Optimization of a schottky barrier mixer diode in the submillimeter wave region

We have designed a mixer Schottky barrier diode (SBD) for use in the submillimeter wave region with a structure optimized for minimum noise temperature. The dependence of mixer noise temperature upon thickness and doping density of the epitaxial layer and diode diameter of SBDs was simulated within the framework of existing theories. Special care was taken to formulate the SBD current-voltage and capacitance-voltage relations in a way that correctly describes the behavior of real SBDs.     

Beta-thujaplicin zinc chelate induces apoptosis in mouse high metastatic melanoma B16BL6 cells

The cytotoxic effects of beta-thujaplicin and five kinds of metal chelates were examined on mouse melanoma B16BL6 cells by cell viability and lactate dehydrogenase (LDH) release assay. Beta-thujaplicin-zinc chelate and beta-thujaplicin-copper chelate had higher cytotoxic effects than beta-thujaplicin, and the 50% effective doses (ED50) of these metal chelates were 12.5 and 25 microM, respectively. In addition, the zinc chelate induced DNA ladder formation in B16BL6 cells, as shown by the DNA fragmentation assay, suggesting that cell death induced by the zinc chelate is apoptosis. The zinc chelate also had a cytotoxic effect and induced DNA fragmentation on other tumor cell lines: HeLa, Meth A, and B16F1 cells, but not on normal human diploid fibroblasts FS-4. These results suggest that beta-thujaplicin-zinc chelate induces apoptotic cell death in various tumor cell lines and is a potent antitumor agent for tumor cells including malignant melanomas.     

Lack of PPCA expression only partially coincides with lysosomal storage in galactosialidosis mice: indirect evidence for spatial requirement of the catalytic rather than the protective function of PPCA

Protective protein/cathepsin A (PPCA) is a pleiotropic lysosomal enzyme that complexes with beta-galactosidase and neuraminidase, and possesses serine carboxypeptidase activity. Its deficiency in man results in the neurodegenerative lysosomal storage disorder galactosialidosis (GS). The mouse model of this disease resembles the human early onset phenotype and results in severe nephropathy and ataxia. To understand better the pathophysiology of the disease, we compared the occurrence of lysosomal PPCA mRNA and protein in normal adult mouse tissues with the incidence of lysosomal storage in PPCA(-/-) mice. PPCA expression was markedly variable among different tissues. Most sites that produced both mRNA and protein at high levels in normal mice showed extensive and overt storage in the knockout mice. However, this correlation was not consistent as some cells that normally expressed high levels of PPCA were unaffected in their storage capability in the PPCA(-/-) mice. In addition, some normally low expressing cells accumulated large amounts of undegraded products in the GS mouse. This apparent discrepancy may reflect a requirement for the catalytic rather than the protective function of PPCA and/or the presence of cell-specific substrates in certain cell types. A detailed map showing the cellular distribution of PPCA in nomal mouse tissues as well as the sites of lysosomal storage in deficient mice is critical for accurate assessment of the effects of therapeutic interventions.     

Surface alterations of the bovine oocyte and its investments during and after maturation and fertilization in vitro

Surface characteristics of the bovine oocyte and its investments before, during, and after maturation, and fertilization in vitro were evaluated by scanning electron microscopy (SEM). Oocyte diameters were also measured during SEM analysis of the oocyte. The cumulus cells manifested a compact structure with minimal intercellular spaces among them in the immature oocytes. These became fully expanded with increased intercellular spaces after maturation in vitro, but contracted again after fertilization. The zona pellucida (ZP) showed a fibrous, open mesh-like structure in the maturing and matured oocytes. The size and number of meshes on the ZP decreased dramatically after fertilization. The vitelline surface of immature oocytes was characterized by distribution of tongue-shaped protrusions (TSPs) varying in density. After 10 and 22 hr of maturation incubation, oocyte surface microvilli (MV) increased to become the predominant surface structure, and TSPs decreased substantially. The vitelline surface of fertilized oocytes (at 6 and 20 hr) was similar to that of the matured oocytes, but unfertilized oocytes had less dense MV than did fertilized oocytes (at 20 hr). The diameter of the oocytes decreased from 99 to 80 microns during maturation and increased to 106 microns after insemination (P < 0.05). Membrane maturation was characterized by surface changes from a TSP-predominant pattern to a MV-predominant pattern. Thus, the bovine oocyte maturation process was found to involve the expansion of cumulus cells and the maturation of the ZP, which changes dramatically upon fertilization. Also, volumetric changes occurred in ooplasm processed for SEM following oocyte maturation and insemination.     

