Temperature Dependence of KIC for High-Pressure Hot-Pressed Si3N4 Without Additives

Temperature dependence of K_IC values for Si₃N₄ bodies sintered at high pressures without additives was studied from room temperature to 1400°C. Little change in K_K was found in this range.     

Effect of MgO Addition on the Bondability and Interfacial Reaction between Dielectric and Glass-Ceramics for the Fabrication of Multi-Component Ceramic Substrates

Bondability and interfacial reaction between dielectric and insulator layers have been examined to obtain a basic understanding of bonding mechanisms. Lead-containing complex perovskite was used as a dielectric material. Two kinds of glass-ceramics were used as insulator material; lead borosilicate glass containing Al_2O3 (insulator A) and the same containing Al₂O₃ and M_gO (insulator B). Dielectric and insulator layers did not bond when insulator A was used. When insulator B was used, however, strong bonding was achieved between the two layers by firing the powder compacts at temperatures between 800° and 1000°C. Addition of M_gO to lead borosilicate glass increased the thermal expansion coefficient to that of the dielectric and enhanced the formation of reaction layers, resulting in good bonding. Two reaction layers were identified. The main reaction products were enstatite and bredigite for one layer contacting the dielectric, and enstatite and a compound with the same diffraction pattern as that of faujasite for the other layers contacting insulator B.     

Influence of the nigrosine dye on the thermal behavior of polyamide 66

To reveal the effect of the nigrosine dye, that the addition of the dye lowers the crystallization point (T_c) of molten polyamide resins with substantially no shift in the melting point (T_m), thus suppressing the crystallization enhancement of the crystalline nucleation agents, the characteristics of polyamide 66 (PA‐66) containing nigrosine dye EX (N‐EX) were investigated. Differential scanning calorimetry (DSC) analysis showed that the addition of N‐EX reduced the crystallization rate and T_c of molten PA‐66 with substantially no shift in T_m, and the crystallization enthalpy per unit of weight of PA‐66 was substantially constant. T_c of molten PA‐66 was lowered with an increase in the amount of N‐EX and reached its maximum at 13 wt % N‐EX. Dynamic mechanical analysis showed that the glass‐transition temperature and the secondary glass‐transition temperature increased with an increasing amount of the dye. On the other hand, the DSC and X‐ray diffraction results indicated that no dye molecule was present in the crystal structure of PA‐66. This effect of the nigrosine dye on PA‐66 is in contrast to those of crystalline nucleation agents, plasticizers, and antiplasticizers. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 3270–3274, 2006     

Effect of degree of polymerization on gelation and flow processability of poly(vinyl chloride)

The effect of degree of polymerization (DP) on the gelation and flow processability of poly(vinyl chloride) (PVC) was studied. Sheets with adjusted degree of gelation were prepared by rolling rigid pipe formulation suspension PVC compounds with DPs of 800, 1050 and 1300 by changing the milling temperature. Their degrees of gelation were measured with DSC and their capillary flow properties were measured with a capillary rheometer at 150, 170 and 190°C and the effect of DP on the relation between gelation and flow processabilities was studied. Because of the higher shearing heat during milling, the sample with the higher DP had a higher history temperature and thus tended to show a higher degree of gelation. The viscosity increased as the gelation increased. The dependency of viscosity on DP was higher at higher milling and extrusion temperatures and thus at a higher degree of gelation and a lower shear rate. This was assumed to be attributed to the more prominent uniform molecular flow as against the particle flow. The die swell increased with increasing the milling and extrusion temperatures and hence with increasing the gelation. A sample with a lower DP tended to show a larger die swell and this tendency was even more pronounced at the higher extrusion temperature. The melt fracture easily occurred when a sample with advanced gelation was extruded at low temperature. Whereas at low milling temperatures a sample with the lower DP showed a lower critical shear rate at onset of melt fracture, and thus easily generating melt fracture, at high milling temperatures it showed a higher critical shear rate and hence scarcely generated melt fracture. These experimental results were explained by the fact and concept that a sample with a lower DP shows a higher increase in the gelation during extrusion and/or the slighter feature of particle flow as against the uniform molecular flow at the same gelation level. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 92: 1915–1938, 2004     

Characterization and Sintering Behavior of Alkoxide-Derived Aluminosilicate Powders

Submicrometer SiO₂-Al₂O₃ powders with compositions of 46.5 to 76.6 wt% Al₂O₃ were prepared by hydrolysis of mixed alkoxides. Phase change, mullite composition, and particle size of powders with heating were analyzed by DTA, XRD, IR, BET, and TEM. As-produced amorphous powders partially transformed to mullite and Al-Si spinel at around 980°C. The compositions of mullite produced at 1400° and 1550°C were richer in Al₂O₃ than the compositions of stable mullite solid solutions predicted from the phase diagram of the SiO₂-Al₂O₃ system. Particle size decreased with increasing Al₂O₃ content. The sintered densities depended upon the amount of SiO₂-rich glassy phase formed during sintering and the green density expressed as a function of particle size.     

