Fracture Energies of Tape-Cast Silicon Nitride with β-Si3N4 Seed Addition

The fracture energies of the tape-cast silicon nitride with and without 3 wt% rod-like β-Si₃N₄ seed addition were investigated by a chevron-notched-beam technique. The material was doped with Lu₂O₃–SiO₂ as sintering additives for giving rigid grain boundaries and good heat resistance. The seeded and tape-cast silicon nitride has anisotropic microstructure, where the fibrous grains grown from seeds were preferentially aligned parallel to the casting direction. When a stress was applied parallel to the fibrous grain alignment direction, the strength measured at 1500°C was 738 MPa, which was almost the same as room temperature strength 739 MPa. The fracture energy of the tape-cast Si₃N₄ without seed addition was 109 and 454 J/m² at room temperature and 1500°C, respectively. On the contrary, the fracture energy of the seeded and tape-cast Si₃N₄ was 301 and 781 J/m² at room temperature and 1500°C, respectively, when a stress was applied parallel to the fibrous gain alignment. The large fracture energies were attributable primarily to the unidirectional alignment fibrous Si₃N₄ grains.     

Physical properties of silk fibers treated with ethylene glycol diglycidyl ether by the pad/batch method

This paper deals with the epoxide treatment of silk fabrics by the pad/batch method. The optimum reaction conditions, i.e., NaOH concentration, and reaction temperature were 2.5 g/L and 30°C, respectively. A weight gain of 8.5% was attained at a reaction time of 6 h. This value slightly increased to 10% after 24 h. The reactivity of tyrosine and basic amino acid residues was dependent on the reaction time and did not significantly differ from the results of epoxide-treated silk fiber by the conventional method in tetrachloroethylene. The moisture regain slightly decreased at 4% weight gain and then increased with the epoxide content, exceeding the value of the untreated control. The crease recovery of the epoxide-treated silk fabrics measured in the wet state was significantly improved, whereas that in the dry state was almost unchanged. The rate of photoyellowing of the epoxide-treated silk fabrics by the pad/batch method was reduced significantly compared with that of the untreated control. Among the mechanical properties, elongation at break and tensile modulus remained unchanged, whereas the tensile strength slightly increased following the epoxide reaction. The thermal properties were evaluated by DSC and TGA and on the basis of the dynamic viscoelastic measurements. The DSC curve of the epoxide-treated sample showed a slight increase of the decomposition temperature of silk fibroin. The rate of weight loss determined by TGA remained unchanged regardless of the chemical modification, whereas the peak of loss modulus became broader and shifted to lower temperature. The X-ray diffractograms showed that the crystalline structure of silk fibers was not affected by the reaction with epoxides. © 1993 John Wiley & Sons, Inc.     

Highly Reactive β-Dicalcium Silicate: III, Hydration Behavior at 40–80°C

The effect of curing temperature (40°, 60°, 80°C) on the hydration behavior of β-dicalcium silicate (β-C₂S) was investigated. The β-C₂S was obtained by decomposition of hillebrandite, Ca₂(SiO₃)(OH)₂, at 600°C, has a specific surface area of about 7 m²/g, and is in the form of fibrous crystals. The dependence of the hydration reaction on temperature continues until the reaction is completed. The hydration is completed in 1 day at 80°C and in 14 days at 14°C. The hydration mechanism is different above and below 60°C, but at a given temperature, the reaction mechanism and the silicate anion structures of C-S-H do not change significantly from the initial to the late stages of the reaction. High curing temperature and long curing times after completion of reaction promote silicate polymerization. The Ca/Si ratio of C-S-H shows high values, being almost 2.0 above 60°C and 1.95 below 40°C.     

In Situ Synthesis and Microstructures of Tungsten Carbide-Nanoparticle-Reinforced Silicon Nitride-Matrix Composites

A W₂C-nanoparticle-reinforced Si₃N₄-matrix composite was fabricated by sintering porous Si₃N₄ that had been infiltrated with a tungsten solution. During the sintering procedure, nanometer-sized W₂C particles grew in situ from the reaction between the tungsten and carbon sources considered to originate mainly from residual binder. The W₂C particles resided in the grain-boundary junctions of the Si₃N₄, had an average diameter of ∼60 nm, and were polyhedral in shape. Because the residual carbon, which normally would obstruct sintering, reacted with the tungsten to form W₂C particles in the composite, the sinterability of the Si₃N₄ was improved, and a W₂C–Si₃N₄ composite with almost full density was obtained. The flexural strength of the W₂C–Si₃N₄ composite was 1212 MPa, ∼34% higher than that of standard sintered Si₃N₄.     

