Application of the solid polymer electrolyte (SPE) method to organic electrochemistry—III. Kolbe type reactions on Pt-SPE

The feasibility of a solid polymer electrolyte (SPE) method for Kolbe type reactions was investigated by using Pt-SPE composed with Nafion 415 and platinum. The Kolbe reaction of acetic acid proceeded effectively on one side and both sides Pt-SPE composites. The lower current efficiency was observed on the latter than on the former. Neat acetic acid could also be electrolysed on both sides SPE though the cell voltage was fairly high.A methanolic solution of monomethyl adipate was electrolysed to give dimethyl sebacate on both sides Pt-SPE according to the Brown-Walker reaction. The current efficiency and the terminal voltage increased with the concentration of monomethyl adipate. Pt-SPE behaved as an active electrode of a high roughness factor, eg about 6, for the Kolbe reaction of acetate.     

Current transients of passive iron observed during micro-indentation in pH 8.4 borate buffer solution

Micro-indentation test of passive iron electrode in deaerated pH 8.4 borate buffer solution was carried out to investigate the rupture and repair of passive film. During driving a conical diamond micro-indenter with a load of 0.1 N order downward to the electrode and driving upward from the electrode, a couple of anodic current peaks were observed. The first current peak spiked during loading was responsible for partial exposure of iron substrate to the solution due to rupture of the passive film when the indenter tip contacted. The second peak emerged during unloading when elastic deformation recovered, which was ascribed to repair at the ruptured sites. The second peak current was larger than the first one. Both peaks were sensitively influenced by electrode potential or concentration of sulfate ions containing in solution. The model for a series of rupture and repair processes of the passive film by micro-indentation was proposed to discuss the current transients.     

Phase structure in the blend of atactic poly(vinyl alcohol) with atactic poly(vinyl alcohol‐block‐vinyl acetate)

An almost fully saponified atactic poly(vinyl alcohol) and an atactic poly(vinyl alcohol‐block‐vinyl acetate) of which degree of saponification is 89 mol % were blended by a solution casting method. The phase structure of the blend film was analyzed by optical microscopy, ¹³C‐NMR, and differential scanning calorimetry. The most remarkable structure of the blend was composed of cylindrical domains penetrating the film. The swelling behavior of the blend films was also investigated in the dimethylsulfoxide and water mixed solvents to find differences in solubility and diffusion behavior between the matrix and the domain. The cylindrical domains could be selectively dissolved away in water and the film became porous. We tried to change the size of the cylindrical domain with various film preparation conditions. This aimed to turn the film into the useful filter membrane. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 86: 1807–1815, 2002     

Production of Ceramic Green Bodies Using a Microwave-Reactive Organic Binder

Because the pyrolysis of organic substances can result in the emission of harmful pollutant gases, a reduction in the use of organic binders is one aim of today's ceramics industry. A novel ceramic-forming process was developed that requires considerably less organic binder than conventional techniques. The process involves immobilizing reactive molecules on the surfaces of the particles, which on subsequent irradiation with microwaves, form bridges that bind the entire particle assembly together. The chemical forces involved produce strong bonds, resulting in a significant reduction in the amount of organic binder that is required to maintain the shape of the ceramic green body. This method will help to decrease emissions of harmful gases produced from pyrolysis of the binder.     

Selective gas transport in miscible PPO-PS blends

The permeation rates of He, CO₂ and CH₄ though miscible blends of polystyrene and poly(phenylene oxide) at 35°C are reported as a function of pressure. Sorption isotherms for CO₂ and CH₄ are also presented. By using ratios of the permeabilities of the pure gases the separation factors for the gas pairs He---CH₄ and CO₂---CH₄ can be estimated. For both pairs the estimated separation factor goes through a prominent maximum, thus indicating that these blends are more permselective than expected from the behaviour of polystyrene and poly(phenylene oxide). This stems from mobility considerations rather than solubility effects and a qualitative free volume argument is proposed as an explanation. The sorption and transport data have been interpreted and correlated using the dual sorption-mobility models developed previously for glassy polymers. Since the commercial polystyrene used contained a small amount of mineral oil to improve flow behaviour, the effect of this additive on polystyrene properties was explored in some detail.     

