腐植酸物质对盐碱化中低产田土壤理化性质及玉米影响的研究

通过田间试验探讨了复合改良制剂、草炭、风化煤等腐植酸类物质施用对盐碱化中低产田土壤理化性质及生长作物的影响，结果表明：复合改良制剂、草炭、风化煤施用对土壤理化性质均有积极的影响，与对照相比达到显著水平。玉米产量的方差分析表明，复合改良制剂处理与草炭、风化煤等处理差异显著，与对照差异极显著，增产率均达到30．67％以上。     

Modification of a carbon/carbon composite with a thermosetting resin precursor as a matrix by the addition of carbon black

Carbon/carbon composites were made through the pyrolysis of stabilized PAN felt and phenolic resin with the addition of 5 or 10 wt % carbon black to the matrix and then heat treatment at 600–2500°C. The effects of adding carbon black to the matrix precursor on the physical properties, microstructure, and mechanical properties of the resultant composites were investigated. Adding carbon black not only reduced the weight loss but also limited the shrinkage of the resultant composites. Adding carbon black also accelerated the formation of carbon basal planes in the matrix. At 2500°C, the crystalline stacking height in the composite with 10 wt % added carbon black was 200% greater than that with no additive. The flexural strength of the composite also increased from 15 to 42 MPa (almost 300%). © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 333–337, 2006     

用电势法测定混合电解质溶液中各个组分的活度系数

本文用无液接电势电池：Ｎａ－ＩＳＥ（或Ｋ－ＩＳＥ）｜（ＮａＣｌ（ｍＡ），ＫＣｌ（ｍＢ），Ｈ２Ｏ｜Ｃｌ－ＩＳＥ同时测定了２９８．１５Ｋ，溶液离子强度Ｉ：０．１、０．５、１．０、１．５、２．０和２．５ｍｏｌ／ｋｇ时，钠电极与氯电极组成的电池和钾电极与氯电极组成的电池的可逆电势值，根据Ｎｅｒｎｓｔ方程分别求出ＮａＣｌ－ＫＣｌ－Ｈ２Ｏ体系中，ＮａＣｌ和ＫＣｌ的平均活度系数。用Ｐｉｔｚｅｒ方程拟合两套实验数据，求出两套基本一致的Ｐｉｔｚｅｒ混合参数θＮａ－Ｋ和。将混合参数代回Ｐｉｔｚｅｒ方程，分别求出另一组分的平均活度系数，计算值与实验值比较，标准偏差分别为：０．００８１（ＮａＣｌ）和０．００７３（ＫＣｌ）。     

渣对铝镁炭砖的侵蚀与渗透

对电炉连铸钢包用后铝镁炭砖进行了ＳＥＭ和ＥＰＭＡ观测分析。探讨了渣对铝镁炭砖的侵蚀与渗透机理，并提出了抑制渣渗透的措施。     

基于WEB的高校教材评价体系的研究与实现

建立基于WEB的教材评价体系,可以及时有效地收集到学生、教师、专家对教材科学的评价意见,并且可以自动生成教材综合评级,为以后的教材编写和教材选取提供科学可靠的重要依据。本文为实现高效、科学、规范、准确的高校教材评价设计开发了一个简易高效的基于WEB的平台,系统基于MVC架构,采用JSP进行功能实现,数据库采用MySQL实现,WEB容器采用TomCat实现。设计中按逻辑划分为:模型(Model)、视图(View)、控制(Control)三个层次。     

PAAD-16酸液稠化剂的合成与性能

以二甲氨基丙基甲基丙烯酰胺和溴代十六烷为原料,丙酮为溶剂,合成了一种疏水单体——二甲基十六烷基(2-甲基丙烯酰胺基丙基)溴化铵(DHAB),并以DHAB、2-甲基-2-丙烯酰胺基丙磺酸(AMPS)和丙烯酰胺(AM)为单体,以自由基水溶液聚合法合成了一种疏水缔合聚合物P(AM-AMPS-DHAB)(PAAD-16),用IR、荧光光谱(FL)和SEM对其进行了结构表征。结果表明:PAAD-16的酸溶时间约为90 min;以该疏水缔合聚合物为主要添加剂配制而成的稠化酸在30℃、170s~(–1)下的表观黏度为59m Pa×s,在60、90℃下的热稳定性(ω)分别为85.0%和66.1%,在该条件下连续剪切120 min后剪切稳定性(ω')为81.4%,具有良好的增黏性、耐温抗剪切性和缓速性能。     

平衡硫化体系硫化天然橡胶的性能研究

对平衡硫化（ＥＣ）体系硫化天然橡胶（ＮＲ）的性能进行了研究，并与半有效硫化（ＳＥＶ）体系和传统硫化（ＣＶ）体系硫化ＮＲ进行了对比。结果表明，ＥＣ体系返原作用略高于ＳＥＶ体系，明显低于ＣＶ体系，硫化６ｈ时的返原率依次为７．７％，０．４％和３４．０％；与ＳＥＶ和ＣＶ体系相比，ＥＣ体系ＮＲ硫化胶拉伸强度、撕裂强度和３００％定伸应力高，生热低，耐磨性和耐屈挠性好。ＥＣ体系ＮＲ硫化胶的耐热氧老化性能优于ＳＥＶ体系，更优于ＣＶ体系。     

浅析呼和浩特市大气SO2发展趋势及防治对策

本文通过对二氧化硫的形成及危害的阐述，以及对我市近几年大气中二氧化硫监测结果的分析，针对发展趋势和存在的问题，根据实际情况提出相应的建议。     

Ohmic contacts to semiconducting diamond using a Ti/Pt/Au trilayer metallization scheme

Ohmic contacts have been fabricated on a naturally occurring type IIb diamond crystal using an annealed Ti/Pt/Au trilayer metallization where the Pt served successfully as a barrier to Ti diffusion into the Au capping layer. However, a specific contact resistance could not be reliably determined using transmission line model measurements. Auger microanalysis revealed the presence of Ti on the diamond surface near the ohmic contact pads. The most likely origin of the Ti on the diamond surface was determined to be lateral diffusion from beneath the contact pads. This would have produced a nonuniform concentration of Ti across the diamond surface which, in turn, would have affected the diamond sheet resistance in a complicated way.     

机械力化学湿法一步制备表面修饰磷酸锌微粉

以氧化锌和磷酸为原料,以硅烷偶联剂为改性剂,采用机械力化学湿法制备微细磷酸锌并进行表面改性.用XRD、润湿角、活化指数、沉降时间等手段对产物进行表征,用FT-IR对改性粉末的结构进行分析,初步探讨了偶联剂与磷酸锌的作用机理.结果表明产物为二水和四水磷酸锌混合物;在红外区域2 800～3 000 cm-1和1 400 cm-1有偶联剂的特征吸收峰,说明偶联剂与磷酸锌之间发生了化学反应;当硅烷偶联剂添加质量分数由0增加到2%,改性产品的活化指数由0增加到98.71%,对水的润湿角由0°增加到93.21°,沉降时间由0.5 h增加到176 h,在涂料中的分散性和贮存稳定性得到改进.