Monodisperse nanoparticles of poly(ethylene glycol) macromers and N‐isopropyl acrylamide for biomedical applications

Poly(ethylene glycol)‐based nanoparticles have received significant attention in the field of biomedicine. When they are copolymerized with pH‐ or temperature‐sensitive comonomers, their small size allows them to respond very quickly to changes in the environment, including changes in the pH, ionic strength, and temperature. In addition, the high surface‐to‐volume ratio makes them highly functionalized. In this work, nanoparticles composed of temperature‐sensitive poly(N‐isopropylacrylamide), poly(ethylene glycol) 400 dimethacrylate, and poly(ethylene glycol) 1000 methacrylate were prepared by a thermally initiated, free‐radical dispersion polymerization method. The temperature‐responsive behavior of the hydrogel nanoparticles was characterized by the study of their particle size with photon correlation spectroscopy. The size of the nanoparticles varied from 200 to 1100 nm and was a strong function of the temperature of the system, from 5 to 40°C. The thermal, structural, and morphological characteristics were also investigated. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 87: 1678–1684, 2003     

Balanced corpus of contemporary written Japanese

The balanced corpus of contemporary written Japanese (BCCWJ) is Japan’s first 100 million words balanced corpus. It consists of three subcorpora (publication subcorpus, library subcorpus, and special-purpose subcorpus) and covers a wide range of text registers including books in general, magazines, newspapers, governmental white papers, best-selling books, an internet bulletin-board, a blog, school textbooks, minutes of the national diet, publicity newsletters of local governments, laws, and poetry verses. A random sampling technique is utilized whenever possible in order to maximize the representativeness of the corpus. The corpus is annotated in terms of dual POS analysis, document structure, and bibliographical information. The BCCWJ is currently accessible in three different ways including Chunagon a web-based interface to the dual POS analysis data. Lastly, results of some pilot evaluation of the corpus with respect to the textual diversity are reported. The analyses include POS distribution, word-class distribution, entropy of orthography, sentence length, and variation of the adjective predicate. High textual diversity is observed in all these analyses.     

Diffusion/adsorption model of cellulose dyeing. II. Ordinary cellulose–direct dye system

The diffusion and adsorption of C.I. Direct Yellow 12 and Blue 15 in water-swollen ordinary cellophane sheets were examined at various ionic strengths. The concentration dependence of apparent diffusion coefficients, D_c, for these dyes was obtained from the diffusion profiles in the substrate, which were measured by the use of the cylindrical film roll method. The decrease of apparent porosity with an increase in the amounts of adsorption was observed. To explain the diffusion/adsorption behaviors of these systems, a variable porosity model was proposed and was applied to analyze the concentration dependence of D_c's. The diffusion/adsorption behaviors of these dyes could be quantitatively described by this model at relatively low ionic strengths. At higher ionic strengths and/or lower values of C, i.e., at the large values of C_im/C_m, where the C's are the concentrations of immobilized (suffix im) and mobile (suffix m) species, it needed to introduce the concept of dynamic equilibria which occurred simultaneously with diffusion but deviated from the true equiliblia measured by the adsorption experiments.     

Reaction and diffusion of reactive disperse dye in nylon 6

The diffusion of a reactive disperse dye with a vinylsulfonyl group accompanied by simultaneous reaction with the amino end groups in nylon 6 was examined by the method of cylindrical film roll at 70°C and pH 2.2–8.0. The experimental diffusion profiles of the active and fixed species of the dye in nylon 6 were confirmed to be described by the diffusion equation accompanied by the chemical reaction with substrate taking the limited amount of the end groups into account, where the active species of dye were assumed to react only with the free base of amino end groups. The completion of the reaction with the amino end groups was observed in the first layer from the surface at pH 6.0–8.0. The value of diffusion coefficient was constant (8.0 × 10^?10 cm²/s) at all the pH's. The product of the second-order rate constant, k₂, of reaction of the dye and the dissociation constant, K_a, of the amino end groups was constant (k₂K_a = 4.0 × 10^?9 s^?1) at pH 2.2–8.0. The k₂ values of the reaction with various substrates for vinylsulfonyl and monochlorotriazinyl-reactive dyes were compared and the practical dyeing conditions were discussed.     

Microstructure and Thermal Shock Resistance of Molten Glass-Coated Carbon Materials Fabricated by Interfacial Control

Carbon substrates were coated completely with a molten silicate glass, where the wettability of carbon to glass was improved by infiltration and pyrolysis of perhydropolysilazane. Microstructures of the carbon–glass interface were dependent on P n ₂ during coating. Coating at lower P n ₂ induced the formation of cristobalite at the carbon–glass interface. When the coating was performed at higher P n ₂, the glass and carbon were strongly adhered, without the formation of cristobalite. Coating at higher P n ₂ improved the thermal shock resistance of the glass layer, because crack initiation was not induced by the phase transformation of cristobalite during the cooling process. In the case of coating at higher P n ₂, an oxynitride glass layer was formed at the glass subsurface by dissolution of N₂. A porous glass subsurface layer with uniform spherical micro-pores could be produced by soaking near the glass transition temperature in a steam environment. The porous layer with fine and homogeneous microstructure acts as a thermal shock absorbing layer, so that glass-coated carbon with a porous glass layer has excellent thermal shock resistance in addition to steam oxidation resistance.     

Higher-order structures and mechanical properties of stereocomplex-type poly(lactic acid) melt spun fibers

Equimolar blend of poly(l-lactic acid) (PLLA) and poly(d-lactic acid) (PDLA) was melt spun into fibers and the relations among the processing conditions, crystalline structures, thermal properties, and mechanical properties were investigated. Drawing and annealing were performed in order to obtain fiber mainly consisting of the stereocomplex crystal phase. Fibers drawn at various temperatures exhibited either amorphous, highly oriented homo crystal, or the mixture of homo and stereocomplex with a fairly low orientation depending on the drawing temperature. Annealing of the drawn fibers at an elevated temperature higher than the melting temperature of homo crystal increased the stereocomplex content significantly. The fractions of the homo and the stereocomplex crystals strongly depended on the higher-order structure of the drawn fibers and the annealing temperature.