Effects of Prior Annealing on the Spark Plasma Sintering of Nanostructured Y2O3 Powders

The effects produced by annealing Y₂O₃ nanopowders on their spark plasma sintering (SPS) behavior are systematically investigated in this work. It is found that the annealed powders display higher sinterability with respect to the as‐received ones. Indeed, the maximum densification level reached from pristine powders is about 97.5%, whereas density decreases when further increasing either the sintering temperature or the dwell time. In contrast, the density of SPS products obtained from pretreated powder monotonically increases with temperature and processing time, thus leading to fully dense materials in 30 min at 1050°C and 60 MPa. Correspondingly, it is found that the annealing treatment markedly inhibits grain coarsening during SPS. Thus, dense translucent samples with grain size below 100 nm can be attained from annealed powders. On the other hand, white‐opaque specimens with significantly coarser microstructures (up to 1‐μm‐sized grains) are obtained when pristine powders are directly processed under the same sintering conditions. Furthermore, it is observed that the annealing treatment of SPS samples in air allows for graphite contamination removal, whereas no improvement in term of light transmittance is produced.     

125I粒子条联合胆道支架植入治疗恶性梗阻性黄疸22例疗效分析

【摘要】　 　目的 研究和探讨125I粒子条联合胆道支架植入治疗恶性梗阻性黄疸的临床疗效。方法 2011年6月—2013年9月收治恶性梗阻性黄疸患者40例。行胆道支架植入术治疗患者18例，为对照组；采用125I粒子条联合胆道支架植入患者22例，为观察组。两组均采用经皮肝穿刺胆道引流（PTCD）并胆道支架植入。结果 观察组与对照组的平均胆道开通时间分别为（8.7 ± 0.7）和（6.2 ± 0.4）个月，两组比较差异有统计学意义（P < 0.05）。观察组与对照组术后平均生存时间分别为（11.4 ± 0.8）和（8.7 ± 0.5）个月，生存时间的差异有统计学意义（P < 0.05）。术后近期疗效及并发症两组之间的比较无明显差异（P > 0.05），但是远期疗效有显著差异（P < 0.05）。结论 与对照组相比，观察组的术后生存时间及胆道开通时间明显延长，对于125I粒子条联合支架治疗恶性梗阻性黄疸值得进一步临床研究。