Effect of Nd2O3 Concentration on the Defect Structure of CeO2–Nd2O3 Solid Solution

An extensive X-ray study of CeO₂–Nd₂O₃ solid solutions was performed, and the densities of solid solutions containing various concentrations of NdO_1.5 were measured using several techniques. Solid solutions containing 0–80 mol% NdO_1.5 were synthesized by coprecipitation from Ce(NO₃)₃ and Nd(NO₃)₃ aqueous solutions, and the coprecipitated samples were sintered at 1400°C. A fluorite structure was observed for CeO₂–NdO_1.5 solid solutions with 0–40 mol% NdO_1.5, which changed to a rare earth C-type structure at 45–75 mol% NdO_1.5. The change in the lattice parameters of CeO₂–NdO_1.5 solid solutions, when plotted with respect to the NdO_1.5 concentration, showed that the lattice parameters followed Vegard's law in both the fluorite and rare earth C-type regions. The maximum solubility limit for NdO_1.5 in CeO₂ solid solution was approximately 75 mol%. The relationship between the density and the Nd concentration indicated that the defect structure followed the anion vacancy model over the entire range (0–70 mol% NdO_1.5) of solid solution.     

Fractionation and enrichment of CLA isomers by selective esterification with Candida rugosa lipase

A commercial product of CLA contains almost equal amounts of cis-9,trans-11 (c9,t11)-CLA and trans-10,cis-12 (t10,c12)-CLA. We attempted to enrich the two isomers by a two-step selective esterification using Candida rugosa lipase that acted on c9,t11-CLA more strongly than on t10,c12-CLA. An FFA mixture containing CLA isomers was esterified with an equimolar amount of lauryl alcohol in a mixture of 20% water and the lipase. When the esterification of total FA reached 50%, two isomers were fractionated in a good yield: t10,c12-CLA was enriched in FFA, and c9,t11-CLA was recovered in lauryl esters. The FFA were esterified again to enrich t10,c12-CLA. At 27.3% esterification of total FA, the t10,c12-CLA content in FFA increased to 64.8 wt% with 89.3% recovery: The ratio of the content of t10,c12-CLA to that of two isomers was 95.9%. Lauryl esters obtained by the single esterification were employed for enrichment of c9,t11-CLA. After the esters were hydrolyzed, the resulting FFA were esterified again with lauryl alcohol. At 62.0% esterification of total FA, the c9,t11-CLA content in lauryl esters increased to 73.3 wt% with 79.4% recovery: The ratio of the content of c9,t11-CLA to that of two isomers was 95.6%. In a 600-g-scale purification, molecular distillation was effective in separating the reaction mixture into lauryl alcohol, FFA, and lauryl ester fractions.     

Radiation-induced polymerization of ethylene in pilot plant. III. Heavy-phase recycling process

Radiation-induced polymerization of ethylene using aqueous tert-butyl alcohol as medium was carried out in a large-scale pilot plant with a 50-liter central source-type reactor at a pressure of 105 to 395 kg/cm², temperature of 30° to 80°C, mean dose rate of 4.5 × 10⁴ to 1.9 × 10⁵ rads/hr, ethylene feed rate of 5.5 to 23.5 kg/hr, and medium feed rate of 21 to 102 l./hr. The space–time yield and molecular weight of the polymer were in the range of 4.7 to 16.8 g/l.-hr and 1.3 × 10⁴ to 8.9 × 10⁴, respectively. The space–time yield and molecular weight increased with mean residence time at 30°C, whereas at 80°C they became almost independent of the time. The space–time yield increased with pressure and dose rate, slightly decreased with temperature, and was maximum at ethylene molar fraction of 0.5. The polymer molecular weight increased with pressure and ethylene molar fraction, and decreased with dose rate and temperature. The total amount of deposited polymer on the reactor wall, source case wall, and scraping blades was usually less than 1 kg, which was negligibly small for the analysis of polymerization. Continuous discharge of the polymer slurry and production of fine-powder polyethylene were successfully carried out. In the central source-type reactor, a dose rate of 1.9 × 10⁵ rads/hr was obtained with a ⁶⁰Co source of ca. 12 kCi.     

Temperature Dependence of Young's Modulus and Internal Friction in Alumina, Silicon Nitride, and Partially Stabilized Zirconia Ceramics

The temperature dependence of Young's modulus and internal friction (Q⁻¹)in alumina, silicon nitride, and partially stabilized zirconia (Y-PSZ) ceramics was studied. Little change in Q⁻¹ was found for alumina, whereas Q⁻¹ for silicon nitride ceramics increased above 700°C. The Q⁻¹ of Y-PSZ increased markedly with increasing temperature up to a peak at ∼200°C.     

Diel rhythms of calling behavior and pheromone production of oriental tobacco budworm moth,Helicoverpa assulta (Lepidoptera: Noctuidae)

Both calling behavior and titer of (Z)-9-hexadecenal (Z9-16: Al), the major sex pheromone component ofHelicoverpa assulta, in pheromone glands showed distinct diel periodicity, and these two were synchronous. Calling was most actively performed and the pheromone titer reached a maximum from 2 to 6 h after lights-off. During photophase, no calling was shown and only a relatively small amount of Z9-16:A1 was detected. However, there was a time lag of a few days between peak calling activity and maximum pheromone titer. The pheromone titer was maximal from age 1 day to age 5 days and thereafter decreased while calling was most actively performed after age 3 days. Titers of three minor components, hexadecenal, (Z)-11-hexadecenal, and (Z)-9-hexadecenyl acetate, showed similar daily fluctuation patterns to that of Z9-16:Al, but relative to the titer of Z9-16:Al, the titer of the two aldehyde components remained relatively constant whereas that ofZ9-16:Ac increased in the late scotophase.