Synthesis of polyethylene oxide end‐capped with perfluoroalkyl groups/polystyrene prototype brushes

Polystyrene (PS)/poly(ethylene oxide) (PEO) prototype brushes were prepared by alternating free‐radical copolymerization of methacryloyl‐terminated PS and α‐vinylbenzyl‐ω‐hydroxy or α‐vinylbenzyl‐ω‐perfluoroalkyl (R_f) PEO macromonomers with the addition of Lewis acid (SnCl₄). It was found from their dilute‐solution properties that PS/PEO end‐capped with R_f (PBR_f), and PS/PEO having OH groups at terminal ends (PBOH) prototype brushes formed a single molecule in benzene and aggregates in chloroform, respectively. However, the brush PBOH formed a single molecule in N,N‐dimethylformamide. Such aggregation behaviors seemed to be caused by the interaction between hydroxy groups of PEO chain ends. The brush PBOH was also converted into PBR_f‐type brush by chemical modification, using corresponding acid chloride. The substitution of R_f groups was ～70% due to slipping of terminal hydroxy groups into PEO internal domains. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 772–778, 2006     

Strength and Fracture Toughness of Isostatically Hot-Pressed Composites of Al2O3 and Y2O3-Partially-Stabilized ZrO2

Composites of Al₂O₃ and Y₂O₃ partially-stabilized ZrO₂ were isostatically hot-pressed using submicrometer powders as the starting material. The addition of Al₂O₃ resulted in a large increase in bending strength. The average bending strength for a composite containing 20 wt% Al₂O₃ was 2400 MPa, and its fracture toughness was 17 MN·w^−3/2     

Coal liquefaction by in-situ hydrogen generation.: 2. Zinc-water model compound reactions

Model compound studies were carried out to elucidate the reaction mechanisms taking place during the liquefaction of coal with the hydrogen produced from the reaction of zinc and water. In compounds of the type Ph-(CH₂)_n-Ph the splitting of the aliphatic bridge was easier with higher n values. Ether type compounds such as diphenylether were unreactive although the C-O bond in dibenzylether was easily cleaved. Condensed ring aromatic compounds gave low conversion with hydrogenation being facilitated by an increase in ring number. Phenolic compounds such as phenol did not react well, but the reactivity increased with increase in aromatic ring size. The cleavage of the aliphatic bridge was accelerated by the OH group, for example, in the case of 4-hydroxydiphenylmethane bond scission was about 15 times higher than that of diphenylmethane. Heterocyclic compounds were unreactive.     

Effects of Annealing on Dielectric Loss and Microstructure of Aluminum Nitride Ceramics

The effect of annealing on tan δ and microstructures of aluminum nitride (AlN) ceramics were explored. Yttria was added as a sintering additive to AlN powders, and the powders were pressureless-sintered at 1900°C for 2 h in a nitrogen flow atmosphere. In succession to sintering, AlN samples were annealed at 720, 970 and 1210°C for 2 and 4 h. Very low tan δ values between 2.6 and 6.0 × 10⁻⁴ at 28 GHz were obtained when the AlN samples were annealed for 4 h at all the annealing temperatures.     

Effect of Grain Boundaries on Thermal Conductivity of Silicon Carbide Ceramic at 5 to 1300 K

The thermal conductivity of a SiC ceramic was measured as 270 W·m⁻¹·K⁻¹ at room temperature. At low temperatures ( T < 25 K), the decrease in the conductivity was proportional to T ³ on a logarithmic scale, which indicated that the conductivity was controlled by boundaries. The calculated phonon mean free path in the ceramic increased with decreased temperature, but was limited to ∼4 μm, a length almost equal to the grain size, at temperatures below 30 K. We concluded that the thermal conductivity of the ceramic below 30 K was influenced significantly by grain boundaries and grain junctions.