Simultaneous Internal Oxidation and Nitridation of Ni–Cr–Al Alloys

A series of Ni–Cr–Al alloys was subjected to thermal cycling to 1100°C in air for up to 260 1-hr cycles. All alloys exhibited poor corrosion resistance. Repeated scale spallation led to subsurface alloy depletion in aluminum and, to a lesser extent, chromium. This caused transformation of the prior alloy three-phase structures (-Cr+-NiAl+-Ni) to single-phase -nickel solution. Destruction of the external scale allowed gas access to this metal, which was able to dissolve both oxygen and nitrogen. Inward diffusion of the two oxidants led to development of a complex internal-precipitation zone: Al₂O₃ and Cr₂O₃ beneath the surface, followed by Al₂O₃, then AlN, then AlN+Cr₂N, and, finally, AlN alone in the deepest region. This distribution is shown to reflect the relative stabilities of the precipitates and the higher permeability of nitrogen. Diffusion-controlled kinetics were in effect initially, but mechanical damage to the internal-precipitation zone led to more rapid gas access and approximately linear kinetics in the long term.     

基于压差控制的蓄能器压力调节方法及其AMESim仿真

为扩展蓄能器的压力适用范围,提出了一种压差控制方法,利用液压缸或增压缸两腔压差,以比例溢流阀调节背压,进而控制蓄能器压力.针对典型的大流量快速加压系统,基于增压缸压差控制,进行了蓄能器补流压力控制回路的设计与计算.通过AMESim软件对压力控制效果进行仿真分析,结果表明该方法达到了控制要求,提高了蓄能器的适用性和压力控制的灵活性.     

环件开式辗扩力和力矩计算

用上限法分析了环件开式辗扩变形，导出了辗扩力和力矩计算公式，阐述了辗扩力和力矩与辗扩进给速度的关系。根据环件辗扩实验结果，对文中的辗扩力和力矩计算公式进行了验证。     

新型半固态铝合金AlSi6Mg2设计与实验研究

结台半固态加工基本原理利用热力学计算方法设计出了新型半固态铝合金AlSi6Mg2，并进行了半固态触变压铸成形和微合金化实验研究。结果显示：新合金在触变成形过程中表现出良好的半固态组织和工艺性能，微合金化改善了新合金组织，提高了合金的综合力学性能，特别是塑性明显提高。     

连铸方坯低倍边部裂纹原因分析

分析了连铸方坯产生低倍边部裂纹的原因。结果表明：由于沿晶界析出MnS夹杂物诱发铁素体网，裂纹沿铁素体网萌生并扩展导致边部裂纹的产生。     

氯化钾转化地面的腐蚀与防护

分析了氯化钾低温转化法生产硫基NPK复合肥转化地面的腐蚀机理，并提出了相应的防护措施。     

Effects of pH value of reaction solution on structure and electrochemical performance of calcium-containing active material of secondary zinc electrodes

The calcium-containing active material of secondary alkaline zinc electrodes was prepared by a chemical coprecipitation method and characterized by scanning electron microscopy(SEM) and X-ray diffractometry(XRD).Their electrochemical performance was tested by the Galvanstatic charge-discharge method. The experimental results show that the sample synthesized at pH: 11. 15 has a typical calcium zincate crystal. The zinc electrode using this sample as active material shows higher discharge capacity, more negative discharge plateau potential and longer cycle lifetime.     

溶剂对溶剂热合成CdS纳米晶体的形貌控制

以溶剂热法在不同溶剂里的160℃下反应12 h制备不同形貌的CdS纳米晶粒,分别选用水(H2O)、二甲基甲酰胺(DMF)、乙醇胺(an)和乙二胺(en)为溶剂来控制纳米CdS的形貌和尺寸.对样品的结构和性能进行表征,重点分析了溶剂的物理性质和结构特征对CdS纳米粒子晶体结构、形貌和尺寸的影响,不同溶剂的作用机制不同,可通过选择合适的反应溶剂来控制纳米粒子的形貌和尺寸,以制备满足不同应用需要的纳米结构,尤其是性能独特的一维纳米结构.     

HPC修饰纳米二氧化钛薄膜的微观结构和光学性能

用羟基纤维素(HPC)作为添加剂,用溶胶-凝胶法制备了二氧化钛薄膜.用扫描电镜(SEM)和透射电镜(TEM)观察不同HPC含量的二氧化钛薄膜的微观结构,研究HPC对膜的微观结构的影响机理.用X射线衍射谱(XRD)分析不同薄膜样品的晶格常数.用吸收光谱观察薄膜光吸收端随HPC含量的变化.发现HPC的加入阻碍二氧化钛晶粒生长和减小膜厚两方面导致了二氧化钛晶格畸变,进而引起薄膜光吸收端的蓝移.     

电火花加工模糊驱动系统的研究

通过对电火花加工过程中间隙电压和放电状态的分析，提出了采用间隙电压作为微观驱动控制，同时利用表征放电状态的参数，即火花放电率、电弧及短路率等进行宏观调节的一种综合控制策略。其中微观模糊控制器调节进给频率，宏观模糊控制器调节进给步距。