Surface modification of biodegradable plastics by ion beams

Biodegradable plastics can be used as conventional plastics, while on disposal they decompose to water and carbon dioxide by microorganisms existing in natural environment. Products using biodegradable plastics have recently been developed in many companies pursuing ecology. In this study, surface modification of biodegradable plastics was carried out by inert ion beams for improvement of photo deterioration under an ultraviolet ray. The hardness of biodegradable plastics tended generally to decrease with irradiation of an ultraviolet ray. In this method, the hardness of ion-bombarded biodegradable plastics was kept at an initial value under an ultraviolet ray, because the modified layer by ion bombardment intercepted an ultraviolet ray. The hardness of He⁺ ion-bombarded biodegradable plastics showed larger value than that of Ar⁺ ion bombardment. He⁺ ion bombardment at ion energy of 10 keV produced the suitable property with both of high transmittance of a visible ray and high interception of an ultraviolet ray in a surface layer of biodegradable plastics.     

Kinetics of reactive diffusion between Au and Sn during annealing at solid-state temperatures

The reactive diffusion between Au and Sn was experimentally studied at solid-state temperatures using Sn/Au/Sn diffusion couples prepared by a diffusion bonding technique. The diffusion couples were annealed at temperatures of T = 393 and 473 K for various times in an oil bath with silicone oil. After annealing, compound layers composed of AuSn₄, AuSn₂ and AuSn were recognized to form at the Au/Sn interface. The thickness of the AuSn₄ layer is about six and four times greater than those of the AuSn₂ and AuSn layers at T = 393 and 473 K, respectively. The ratio of the thicknesses of the compound layers is kept constant independently of the annealing time. The total thickness l of the compound layers is described as a function of the annealing time t by the equation l = k(t/t₀)ⁿ, where t₀ is unit time, 1 s. The exponent n is nearly equal to 1/2 at T = 393 K but takes a value between 1/4 and 1/2 at T = 473 K. Such an intermediate value of n at T = 473 K indicates that the grain boundary diffusion contributes to the reactive diffusion and the grain growth occurs at certain rates. As the annealing temperature decreases, the contribution of the grain boundary diffusion should become more remarkable, but the grain growth will slow down. Consequently, n becomes close to 1/2 at T = 393 K. According to the constancy of the ratio of the thicknesses, it is concluded that the same rate-controlling process works in the AuSn₄, AuSn₂ and AuSn layers at a constant annealing temperature.     

基于微放电加工元件轮廓测量的探针制造

为了推动微加工和微机械技术的进步，微型零件轮廓和尺度测量方法的发展非常重要．可行方法之一就是使用带微探头的小型三维轮廓测量仪．这种仪器的探头必须针对某个零件的测量，按照最佳外形制造．微放电加工有着极小加工力，可用于各种探头的制造，本研究中用它进行探头加工．用这种方法制造了多种探头，将其装在基于扫瞄隧道显微技术(STM)的小型三维轮廓测量仪上．所制造的探头已被成功地用于各种微元件测量，结果表明此方法可行．     

High‐luminance 1‐m‐long plasma tubes for wall displays

Abstract— The plasma‐tube array is expected to realize a wall‐sized display. This method will realize an emissive‐type display with a flexible screen shape and an expandable screen size. The shape of the plasma tube was investigated to realize high luminance, high luminance efficacy, and high flexural strength. As the result, a cylindroid tube is proposed to satisfy these demands. An experimental display of 1 m × 128 mm has been developed with these cylindroid tubes and it demonstrated a high luminous efficacy of 3.1 lm/W.     

A novel bistable reflective display using quick‐response liquid powder

Abstract— We have developed new powder materials that exhibit liquid behavior, which can lead to the realization of novel bistable and reflective displays having paper‐white appearance, high contrast, and quick response. Two types of display were demonstrated, one had 160 × 160 array of pixels and the other had 320 × 320 in a 3.1‐in.‐diagonal viewable image size corresponding to 66 and 132 dpi, respectively. These displays were driven by passive‐matrix addressing. The displays showed a reflectivity of more than 41%, a contrast more than 1:10, and a pixel response time of less than 0.2 msec. The seven‐segment display for use in clocks was also demonstrated.     

