基体温度对磁控溅射沉积ZAO薄膜性能的影响

利用中频交流磁控溅射方法 ,采用氧化锌铝陶瓷靶材 [w(ZnO) =98%、w(Al2 O3 ) =2 % ]制备了ZAO(ZnO∶Al)薄膜 ,观察了基体温度对ZAO薄膜的晶体结构、电学和光学性能的影响 ,采用X射线衍射仪对薄膜的结构进行了分析 ,采用光学分度计和电阻测试仪测量了薄膜的光学、电学特性 ,采用霍尔测试仪测量了薄膜的载流子浓度和霍尔迁移率。结果表明 :沉积薄膜时的基体温度对薄膜的结构、结晶状况、可见光透射率以及导电性有较大的影响。当基体温度为 2 5 0℃ ,Ar分压为 0 8Pa时 ,薄膜的最低电阻率为 4 6× 10 -4Ω·cm ,方块电阻为 35Ω时 ,可见光 (λ =5 5 0nm)透射率高达 92 0 %。     

Local residence time,residence revolution,and residence volume distributions in twin‐screw extruders

This work was aimed at studying the overall, partial, and local residence time distributions (RTD); overall, partial and local residence revolution distributions (RRD) and overall, partial and local residence volume distributions (RVD) in a co‐rotating twin screw extruder, on the one hand; and establishing the relationships among them, on the other hand. Emphasis was placed on the effects of the type and geometry of mixing elements (a gear block and various types of kneading elements differing in staggering angle) and process parameters on the RTD, RRD and RVD. The overall and partial RTD were directly measured in‐line during the extrusion process and the local ones were calculated by deconvolution based on a statistical theory. The local RTD allowed comparing the mixing performance of mixing elements. Also it was confirmed both experimentally and theoretically that specific throughput, defined as a ratio of throughput (Q) over screw speed (N), controlled all the above three types of residence distributions, be they local, partial or overall. The RRD and RVD do not provide more information on an extrusion process than the corresponding RTD. Rather they are different ways of representing the same phenomena. POLYM. ENG. SCI., 48:19–28, 2008. © 2007 Society of Plastics Engineers     

变频器在暖通空调行业中的应用

本文提出中央空调系统的一种变频调速改造方案，介绍了该系统的结构组成及运行原理，对系统各部分的作用进行了讨论。     

当代建筑源自通神学

通神学是西方社会科学发展的产物.当科学和人们信仰的宗教产生冲突时,人们的精神该何去何从？最终,人们的精神从通神学那里获得了安宁.本文通过研究通神学的产生,以及它对艺术,包括建筑艺术的影响,探索当代建筑的本原和发展方向--表达情感、激起情感.     

Global practical stabilization of planar linear systems in the presence of actuator saturation and input additive disturbance

In this note, we revisit the problem of global practical stabilization for planar linear systems subject to actuator saturation and input additive disturbances. A parameterized linear state feedback law is designed such that, by tuning the value of the parameter, all trajectories of the closed-loop system converge to an arbitrarily small neighborhood of the origin in a finite time and remain in there.     

Cr-Mo solid solutions forced by high-energy ball milling

Mixtures of Cr and Mo elemental powders, with the nominal compositions Cr₂₅Mo₇₅, Cr₅₀Mo₅₀, and Cr₇₅Mo₂₅, are processed by high-energy ball milling at ambient temperature. Milling is observed to force the mixing of the immiscible bcc elements Cr and Mo into solid solutions. The lattice parameter of these solid solutions, measured by X-ray diffraction (XRD), displays the expected positive deviation from Vegard’s law. These deviations are compared to the ones predicted by Eshelby’s inclusion model for dilute alloys. The conventional Williamson-Hall approach is shown to fail to determine the grain size in as-milled samples, probably due to the high density of dislocations. Annealing at 700 °C for 10 hours under argon leads to a large reduction in structural defect density, without inducing any significant decomposition. The mixing measured in Cr-Mo is discussed in the broader context of the mechanical mixing forced by ball milling in moderately immiscible systems.     

关于本地传输网网络优化的探讨

根据长期工作经验,对现有网络存在的问题进行分析,提出对本地传输网网络优化的有关建议。     

Parallel multilevel fast multipole method for solving large-scale problems

The Multilevel Fast Multipole Method (FMM) is a well-established method and can be applied to solve electromagnetic (EM) scattering problems. Compared with other traditional methods, it requires less computational time and memory. However, constrained by a single processor's speed and memory limitations, the problem size that can be solved by serial implementation is still relatively small. For a million-unknown target, the computational time on a single processor is intolerable, and memory could be easily exhausted. Parallel-computing technology, which can utilize multiprocessors, provides an efficient way to solve electrically large-scale EM problems. This paper will focus on discussing the parallel methodologies applied to a multilevel FMM code, as well as demonstrating the computational efficiency of the parallel approach.     

Al-Zn-Ce非晶合金的相选择与组织结构演化

本文研究了具有典型分解特征的Al-Zn-Ce非晶合金的形成和晶化过程，探讨了各种相的生成顺序。XRD和DSC测试结果表明强烈的化合物短程序有利于Al-Zn-Ce非晶合金的形成。在Al-Zn-Ce非晶合金的晶化过程中存在复杂的相选择行为，多种相的竞争形核和有限生长使其具有复杂的结构特点。同时，结果也表明冷速对该体系非晶的形成有很大影响。     

API长圆螺纹套管抗粘结性能的试验研究

通过对国内外大量石油套管螺纹参数的测量和全尺寸的模拟试验，以及对测量和试验数据的理论分析，找出了影响国产套管发生粘扣的原因，并在实际生产中实施验证。采取相应的措施改善了套管的抗粘结性能，同时套管的密封和抗滑脱性能并未下降。