铝带材冷轧机机前展平辊重叠量的探讨

目前国内大多数铝加工厂对铝带材冷轧机机前展平辊的作用缺乏足够的认识，甚至弃而不用。本文主要论述展平辊的作用及展平辊重叠量的计算方法。     

军械调运方案优化算法的设计与仿真

军械调运问题的数学模型和手工算法过去已有研究,但是当问题较为复杂时,手工算法就要花费大量时间而且准确性也难以保证。针对这一缺陷,本文在已有的数学模型和手工算法的基础上,设计了一种可以用计算机实现的基于递归的算法来寻求军械紧急调运问题的最优方案,并使用面向对象的java语言将算法实现。     

Traveling wave method for calculation of linewidth, frequencytuning, and stability of semiconductor lasers

The authors present a new traveling wave method for calculating the linewidth, the frequency tuning efficiency, and a mode stability parameter for a general class of laser-diode structures. The method leads to simple semianalytic expressions which allow an easy numerical determination of the three parameters     

双噁唑啉化合物对PBT的增粘作用

以２．２＇－双（２－唑啉）和双（２－唑啉基）苯作扩链剂，用焙融挤出的方法，对聚对苯二甲酸丁二酯（ＰＢＴ）进行扩链，考察扩链剂的用量、反应时间和反应温度对ＰＢＴ的特性粘度及端羧基含量（ＣＶ）的影响。结果表明，当用２，２＇－双（２－唑啉）作扩链剂时，ＰＢＴ的特性粘度［η］从０．７９９提高到０．９２６ｄＬ／ｇ，ＣＶ降至５ｅｑ／１０￣６ｇ以下；当用双（２－　唑啉基）苯作扩链剂，［η］从０．７６３增至０．９２５ｄＬ／ｇ，ＣＶ降至１０ｅｑ／１０￣６ｇ以下，达到了较满意的扩链效果。     

SiCf/O′-SiAlON composite: properties and oxidation retained properties

A composite of O′SiAlON (Si_2-xAl_xN_2-xO_1+x, with x 0.14) reinforced with 20 vol.% SiC monofilaments was fabricated by hot-pressing, at 1600°C, for 2 h under 34 MPa pressure. The mechanical and interfacial properties of the composites, as-fabricated as well as post-oxidized, were, investigated. The composite exhibited a significant improvement in ultimate flexure strength (640 MPa) and work of fracture (42 kJ m⁻²) compared with that (350 MPa and 1.8 kJ m⁻², respectively) of the monolithic material. These mechanical properties were slightly increased after the composite was heat treated for 24 h in air at 1200 and 1300°C. However, the composite exhibited a significant degradation in ultimate strength, while the work of fracture (WOF) remained unchanged after exposure in air at temperatures beyond 1400°C. The as-fabricated composite revealed a low interfacial shear strength (6.2 MPa) and a frictional sliding stress (3.2 MPa). After the composite was oxidized at elevated temperatures, the interfacial bonding and sliding stresses were reduced to noticeable extents, resulting from the degradation of the carbon coating layer of the SiC monofilaments.     

激光辐照40Cr钢组织结构的穆斯堡尔谱分析

４０Ｃｒ钢试样经不同热处理后在空气中用ＣＯ２连续激光束进行辐照，以穆斯堡尔谱学研究试样在辐照后的组织结构变化。试验结果表明，调质预处理后再进行激光辐照的试样，不仅残作产奥氏体含量较低，而且其中碳的含量最低。     

压力容器标准对不等厚板材对接要求的分析

欧盟、美国和我国压力容器标准对不等厚板材对接时均有削薄要求,通过有限元方法计算不同条件下连接时的应力分布,认为不等厚板材对接连接时,按照EN13445(2002)要求增加直边段,对减小局部应力有一定好处,对提高射线检测灵敏度有利.     

活性炭载体的超声波处理对Pt／C催化剂活性的影响分析

通过对活性炭载体进行不同条件的超声波处理获得了具有不同表面化学性质的载体，使用比表面积（BET）、酸碱滴定等技术手段对载体的物理化学性质进行了表征。将经过超声波处理的活性炭载体制备成Pt／C催化剂，并将催化剂直接用于催化反应，考察了活性炭载体的不同超声波处理条件对Pt／C催化剂性能的影响。实验发现，活性炭载体经过超声波处理后，表面灰分含量、pH值和中孔孔容有较大的变化；使用经过60min超声波处理后中孔孔容较大的活性炭作为载体制备的Pt／C催化剂，在催化加氢反应性能测试中显示了最高的催化活性。在此基础上，就活性炭载体的超声波处理对Pt／C催化剂活性的影响进行了讨论。