以新型褶式滤筒为研究对象,选取滤筒褶数N_2、褶夹角θ、褶高h、过滤风速v为影响因子,除尘器压力损失为响应值,基于响应曲面法分析影响因子对压力损失的影响,建立滤筒除尘器压力损失的预测模型并得到滤筒褶皱结构最优参数。以滤筒内径D、筒体高度D_1为标准尺寸,依据相关国家标准设计滤筒筒体部分;以锥体高度D_2、锥体上圆直径D_3为系列尺寸,利用尺寸变化法设计锥体部分;通过Access软件建立滤筒产品数据库。结果表明:当θ=5.2°,N_2=50,v=0.01 m/s,h=0.035 m时,除尘器压力损失最低;当D_1=1 000 mm,D=320 mm时,D_2和D_3最佳值分别为600,130 mm,故采用D_2/D_1=0.6,D_3/D=0.4的比值设计相应滤筒锥体系列。     

Tailoring the electron-blocking layer by addition of YSZ to Ba-containing anode for improvement of ceria-based solid oxide fuel cell

The in-situ fabrication of an electron-blocking layer between the Ba-containing anode and the ceria-based electrolyte is an effective approach in suppressing the internal electronic leakage in ceria-based solid oxide fuel cell (SOFC). To improve the thickness of the electron-blocking layer and to research the effect of the layer thickness on the improvement of SOFC, a Ba-containing compound (0.6NiO-0.4BaZr_0.1Ce_0.7Y_0.2O_3-δ) modified by Y stabilized zirconia (YSZ) was employed as a composite anode in this research. SEM analyses demonstrated that the thickness of the interlayer can be simply controlled by regulating the proportion of YSZ at anode. The in-situ formed interlayer in the cell with the anode modified by 20?mol% YSZ possesses a thickness of 0.9?µm which is more suitable for the cell achieving an enhanced performance.     

Theoretical Prediction of Chiral 3D Hybrid Organic–Inorganic Perovskites

Hybrid organic–inorganic perovskites (HOIPs), in particular 3D HOIPs, have demonstrated remarkable properties, including ultralong charge‐carrier diffusion lengths, high dielectric constants, low trap densities, tunable absorption and emission wavelengths, strong spin–orbit coupling, and large Rashba splitting. These superior properties have generated intensive research interest in HOIPs for high‐performance optoelectronics and spintronics. Here, 3D hybrid organic–inorganic perovskites that implant chirality through introducing the chiral methylammonium cation are demonstrated. Based on structural optimization, phonon spectra, formation energy, and ab initio molecular dynamics simulations, it is found that the chirality of the chiral cations can be successfully transferred to the framework of 3D HOIPs, and the resulting 3D chiral HOIPs are both kinetically and thermodynamically stable. Combining chirality with the impressive optical, electrical, and spintronic properties of 3D perovskites, 3D chiral perovskites is of great interest in the fields of piezoelectricity, pyroelectricity, ferroelectricity, topological quantum engineering, circularly polarized optoelectronics, and spintronics.     

Single-Crystalline TiO2(B) Nanobelts with Unusual Large Exposed {100} Facets and Enhanced Li-Storage Capacity

The {100} facet of single-crystalline TiO₂(B) is an ideal platform for inserting Li ions, but it is hard to be obtained due to its high surface energy. Here, the single-crystalline TiO₂(B) nanobelts from H₂Ti₃O₇ with nearly 70% {100} facets exposed are synthesized, which significantly enhances Li-storage capacity. The first-principle calculations demonstrate an ab in-plane 2D diffusion through the exposed {100} facets. As a consequence, the nanobelts can significantly accommodate Li ions in LiTiO₂ formula with specific capacity up to 335 mAh g⁻¹, which is in good agreement with the electrochemical characterizations. Coating with conductive and protective poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate), the cut-off discharge voltage is as low as 0.5 V, leading to a capacity of 160.7 mAh g⁻¹ after 1500 cycles with a retention rate of 66% at 1C. This work provides a practical strategy to increase the Li-ion capacity and cycle stability by tailoring the crystal orientation and nanostructures.     

Evaluation model of green supply chain cooperation credit based on BP neural network

Neural Computing and Applications - More and more enterprises hope to achieve cooperation and win–win. However, many companies often have problems such as insufficient partner credit, which...     

Compressive properties of pristine and SiC-Te-added MgB2 powders,green compacts and spark-plasma-sintered bulks

Pristine and (SiC+Te)-added MgB₂ powders, green and spark plasma sintered (SPS) compacts were investigated from the viewpoint of quasi-static and dynamic (Split-Hopkinson Pressure Bar, SHPB) compressive mechanical properties The amount of the additive (SiC+Te) was selected to be the optimum one for maximization of the superconducting functional parameters. Pristine and added MgB₂ show very similar compressive parameters (tan δ, fracture strength, Vickers hardness, others) and fragment size in the SHPB test. However, for the bulk SPSed samples the ratio of intergranular to transgranular fracturing changes, the first one being stronger in the added sample. This is reflected in the quasi-static K_IC that is higher for the added sample. Despite this result, sintered samples are brittle and have roughly similar fragmentation behavior as for brittle engineering ceramics. In the fragmentation process, the composite nature of our samples should be considered with a special focus on MgB₂ blocks (colonies) that show the major contribution to fracturing. The Glenn-Chudnovsky model of fracturing under dynamic load provides the closest values to our experimental fragment size data.