Activities of FexO in CaO + CaF2 + SiO2 + FexO quaternary slags by disposable electrochemical oxygen probes

The activities of Fe_xO in CaO + CaF₂ + SiO₂ + Fe_xO quaternary slags were measured by means of solid-oxide galvanic cell. The Fe_xO activities in the slags are influenced by CaF₂ as well as SiO₂. At constant Fe_xO mole fractions, e.g., , at low SiO₂ mole fractions i.e., , the substitution of CaF₂ for CaO has an effect of raising the Fe_xO activity. At higher SiO₂ mole fractions, e.g., , however, such an effect becomes insignificant.     

A new correlation for the viscosity of gaseous fluorocarbon refrigerants

A new generalized correlation is presented for the low-pressure gaseous viscosity of fluorocarbon refrigerants. The following empirical equation is obtained based on the most reliable experimental data for 16 fluorocarbons: $$\eta \xi = \left( {0.5124T_r - 0.0517} \right)^{0.82} Z_c ^{ - 0.81}$$ where η is the viscosity in μPa·s and ξ is the viscosity parameter defined using the critical temperature T _c in K, the critical pressure P _c in MPa, and the molar mass M in g·mol^?1 as follows: $$\xi = T_c ^{1/6} M^{ - 1/2} P_c ^{ - 2/3}$$ The applicable ranges are 0.6<T _r<1.8 and 0.253<Z _c<0.282. The availability of the correlating equation for both pure fluorocarbons and their mixtures has been investigated based on the experimental data of these authors and those in the literature. It is found that the present correlation is useful for the prediction of the viscosity of pure fluorocarbons and their binary mixtures at atmospheric pressure with mean deviations less than 1.6%.     

Strengthening of nickel -base superalloys for nuclear heat exchanger application

Strengthening mechanisms of nickel-base superalloys have been discussed with the background of the Japanese research and development activities in this field. As candidates for materials of intermediate heat exchangers which will be used for a future programme of nuclear steelmaking systems, two kinds of alloys have successfully been developed in Japan. The designs of these alloys have been reviewed from metallurgical aspects including their composition and creep properties. In addition to the conventional methods to strengthen these alloys, such as solid solution hardening or particle precipitation hardening, a grain-boundary precipitation strengthening due to tungsten-rich ₂ phase in the Ni-Cr-W system, would be expected as a further advanced method.     

Screening of Inhibitors Targeting Heat Shock Protein 47 Involved in the Development of Idiopathic Pulmonary Fibrosis

Heat shock protein 47 (HSP47), a collagen-specific molecular chaperone, is causally related to fibrotic diseases, including idiopathic pulmonary fibrosis. The identification of Compounds that interfere with the HSP47-collagen interaction is essential for the development of relevant therapeutics. Herein, we prepared human HSP47 as a soluble fusion protein expressed in E. coli and established an assay system for HSP47 inhibitor screening. We screened a natural and synthetic Compound library established at Nagasaki University. Among 1023 Compounds, 13 exhibited inhibitory activity against human HSP47, of which three inhibited its function in a dose-dependent manner. Epigallocatechin-3-O-gallate, one of these three Compounds, is a typical polyphenol Compound derived from tea leaves. Structurally related Compounds were synthesized and examined for their activity, revealing a hydroxyl group at A-ring position 5 as important for its activity. The present findings provide valuable insight for the development of natural product-derived therapeutics for fibrotic diseases, including idiopathic pulmonary fibrosis.     

