X射线干涉光刻光束线关键光学元件热-结构耦合分析

为了保证上海光源X射线干涉光刻光束线的稳定性,减小热变形对实验结果的影响,对X射线干涉光刻光束线的3个关键光学元件——偏转镜、聚焦镜和精密四刀狭缝进行热-结构耦合分析。首先,计算偏转镜、聚焦镜和精密四刀狭缝所承载的功率密度;然后,建立其有限元模型;最后,获得光学元件的温度场和热变形的结果。结果表明,偏转镜和聚焦镜采用间接水冷方式可有效抑制热变形,冷却后的最大面形误差分别为7.2μrad和9.2μrad。精密四刀狭缝未冷却时,刀片组件温度介于271.56~273.27℃,刀口热变形为0.19 mm,直线导轨热变形为0.08 mm;经过铜辫子冷却后,刀片组件温度降至22.24~23.94℃,刀口热变形降至0.2μm,直线导轨热变形降至0.1μm;采用影像法和接触探头法测试后,刀口直线度、平行度和重复精度均满足技术要求。偏转镜、聚焦镜和精密四刀狭缝的热变形通过间接水冷和铜辫子的冷却方式可以得到很大程度的抑制,进而保证光斑质量。     

Lead-free sodium niobate nanowires with strong piezo-catalysis for dye wastewater degradation

In this work, the hydrothermally-synthesized sodium niobate nanowires were used to decompose Rhodamine B dye solution through the piezo-catalytic effect. With the sodium niobate catalyst, a high piezo-catalytic degradation ratio of ～80% was achieved under the excitation of vibration for the Rhodamine B dye solution (～5?mg/l). These active species in the catalytic process, hydroxyl radicals and superoxide radicals with the strong oxidation ability, were also observed, which confirmed the key role of piezoelectric effect for piezo-catalysis. The piezo-catalysis of sodium niobate nanowires provides a high-efficiency and reusable tool in application in depredating the dye wastewater.     

Oxide-Scale Evolution on a New Ni–Fe-Based Superalloy at High Temperature

Oxidation of Metals - The isothermal oxidation behavior and oxide-scale evolution on a newly developed Ni–Fe-based superalloy were investigated. Three oxidation stages were generally...     

Fabrication of dense nano-laminated tungsten carbide materials doped with Cr3C2/VC through two-step sintering

This work investigates the critical roles of two-step sintering (TSS) and laminated structure on the sintering behavior and mechanical properties of functionally graded WC-TiC-Al₂O₃ nanostructured composite materials doped with Cr₃C₂/VC. Results show that excellent mechanical properties are achieved for tailored TSS conditions with a hardness of 27.91?±?2.3?GPa and a flexural strength of 1423.3?±?23.5?MPa. The desirable mechanical properties are attributed to the suppressed grain growth without densification deterioration. TSS is more effective in facilitating the favorable dispersion of secondary phase toughening nano-particulates in a WC matrix than conventional sintering (CS). Cr₃C₂/VC dopant plays an important role in maximizing and shifting the temperature range of the kinetic window for WC-Al₂O₃ composites. Al₂O₃ crack deflection, transgranular Al₂O₃, microcracking, WC crack bridging and plate-like WC crack deflection are the major toughening mechanisms. Residual surface compressive stress induced by the graded structure is also an appreciated contribution to the improvement of mechanical properties.     

Super-oleophilicity Co-doping Co2+/F-/TiO2 one-dimensional nanotubes for photocatalytic denitrification of light oil

In this study, a simple hydrothermal synthesis method was adapted for the preparation of Co-doping Co²⁺/F^-/TiO₂ nanotubes photocatalyst, and the micro-nano structure of catalysts prepared by biomimetic technology which makes the catalyst have super-oleophilicity property. Co²⁺/F^-/TiO₂ revealed improved photocatalytic performance for denitrification of light oil compared to single TiO₂ photocatalysts. The enhance of photocatalytic activity can be attributed to narrowing the band gap, increasing the light response wavelength and exposing more highly active crystal surfaces due to synergistic effects of Co²⁺ and F^? in the photocatalyst.     

Stabilizing temperature-capacitance dependence of (Sr,Pb, Bi)TiO3-Bi4Ti3O12 solutions for energy storage

(1-x)Sr_0.7Pb_0.15Bi_0.1TiO₃-xBi₄Ti₃O₁₂ ((1-x)SPBT-xBIT, x = 0-0.125) bulk ceramics were developed and calcined via the solid-state method, aimed at the application of pulsed power capacitors. The phase structures, temperature stability, hysteresis loop, and discharge properties were systematically investigated. Considering both the temperature stability and dielectric properties, 0.925SPBT-0.075BIT bulk ceramics with a capacitance variation satisfying the X7R specification were developed for pulsed power capacitors. The energy storage density was 0.252 J/cm³, and the ceramics showed high temperature stability at 80 kV/cm. The discharge current waveforms of the 0.925SPBT-0.075BIT ceramics were recorded. A high discharge power density of approximately 1.01 × 10⁸ W/kg with an 8 Ω load resistor and short discharge period of 84 ns were achieved at 50 kV/cm. The good temperature stability properties and high power density show that the 0.925SPBT-0.075BIT ceramics are well suited for pulsed power capacitors with a wide temperature range.