粉末冶金TiAl合金排气门的研制

利用元素粉末冶金方法制备了TiAl合金排气阀。为提高排气门杆部的致密度、均匀度 ,设计了特有的径向热压工艺 ,并从理论上分析了与该工艺相关的压坯密度、致密化和应力变化规律。制备出高径比为 10 .7,密度为 3.79g/cm3 的粉末冶金TiAl合金汽车发动机排气门     

铍材应力常数的X射线法测试

在X2001应力分析仪上采用悬臂梁加载法测试了可以用于铍的X射线应力测试的5个衍射晶面的应力常数。结果表明,铍的5个衍射晶面的应力常数差异较大，在进行X射线应力分析时．应采用相应衍射晶面的应力常数，才能获得准确的应力分析结果。由于X射线对铍有较大的穿透深度，必须考虑X射线穿透深度对应力常数标定的影响。     

Graph-Based Dimensionality Reduction for Hyperspectral Imagery: A Review

Hyperspectral image(HSI) contains a wealth of spectral information, which makes fine classification of ground objects possible. In the meanwhile, overly redundant information in HSI brings many challenges. Specifically, the lack of training samples and the high computational cost are the inevitable obstacles in the design of classifier. In order to solve these problems, dimensionality reduction is usually adopted. Recently, graph-based dimensionality reduction has become a hot topic. In this paper, the graph-based methods for HSI dimensionality reduction are summarized from the following aspects. 1) The traditional graph-based methods employ Euclidean distance to explore the local information of samples in spectral feature space. 2) The dimensionality-reduction methods based on sparse or collaborative representation regard the sparse or collaborative coefficients as graph weights to effectively reduce reconstruction errors and represent most important information of HSI in the dictionary. 3) Improved methods based on sparse or collaborative graph have made great progress by considering global low-rank information, local intra-class information and spatial information. In order to compare typical techniques, three real HSI datasets were used to carry out relevant experiments, and then the experimental results were analysed and discussed.Finally, the future development of this research field is prospected.     

熔剂净化对Al－4．5wt％Cu合金过冷及组织的影响

采用盐类熔剂对大体积Ａｌ－４．５ｗｔ％Ｃｕ合金进行净化处理，研究了熔剂净化对Ａｌ－４．５ｗｔ％Ｃｕ合金过冷及组织的影响。通过大量的实验研究证明：粘性熔剂更能有效地去除合金中的异质核心，使合金获得较大的过冷度；随着过冷度的增大，合金的宏观组织由细小的等轴晶逐渐过渡到粗大的柱状晶，其临界转变过冷度为４０℃；二次枝晶间距随过冷度的增大而增大，其转变过冷度为５０℃。     

Simulation study on the gasification process of Ningdong coal with iron-based oxygen carrier

Chemical looping gasification (CLG) of Ningdong coal by using Fe₂O₃ as the oxygen carriers (OCs) was studied, and the gasification characteristics were obtained. A computation fluid dynamics (CFD) model based on Eulerian‐-Lagrangian multiphase framework was established, and a numerical simulation the coal chemical looping gasification processes in fuel reactor (FR) was investigated. In addition, the heterogeneous reactions, homogeneous reactions and Fe₂O₃ oxygen carriers' reduction reactions were considered in the gasification process. The characteristics of gas flow and gasification in the FR were analyzed and it was found that the experiment results were consistent with the simulation values. The results show that when the O/C mole rate was 0.5:1, the gasification temperature was 900 ℃ and the water vapor volume flow rate was 2.2 ml·min^-1, the mole fraction of syngas reached a maximum value of the experimental result and simulation value were 71.5% and 70.2%, respectively. When the O/C mole rate was 0.5:1, the gasification temperature was 900 ℃, and the water vapor volume flow was 1.8 ml·min^-1; the gasification efficiency reached the maximum value was 62.2%, and the maximum carbon conversion rate was 84.0%.     

Fouling characteristics of 90° elbow in high salinity wastewater from coal chemical industry

Due to the high salt content of coal chemical wastewater, pipeline fouling often occurs during wastewater treatment. Fouling will cause the diameter of the pipe to shrink or even block, which is not conducive to the safe and stable operation of the wastewater treatment process. In this paper, the experimental device was designed by using FLUENT software and the fouling deposition mechanisms at different flow velocities and different positions in a 90 deg bend were studied. The experimental results show that when the flow velocity is between 0.2 m·s~(-1) and 0.3 m·s~(-1), the thickness of fouling layer was positively correlated with the flow velocity; when the flow velocity is equal to 0.4 m·s~(-1), the formation of fouling is the most serious; when the flow velocity is between 0.4 m·s~(-1) and 0.7 m·s~(-1), the thickness of fouling layer was negative correlation with the flow velocity; with the increase of inlet velocity, the time for sediment point to develop into sediment surface is shortened. The fouling layer is easy to fall off because of the large shear force on the wall surface of the inner bend of the 90° elbow, so the density of sediment at this position is high.     