Removal of nitrogen oxides from air by chemicals-impregnated carbons

Fixation of nitrogen oxides (NO_x) in air onto granular activated carbon impregnated with chemicals was attempted to improve removal efficiency of NO_x by activated carbon adsorption. Nitric oxide (NO) and nitrogen dioxide (NO₂), were tried to remove by a flow test. Fixed-bed adsorption breakthrough curves were obtained when some kinds of carbon were used. The amount adsorbed of NO₂ changed with the amount and kinds of metallic salts impregnated. Chemicals-impregnated carbons were prepared from a commercial activated carbon. Among obtained carbons, the one which showed the highest selectivity for NO_x was chosen, and its performance with the change in humidity was determined. Removal mechanism of NO₂ was estimated, and the carbon impregnated with potassium hydroxide was found to be superior to any other carbon tested. The amount of the adsorbed NO and that produced by the reduction of NO₂ were determined from the breakthrough curves.     

Effect of Composition on the Oxygen Tracer Diffusion in Transparent Yttrium Aluminium Garnet (YAG) Ceramics

The grain boundary structure and oxygen tracer diffusion in transparent yttrium aluminum garnet (YAG) ceramics varying from 2% excess of Y₂O₃ to 0.5% excess of Al₂O₃ were studied. The characterization of the specimens is as follows: (i) For the Y₂O₃-excess specimen, a second phase (yttrium aluminum perovskite: YAP) containing silicon in the grain boundary was found, (ii) For the Al₂O₃-excess specimen, both aluminum-rich particles (alumina) and a silicon-rich segregant layer were observed in the grain boundary. The volume diffusion of the oxygen tracer is little influenced by the excess composition. In contrast, the grain boundary diffusion of the oxygen tracer is suppressed in the Y₂O₃-excess specimens, compared to Al₂O₃-excess specimens. These differences are thought to result from the chemical reaction between the second phase and the intergranular liquid phase during the sintering.     

Structural analysis of Au/Mg(OH)2 during deactivation by Debye function analysis

Using a Debye function analysis, the presence of icosahedral and face centered cuboctahedral gold in a 1 1 ratio has been found in freshly prepared Au/Mg(OH)₂ catalyst. The results support earlier studies which suggest the icosahedral form to be more stable at small nanometer sizes. Interactions between the gold and the Mg(OH)₂ support appear to be weak, with the gold rapidly coagulating over a period of three months. Re-analysis of the aged sample shows the gold to be mainly in the form of truncated decahedra.     

Different feeding and gustatory responses to ecdysone and 20-hydroxyecdysone by larvae of the silkworm,Bombyx mori

The feeding and gustatory responses to ecdysone and 20-hydroxyecdysone were investigated in the silkworm,Bombyx mori. 20-Hydroxyecdysone reduced feeding response strongly in fourth- and fifth-instar larvae, whereas ecdysone had no effect on feeding response. 20-Hydroxyecdysone stimulated the R receptor, the receptor to feeding deterrents, to a great degree. By contrast, ecdysone was much less effective for stimulating the R receptor. These results indicate that ecdysone and 20-hydroxyecdysone have different effects on feeding response due to different interactions with mouthpart chemoreceptors.     

Studies on biaxial stretching of polypropylene film. IX. Melting behavior of biaxially stretched film in one step

Melting temperature of a film biaxially stretched in one step in air at 152 or 140°C increases with increase of vA, whereas heat of fusion and density decrease with increase of vA, where vA is the degree of stretching in area. The rapid decrease in density occurs for vA > 10. Extrapolation of the plot of the density versus vA^?1/2 gives a value of 0.870 g/cm³ at infinite vA, which has been reported as the amorphous density of isotactic polypropylene by Farrow. This is so because the fine structure of the film becomes more and more amorphous with further stretching and reaches completely amorphous state at infinite vA. The temperature of stretching has a strong effect on the thermal behavior of a film; a low stretching temperature (140°C) brings about lower melting temperature, heat of fusion, and density. Crystallinity after melt press has not so large an effect on the melting behavior as the stretching temperature. Melting temperature and the shape of the thermogram also depend on the heating rate. There is an appropriate heating rate depending on vA which gives the minimum melting temperature. With stretched samples, a small side peak or a shoulder appears at a relatively low temperature in the thermogram when a high heating rate is used.