The electrochemical behaviour of nitrogen-containing austenitic stainless steel in methanolic solution

The corrosion behaviour of nitrogen-containing austenitic stainless steel in methanol containing different concentrations of H₂SO₄, HCl, LiCl and H₂SO₄ + HCl has been investigated using a potentiostatic polarization method. The cathodic reaction in the H₂SO₄, HCl and H₂SO₄ + HCl solutions was proton reduction whereas in the neutral LiCl solution, oxygen reduction was the predominant cathodic reaction. Active, passive and transpassive behaviours were observed only for higher concentrations of H₂SO₄ (0.01–2.0 M) due to the inherent water content. A cathodic loop, characterized by measured negative current in the anodic region, was also observed in solutions, in which the concentration of H₂SO₄ was 1.0 M or higher. The relative stability of the passive films decreased as the H₂SO₄ concentration increased, and thus the steel suffered from mild pitting corrosion. In the chloride environment, the rate of corrosion increased as the Cl⁻ ion concentration increased. The presence of acid along with Cl⁻ ions enhanced corrosion, and the corrosion rate increased significantly. The steel suffered from mild intergranular corrosion in acidic chloride solutions of methanol. In the H₂SO₄ + HCl solutions, passive films were only formed when the H₂SO₄ to HCl concentration ratio was greater than ∼10:1.     

Nanocrystalline Ni coatings strengthened with ultrafine particles

In this study, nanocrystalline Ni powders and thermally sprayed coatings, containing ultrafine AlN particles, were synthesized and characterized. The results indicated that the presence of AlN particles in the powders drastically decreased the dimension of agglomerates formed by cryomilling and increased the surface roughness of the agglomerates. The AlN phase was broken down into ultrafine particles of approximately 30 nm in size. These particles were dispersed in the Ni matrix and enhanced the development of a nanocrystalline structure in the Ni matrix during cryomilling. Selected-area diffraction patterns, obtained from transmission electron microscopy (TEM) and X-ray mapping with scanning electron microscopy (SEM), confirmed the presence of AlN particles in the coatings. The presence of AlN particles also led to an increase in the amount of NiO phase that was distributed in the coating, in the form of ultrafine, round particles. AlN particles increased the microhardness of the Ni coating by approximately 60 pct. Indentation-fracture results also indicated that the fine, dispersed AlN particles raised the apparent toughness of the Ni coating. The synthesized Ni coatings containing ultrafine AlN particles were characterized as equiaxed nanocrystalline grains with an average size of 24 nm, in which twins were observed. The increase in microhardness resulted from both grain refinement and the presence of ultrafine particles. The latter played the primary role in strengthening.     

低松装密度水雾化铜粉工艺的研究

本文研究了氧化 还原法生产铜粉的新工艺 ,该工艺是通过氧化还原将水雾化铜粉加以表面改性 ,形成海绵状的粉末 ,显著降低水雾化铜粉的松装密度 ,这种铜粉既具有电解铜粉低的松装密度 ,又具有水雾化铜粉高的流动性。讨论了氧化时间、氧化温度对铜粉松装密度的影响。本工艺是一种新型环保、节能、可替代电解法生产铜粉的先进工艺     

Time-dependent deformation in an enhanced SiC/SiC composite

Time-dependent deformation in an enhanced SiC/SiC composite has been studied under constant load at high temperatures of 1200 °C, 1300 °C, and 1400 °C. Creep damage evolution was evaluated by a Young’s-modulus change of partial unloading and microscopic observation. The addition of the glassy phase in the matrix is very effective for protecting the composite from oxidation. The transient creep is dominant in creep life at all the temperatures. An empirical equation is proposed to describe creep behavior of the composite. It is found that creep activation energy increases with creep time at stresses lower than matrix cracking stress, but the activation energy remains constant at stresses higher than the matrix cracking stress. The creep strain rate of the composite is considered to be controlled by creep of fibers based on examining the time, strain, stress, and temperature dependencies of creep strain rates.     

废槽衬的性能研究

研究了废槽衬的外观形貌、微观结构、物相组成、元素含量,并对寿命相同的两种典型废槽衬的性能进行了对比分析,为选择废槽衬的无害化处理工艺提供了基础数据。     

苯乙烯与1-(2-叔丁基过氧异丙基)-3-异丙烯基苯共聚行为研究

苯乙烯与1－（2－叔丁基过氧异丙基）－3－异丙烯基苯（D120）能进行自由基共聚合反应，聚合后过氧基团以侧基的形成被保留在共聚物大分子链上，凝胶色谱分析发现，随原料单体中D120比例增加，共聚物的分子量减小，分子量分布变窄，DSC分析发现共聚物中过氧基团的分解温度随D120结构单元含量的增加而下降，但仍高于D120单体过氧基团的分解温度，苯乙烯与D120的竞聚率为：rD120=0.700,rSt=0.714。     

从铅阳极泥处理后的渣料中综合回收有价金属的生产实践

叙述了从铅阳极泥回收金银后的渣料中综合回收有价金属的生产实践。根据渣料性质，将火法和湿法工艺相互结合，使渣料中的锑、铋、金、银、铅、铜得以较彻底的分离和回收。     

Numerical Simulation of Thermal Stress Fields in the Magnetic Quenching Process of 45 Steel

Based on a transient temperature distribution of a 45 steel cylinder workpiece during magnetic quenching, which was obtainedby solving the governing equations with nonlinear boundary on the condition of coupling effects of heat-magnetism. Accordingto the     