聚氨酯分散剂在液体靛蓝制备中的应用

采用异佛尔酮二异氰酸酯(IPDI)、聚乙二醇200、400、600、800(PEG200、PEG400、PEG600、PEG800)、2,2-二羟甲基丙酸(DMPA)、1-苯基-1,2-乙二醇、中和剂三乙胺(TEA)、甲乙酮肟等为原料,制备了一种阴离子聚氨酯分散剂.通过FTIR、GPC、TG表征了分散剂的结构与性能.利用自制的分散剂采用研磨法制备了液体靛蓝分散液,以液体靛蓝分散液粒径、离心稳定性、储存稳定性为指标,探讨了分散剂链长、用量对分散液性能的影响.结果表明,研磨1 h后,以PEG400为软段合成的聚氨酯分散剂用量为染料质量的60％时制备的液体靛蓝粒径为277.1 nm,1000 r/min离心稳定性达到93.98％,3000 r/min离心稳定性为51.13％,常温放置7 d后粒径变化在20 nm以内,染色后织物的颜色深度(K/S)为10左右,约是粉状靛蓝染色K/S的2倍,染色织物的颜色性能并未改变,SEM显示分散体颗粒大小分布均匀,与分散剂甲基萘磺酸钠的甲醛缩合物(MF)和木质素85A相比,其分散体系稳定性差别不大.     

Fabrication and characterizations of Cr3+-doped ZnGa2O4 transparent ceramics with persistent luminescence

0.5 at.% Cr:ZnGa₂O₄ precursor was synthesized by the co-precipitation method with nitrates as raw materials, using ammonium carbonate as the precipitant. Low-agglomerated Cr:ZnGa₂O₄ powders with an average particle size of 43 nm were obtained by calcining the precursor at 900℃ for 4 h. Using the powders as starting materials, 0.5 at.% Cr:ZnGa₂O₄ ceramics with an average grain size of about 515 nm were prepared by presintering at 1150℃ for 5 h in air and HIP post-treatment at 1100℃ for 3 h under 200 MPa Ar. The in-line transmittance of 0.5 at.% Cr:ZnGa₂O₄ ceramics with a thickness of 1.3 mm reaches 59.5% at the wavelength of 700 nm. The Cr:ZnGa₂O₄ ceramics can be effectively excited by visible light and produce persistent luminescence at 700 nm. For Cr:ZnGa₂O₄ transparent ceramics, the brightness of afterglow was larger than 0.32 mcd/m² after 30 min, which is far superior to that of Cr:ZnGa₂O₄ persistent luminescence powders.     

Adaptive compensation of persistent actuator failures of nonlinear systems

In this article, adaptive compensation designs are developed for nonlinear systems with uncertainties from the system functions and persistent actuator failures of characterizations that (i) some unknown system inputs are stuck at some unknown fixed or varying values at unknown time instants and (ii) the failure pattern always switches from one to another and the switching does not stop. Such a controlled plant is described by an uncertain time-varying nonlinear system, and some robust adaptive feedback linearization based failure compensation results are studied for closed-loop system stabilization and bounded output tracking for some specific conditions. To improve the tracking performance in the presence of persistent actuator failures, a new adaptive control scheme is developed, using the failure indicator function which contains the failure pattern and failure time in the formulation. Detailed stability and tracking performance are shown. Simulation results are shown to verify the effectiveness of the proposed adaptive actuator failure compensation method.     

Structural,optical and electrical properties of indium doped Cu2ZnSn(S,Se)4 thin films synthesized by the DC and RF reactive magnetron cosputtering

Element doping into the Cu₂ZnSn(S,Se)₄ (CZTSSe) absorber is an effective method to optimize the performance of thin film solar cells. In this study, the Cu₂In_xZn_1-xSn(S,Se)₄ (CIZTSSe) precursor film was deposited by magnetron cosputtering technique using indium (In) and quaternary Cu₂ZnSnS₄ (CZTS) as targets. Meanwhile, the In content was controlled using the direct current (DC) power on In target (P_In). A single kesterite CIZTSSe alloy was formed by successfully doping a small number of In³⁺ into the main lattice of CZTSSe. The partial Zn²⁺ cations were substituted by In³⁺ ions, resulting in improving properties of CZTSSe films. Morphological analysis showed that large grain CIZTSSe films could be obtained by doping In. The well-distributed, smooth, and dense film was obtained when the P_In was 30 W. The band gap of CIZTSSe could be continuously adjusted from 1.27 to 1.05 eV as P_In increased from 0 to 40 W. In addition, the CIZTSSe alloy thin film at P_In = 30 W exhibited the best p-type conductivity with Hall mobility of 6.87 cm²V^?1s^?1, which is a potential material as the absorption layer of high-performance solar cells.     