风电叶片大梁用碳纤维拉挤板材组合式加载压缩(CLC)测试浅析

依据ASTM D6641/D6641M-16《采用组合加载方式(CLC)测定聚合物基复合材料层压板压缩性能试验方法》标准,对风电叶片大梁用碳纤维拉挤板材进行压缩性能测试,通过采用不同类型的加强片制备压缩试样,对所测得的压缩强度、压缩模量和压缩应变的试验结果与失效模式进行分析.结果 表明,采用文中C型加强片制备的压缩试样,测得的压缩强度、压缩模量、压缩应变以及失效模式均较为理想,试验结果重复性较好.     

Importance of Low-Temperature Melt-Mixing on the Construction of Stereocomplex Crystallites with Superior Nucleation Efficiency in Asymmetric Poly(l-lactide)/Poly(d-lactide) Blends

The nucleation efficiency (NE) of stereocomplex crystallites (SCs) formed in asymmetric poly(L-lactide)/poly(D-lactide) (PLLA/PDLA) blends is generally unsatisfactory because the competition between stereocomplexation and chain mixing involved in the melt-mixing process can cause low formation efficiency and even severe aggregation of SCs. Herein, it is attempted to achieve high-efficient formation of finely dispersed SCs particles by designing a unique melt-mixing procedure, where the mixing of PLLA with 0.75 wt% PDLA is first performed at elevated temperatures (far above the melting temperature of SCs) to allow the homogeneous mixing of PLLA/PDLA chains and then at a low temperature (slightly above that of homocrystallites) to permit the full stereocomplexation of the premixed chains. It is found that the SCs formed in the blends exhibit unexpectedly low NEs (e.g., 54.5%), much inferior to that (73.6%) in the counterpart without undergoing premixing. This is because the introduction of premixing leads to a remarkable deterioration in the amount of SCs particles formed, despite decreased particle size, highlighting that the direct mixing at low temperatures of 170–180 °C (about 20–30 °C lower than that used in common melt-processing of PLA) is more effective for the construction of SCs with superior NE. The mechanisms for these striking findings are discussed.     

Stereocomplex Crystallization Induced Significant Improvement in Transparency and Stiffness–Toughness Performance of Core-Shell Rubber Nanoparticles Toughened Poly(l-lactide) Blends

Toughening modification of poly(l -lactide) (PLLA) with rubber particles is often realized at the cost of transparency, mechanical strength, and modulus because high rubber loadings are generally required for toughening. In this work, a promising strategy to simultaneously improve the transparency and stiffness–toughness performance of poly(butyl acrylate)-poly(methyl methacrylate) (BAMMA) core-shell rubber nanoparticles toughened PLLA blends by utilizing the stereocomplex (SC) crystallization between PLLA and poly(d -lactide) (PDLA) is devised. The results reveal that the construction of SC crystallites in PLLA matrix via melt-mixing PLLA/BAMMA blends with PDLA can prevent BAMMA nanoparticles from aggregation and promote them to form network-like structure at lower contents. As a result, not only higher toughening efficiency with less rubber contents but also superior transparency is achieved in the PLLA/PDLA/BAMMA blends as compared with the PLLA/BAMMA ones where large aggregated BAMMA clusters are formed. Moreover, the outstanding reinforcement of SC crystallites network for PLLA can impart an enhanced tensile strength and modulus to PLLA/PDLA/BAMMA blends, thus improving the stiffness–toughness performance of PLLA/PDLA/BAMMA blends to a higher degree. This work demonstrates that SC crystallization is a promising solution to solve the contradiction between transparency and mechanical properties and then obtain superior comprehensive performances in rubber toughened PLLA blends.     

Influences of mullite fibers on mechanical and thermal properties of silica-based ceramic cores

Mullite fibers composite silica-based ceramic cores were successfully prepared by injection molding. The effects of mullite fibers on the mechanical and thermal properties of ceramic cores were investigated. The results indicated that the linear shrinkage was significantly decreased and the porosity was gradually increased with the increase of mullite fibers. In addition, the flexural strength for the room temperature and the simulated casting temperature of 1500°C was increased to a maximum value when the content of mullite fibers was about 1 wt.%, and then decreased with the increase of mullite fibers. The mullite fibers of 1 wt.% presented excellent mechanical properties with a linear shrinkage of .65%, a porosity of 6.96%, and a flexural strength of 17 MPa at room temperature and 34.83 MPa at the simulated casting temperature of 1500°C. Besides, the change in microstructure and properties in various contents of mullite fibers were analyzed.