Photochemical damage of ocular tissues by solar radiation depends on the spectral composition of the radiation in the environment, the geometry of the coupling of that radiation to the eye, the spectral transmittances of the ocular components and any auxiliary lenses used, the spectral sensitivity of the irradiated tissue, the accumulated exposure dose, and the action of repair processes. This paper provides formulas for quantitative estimation of corneal, lenticular, and retinal UV irradiances from the sunlit environment under clear sky conditions. Applications of these formulas for ocular irradiation will be presented in subsequent papers for the cornea, lens, and retina, and the results will be evaluated using weighting functions for the sensitivity of ocular tissue.     

Mechanical property changes in sapphire by nickel ion implantation and their dependence on implantation temperature

Sapphire plates, cut parallel to an {0001} plane, have been implanted with 300 keV nickel ions to doses ranging from 5×10¹² to 1×10¹⁷ Ni cm^–2 at specimen temperatures of 100, 300 and 523 K, in order to investigate the effect of implantation temperature on the mechanical property changes in sapphire caused by ion implantation. The measured changes in surface hardness, surface fracture toughness and bulk flexural strength were found to depend strongly on the implantation temperature, and were largely correlated with the residual surface compressive stress measured by using a cantilever beam technique. The surface amorphization that occurred only by the implantation at 100 K and at doses larger than 2×10s15 Ni cm^–2 reduced the hardness to 0.6 relative to the value of the unimplanted sapphire, and considerably increased the surface plasticity. Furthermore, the amorphization was found to involve a large volume expansion of 30% and to change drastically the apparent shape and size of a Knoop indentation flaw made prior to implantation. This effect was suggested to reduce stress concentrations at surface flaws and hence to increase the flexural strength.