Wide gamut LCD using locally dimmable four‐primary‐color LED backlight

This paper proposes a wide gamut LCD using locally dimmable four‐primary‐color (4PC) LED backlight. Although the color gamut of LCDs has been improved in recent years, it is insufficient to reproduce all the colors in the real world. The objective of this paper is to propose a wide gamut LCD that reproduces all the colors in the real world while keeping the cost increases to a minimum. We evaluated the color gamut reproduced by LEDs of multiple primary colors and selected cyan as the optimal color to be added to the three primary colors to reproduce all the colors in the real world. Therefore, we designed an LED backlight consisting of an additional only‐cyan LED with three‐primary‐color LEDs and developed a prototype LCD with 4PC LED backlight. Furthermore, we developed a local dimming algorithm for the 4PC LED backlight. As a result, we confirmed that the prototype LCD with the 4PC LED backlight is able to cover almost all the colors in the real world and also able to display natural images with highly saturated colors by local dimming.     

Properties of indium oxide/tin oxide multilayered films prepared by ion-beam sputtering

The preparation and characterization of indium oxide (InO _x )/tin oxide (SnO _y ) multilayered films deposited by ion-beam sputtering are described and compared with indium tin oxide (ITO) films. The structure and the optoelectrical properties of the films are studied in relation to the layered structures and the post-deposition annealing. Low-angle X-ray diffraction analysis showed that most films retained the regular layered structures even after annealing at 500° C for 16 h. As an example, we obtained a resistivity of 6×10^–4 cm and a transparency of about 85% in the visible range at a thickness of 110 nm in a multilayered film of InO _x (2.0 nm)/SnO _y (0.2 nm)×50 pairs when annealed at 300° C for 0.5 h in air. Hall coefficient measurements showed that this film had a mobility of 17 cm² V^–1 sec^–1 and a carrier concentration (electron density) of 5×10²⁰ cm^–3.     

Preparation of zirconia-toughened bioactive glass-ceramics

Bioactive glass-ceramics toughened by tetragonal zirconia polycrystal (TZP) were prepared by hot-pressing mixed powders of the MgO-CaO-P₂O₅-SiO₂ glass and TZP containing 20 to 80% alumina. The bending strength and the fracture toughness of the composite materials were improved compared with those of the material without TZP. These composites showed high bending strengths (400 to 500MPa) and high fracture toughness ( 2.8MPa m^1/2). The existence of a crack deflection mechanism was observed by scanning electron microscopy. After soaking in simulated physiological solution at 100 °C, no phase transformation from tetragonal to monoclinic of TZP in the composites and no degradation in bending strength occurred.     

Deformation of NiO single crystals below room temperature: dislocation configurations

NiO single crystals prepared by two crystal growth techniques (zone melting in an arc-image furnace and Verneuil crystallization have been deformed by compression along 001 at temperatures as low as 4.2 K, and the dislocation substructure observed by transmission electron microscopy. The Peierls mechanism has been suggested as the mechanism controlling the mechanical behaviour at the lower temperatures. The dislocations generated at cavities found in the zone-melted crystals may be responsible for the increase of the flow stress of these crystals compared with the Verneuil ones.     

Surface tension of liquid3He and4He near the liquid-gas critical point

The surface tension of liquid³He and⁴He was measured near the gas-liquid critical points in the reduced temperature range 3×10^–4–1, where t (T _c –T)/T _c . The critical exponents were found to be ₃=1.289±0.015 for³He and ₄=1.306±0.017 for⁴He. These values are very close to those for classical liquids, and are consistent with the value of 1.28 predicted by Widom, but are apparently different from the exponents previously obtained for liquid helium isotopes, which are near unity. The critical coefficients show good agreement with the quantum-corrected corresponding states theory for the Lennard-Jones 6–12 potential discussed by Young. The interface thickness is deduced from Widom's theory to bed=d ₀t^–v withd ₃₀=0.14±0.03nm and v₃=0.57±0.04 for³He, andd ₄₀=0.37±0.07 nm and v₄=0.58±0.01 for⁴He.