笼型八苯基硅倍半氧烷对阻燃三元乙丙橡胶性能的影响

以聚磷酸铵和季戊四醇为膨胀阻燃体系(IFR),研究了笼型八苯基硅倍半氧烷(OPS)对阻燃三元乙丙橡胶(EPDM)力学性能及其阻燃性能的影响,并对燃烧残炭进行了表征。结果表明,与单独加入30份的IFR相比,同时加入20份OPS后,EPDM阻燃材料的综合性能得到改善,拉伸强度为2.47MPa,极限氧指数为24.2%,热释放速率峰值降低到331.2kW/m2,但生烟量增加到1058m2,且该材料的燃烧残炭结构相对致密均匀。     

含笼型八苯基硅倍半氧烷的三苑乙丙橡肢绝热层材料研究

将笼形八苯基硅倍半氧烷(OPS)应用于三元乙丙橡胶(EPDM)绝热材料,测定了EPDMl OPS绝热材料的力学性能、线烧蚀率、烟雾和密度等主要性能。结果表明,用OPS取代部分聚磷酸铵( APP)的EPDM绝热材料的线烧蚀率、烟雾和密度均明显降低,力学性能也有提高。     

煅烧三氧化二铬对高氯酸铵燃烧的催化作用

本文研究了煅烧三氧化二铬(Cr_2O_3)对高氯酸铵(AP)燃烧的催化作用,发现Cr_2O_3在研究的煅烧温度范围内,煅温度提高,对AP的燃烧催化作用增加。对Cr_2O_3进行了X射线光电子能谱(XPS),红外光谱(IR)和X-射线衍射分析,表明煅烧Cr_2O_3表面发生了氧化,提出Cr_2O_3表面不同价态铬的共存促进了AP燃烧过程中的电子转移过程,从而提高了Cr_2O_3时AP燃烧的催化作用。     

不同蒙脱土对Al(OH)_3/乙烯-醋酸乙烯酯复合材料力学性能和阻燃性能的影响

对比研究了钙基蒙脱土(Ca-MMT)和有机改性的钠基蒙脱土(Na-MMT)对Al(OH)_3/乙烯一醋酸乙烯醋(EVA)复合材料的力学性能、热稳定性和阻燃性能的影响。采用熔融插层法制备MMT-Al(OH)_3/EVA复合材料。用XRD和TEM进行微观结构表征。结果表明:两种MMT在复合材料中均表现为一定程度的剥离分散状态,其中Ca-MMT的剥离片层相对尺寸更小。测试显示,Ca-MMT-Al(OH)_3/EVA的拉伸强度、热稳定性均高于Na-MMT-Al(OH)3/EVA;在燃烧过程中,加入Ca-MMT的Ca-MMT-Al(OH)_3/EVA复合材料热释放更低,形成的炭层隔热效果更好,表现出更优异的阻燃性能;同时火灾性能指数(FPI)提高,火灾危险性明显降低。分析原因是Ca-MMT中的Ca~(2+)在燃烧成炭中具有促进作用。     

胍类阻燃剂处理木材的热解机理

为了研究木材热解行为与阻燃性能的关系,探讨其热解机理,将木材用一系列胍类阻燃剂进行阻燃处理,所得阻燃木材采用热重(TG)、差热分析(DTA)和红外光谱(IR)进行分析,并用Broido方程计算木材的热解活化能.结果发现,经磷酸二氢胍和磷酸氢二胍处理的木材阻燃性较好,氧指数为39%~42%;主要热解阶段在低于300℃进行,热解表观活化能降低约60 kJ/mol,这主要是由于木材在低于300℃热解主要发生脱水、重排交联炭化产生少量可燃性气体,剩炭增加.而经碳酸胍、硝酸胍处理的木材样品虽然其主要热解阶段温度降低,但阻燃性差,氧指数小于26%,主要是由于其热解仍然包括1个较高温度阶段(300℃以上),在此阶段热解产生较多的可燃性气体.     

Thermal aging behavior of high performance poly(vinyl alcohol) hydrogel

The thermal aging behavior of poly(vinyl alcohol) (PVA) hydrogel was studied at four different temperatures of 40 ℃, 50 ℃, 60 ℃ and 70 ℃ in one year. The samples of PVA hydrogel were closely covered by plastic film. The changes of their chemical structures and physical properties during aging were measured through different measurable techniques including tensile testing, gel permeation chromatography (GPC), viscosity analysis, and Fourier transform infrared (FTIR) spectrum. The results showed that the molecular weight of PVA in hydrogel changed little with time and temperature. FTIR spectra of PVA in all the samples were similar to those of the original samples. The tensile strength of PVA hydrogel didn’t change until the 330th days.     

Study of Flame Retardation of Polycarbonate Modified by Polyhedral Oligomeric Silsesquioxane and Caged Bicyclic Phosphate

The flame-retarded polycarbonate (PC) has been made with octaphenyl polyhedral silsesquioxane (OPS) and/or caged bicyclic phosphate (Trimer). Thermal gravimetric analysis (TGA), Fourier-transform infrared (FTIR), TGA-FTIR, limiting oxygen index (LOI), and mechanical tests have been employed to characterize the modified PC. The additives of OPS and Trimer in PC have been proved to be effective flame-retardants because of the synergistic interaction between the elements of P and Si. The role of OPS and Trimer in PC degradation are different: OPS participates in the charring of PC, while Trimer makes PC degrade in advance. In addition, OPS and Trimer induced obvious differences in the mechanical properties of PC.     

聚乙烯醇缩丁醛包覆硝酸铵的性能研究

采用液相分离技术,用聚惭烯醇缩丁醛（PVB）对硝酸铵（AN）进行包覆。研究了包覆后硝酸铵的性能,并对包覆的效果进行了表征。结果表明,用PVB包覆AN,包覆效果较好,产品的吸湿性、结块性都有大幅度下降,Ⅱ→Ⅲ的晶型转变吸收峰移向高温甚至消失。     

微胶囊技术在硝酸铵改性中的应用

提出了用聚苯乙烯包覆硝酸铵制备硝酸铵微胶囊的新方法 ,采用电子能谱仪研究了包覆效果 ,并对包覆前后的硝酸铵进行吸湿性测量 ,分析了改性后的硝酸铵吸湿结块性降低的原因和机理。     

基于文献计量的中国电缆阻燃技术分析

以中国知网和国家知识产权局数据库为基础,采用文献计量法,对我国电线电缆阻燃技术的科研产出进行了分析。重点统计了近30 a来论文发表及专利申请情况,依据年度数据总结分析了阻燃电线电缆的技术发展,并通过热点关键词分析、不同基材聚合物和阻燃体系的年度发文数据对研发热点进行了总结。统计显示:进入21世纪以后,我国电缆阻燃技术研究论文的发表数量明显上升,专利申请数量呈倍数增长;现阶段电缆阻燃论文中的热点聚合物基体为聚氯乙烯,而专利技术申请中的热点基体为聚乙烯;阻燃体系仍然以无机填充型阻燃剂为主,高效的膨胀型阻燃剂、纳米协效等技术正日益得到关注。