液相色谱法快速检测染色梅鱼中日落黄、柠檬黄的含量

目的建立一种快速、低成本检测染色梅鱼中日落黄、柠檬黄的方法。方法将染色梅鱼剥皮,鱼皮经70%甲醇氨水提取液提取,经EclipseXDB-C_(18)色谱柱分离,以甲醇和乙酸铵水溶液为流动相,进行梯度洗脱,流速为1.0 mL/min,柱温35℃,利用紫外检测器检测日落黄、柠檬黄的含量。结果日落黄、柠檬黄在1.25、2.5、12.5、25 mg/kg添加水平的加标回收率为80%～90%,相对标准偏差小于10%(n=6),柠檬黄检出限为0.05 mg/kg,日落黄检出限为0.025 mg/kg。结论该方法快速、准确、成本低,适合染色梅鱼中日落黄、柠檬黄的快速检测。     

Combining molybdenum carbide with ceria overlayers to boost Mo/CeO2 catalyzed ammonia synthesis

The design of an efficient non-noble metal catalyst is of burgeoning interest for ammonia synthesis. Herein, we report a Mo₂C/CeO₂ catalyst that is superior in ammonia synthesis activity. In this catalyst, molybdenum carbide coexisted with the ceria overlayers which is from the ceria support as the strong metal–support interaction. There is a high proportion of low-valent Mo species, as well as high concentration of Ce³⁺ and surface oxygen species. The presence of Mo₂C and CeO₂ overlayers not only leads to enhancement of hydrogen and nitrogen adsorption, but also facilitates the desorption and exchange of adsorbed species with the gaseous reagents. Compared with the Mo/CeO₂ catalyst prepared without carbonization, the Mo₂C/CeO₂ catalyst is more than sevenfold higher in ammonia synthesis rate. This work not only presents an explicit example of designing Mo-based catalyst that is highly efficient for ammonia synthesis by tuning the adsorption and desorption properties of the reactant gases, but opens a perspective for other elements in ammonia synthesis.     

Toughness enhancement and equivalent initial fracture toughness of cementitious composite reinforced with aligned steel fibres

Based on theoretical analysis and numerical simulation, the impact of steel fibres on the stress intensity factor (SIF) at the crack tip for cementitious composite was studied. The enhanced toughness of steel fibre reinforced cementitious composite (SFRC) in resisting cracks was explained by the decrement of SIF caused by steel fibre inclusions at the crack tip of the composite. The equivalent initial fracture toughness was used to characterize the crack initiation of SFRC. A simplified method for determining the of SFRC was proposed based on a linear regression method. Fracture tests were conducted on three‐point bending notched beams with different steel fibre volume fractions and specimen sizes to study the crack initiation behaviour of aligned steel fibre reinforced cementitious composite (ASFRC). of ASFRC was calculated, and the size effect of was analysed. The results showed that slightly increased with the steel fibre volume fraction and gradually became stable. For the tested specimens, whose heights varied between 40 and 100 mm, the specimen size had little impact on the .     

Data sharing mechanism of various mineral resources based on blockchain

Basins with various mineral resources coexisting and enriching often occupy an important strategic position. The exploration of various mineral resources is repetitive at present due to unshared data and imperfect management mechanism. This situation greatly increases the cost of energy exploitation in the country. Traditional data-sharing mode has several disadvantages, such as high cost, difficulty in confirming the right of data, and lack of incentive mechanism, which make achieving real data sharing difficult. In this paper, we propose a data-sharing mechanism based on blockchain and provide implementation suggestions and technical key points. Compared with traditional data-sharing methods, the proposed data-sharing mechanism can realize data sharing, ensure data quality, and protect intellectual property. Moreover, key points in the construction are stated in the case study section to verify the feasibility of the data-sharing system based on blockchain proposed in this paper.