对该方向的研究进展进行了总结,并对其发展方向进行了展望。 相似文献
6.
7.
将Cu元素合金化Nocolok钎剂成功应用于铝/钛异种金属TIG熔-钎焊。与采用纯Nocolok钎剂相比,采用Cu元素合金化钎剂可显著提高钎料润湿性、有效控制界面化合物厚度并提高接头性能,断裂模式由钛侧钎焊界面的韧脆混合型改变为铝侧熔合区的韧性断裂。Cu元素对润湿性的改善与固、液相线的温度降低及钎剂中的金属氧化物有关。界面化合物厚度的减小及接头性能的提高可归因于钎剂中Cu元素的化学阻挡及界面合金化的共同作用。 相似文献
8.
针对100 mm超厚板TC4钛合金电子束焊接接头,采用慢应变速率拉伸方法评价接头在人造海水中的应力腐蚀敏感性,分析接头的显微组织和断口形貌,对接头的腐蚀机制进行研究. 结果表明,室温条件下应变速率为ε=1×10-6 s-1时,母材在海水中未表现出应力腐蚀敏感性;焊缝上部、中部和下部具有轻微应力腐蚀敏感性. 焊缝在海水中发生阳极溶解,产生氢吸附,导致裂纹的萌生. 同时氢扩散诱导α'相界及α'相内发生位错塞积,进而使裂纹在更低的应力水平下发生扩展. 相似文献