Left ventricular diastolic properties of hypertensive patients measured by pulsed tissue Doppler imaging

Examination of left ventricular (LV) diastolic dysfunction in hypertensive patients has been based on parameters obtained from the transmitral flow velocity during pulsed Doppler echocardiography. However, these parameters are affected by loading conditions. We evaluated LV diastolic function along the longitudinal and transverse axes by pulsed tissue Doppler imaging (TDI) in 50 hypertensive (HT) patients and 36 age-matched healthy volunteers (N). Transmitral flow velocity was recorded by pulsed Doppler echocardiography. LV posterior wall motion velocity along the longitudinal and transverse axes also was recorded by pulsed TDI. In both groups, peak early diastolic velocity of the LV posterior wall (Ew) along the transverse axis (N: 15.8+/-5.2 cm/s, HT: 12.2+/-4.4 cm/s) was higher than that along the longitudinal axis (N: 12.7+/-3.1 cm/s, HT: 9.5+/-3.3 cm/s). Peak atrial systolic velocity of the LV posterior wall (Aw) along the longitudinal axis (N: 9.1+/-1.8 cm/s, HT: 9.7 +/-2.6 cm/s) significantly exceeded that along the transverse axis (N: 8.0+/-2.2 cm/s, HT: 8.4+/-2.4 cm/s) in both groups. The Ews were lower and the Aws were higher along both axes in the patient group than in the control group. The time intervals from the aortic component of the second heart sound to the peak of the early diastolic wave (IIA-Ews) along both the transverse (N: 142+/-18 ms, HT: 154+/-19 ms) and longitudinal (N: 151 16 ms, HT: 162+/-20 ms) axes were longer in the patient group. In 29 patients, Ews along both axes correlated negatively (transverse: r = -0.80, P < .0001; longitudinal: r = -0.71, P < .0001) and IIA-Ews correlated positively (transverse: r = 0.81, P < .0001; longitudinal: r = 0.74, P < .001) with the time constant of the LV pressure decay during isovolumic diastole. The Aws along both axes in the 24 patients without pseudonormalization in transmitral flow velocity correlated positively (transverse: r = 0.60, P < .001; longitudinal: r = 0.74, P < .0001) with the LV end-diastolic pressure. In conclusion, LV relaxation and filling along the longitudinal and transverse axes were impaired in many patients with hypertension. Pulsed TDI was useful for evaluating LV diastolic dynamics in this disease.     

Fabrication of TiO2-based transparent conducting oxide on glass and polyimide substrates

We report on preparation and properties of anatase Nb-doped TiO₂ transparent conducting oxide films on glass and polyimide substrates. Amorphous Ti_0.96Nb_0.04O₂ films were deposited at room temperature by using sputtering, and were then crystallized through annealing under reducing atmosphere. Use of a seed layer substantially improved the crystallinity and resistivity (ρ) of the films. We attained ρ = 9.2 × 10^− 4 Ω cm and transmittance of ~ 70% in the visible region on glass by annealing at 300 °C in vacuum. The minimum ρ of 7.0 × 10^− 4 Ω cm was obtained by 400 °C annealing in pure H₂.     

Development and Use of a Kinetical and Real-Time Monitoring System to Analyze the Replication of Hepatitis C Virus

In microbiological research, it is important to understand the time course of each step in a pathogen’s lifecycle and changes in the host cell environment induced by infection. This study is the first to develop a real-time monitoring system that kinetically detects luminescence reporter activity over time without sampling cells or culture supernatants for analyzing the virus replication. Subgenomic replicon experiments with hepatitis C virus (HCV) showed that transient translation and genome replication can be detected separately, with the first peak of translation observed at 3–4 h and replication beginning around 20 h after viral RNA introduction into cells. From the bioluminescence data set measured every 30 min (48 measurements per day), the initial rates of translation and replication were calculated, and their capacity levels were expressed as the sums of the measured signals in each process, which correspond to the areas on the kinetics graphs. The comparison of various HuH-7-derived cell lines showed that the bioluminescence profile differs among cell lines, suggesting that both translation and replication capacities potentially influence differences in HCV susceptibility. The effects of RNA mutations within the 5′ UTR of the replicon on viral translation and replication were further analyzed in the system developed, confirming that mutations to the miR-122 binding sites primarily reduce replication activity rather than translation. The newly developed real-time monitoring system should be applied to the studies of various viruses and contribute to the analysis of transitions and progression of each process of their life cycle.     

Self-assembly of three dimensional micro mechanisms using thermal shrinkage of polyimide

This paper describes three-dimensional microstructures fabricated using a simple self-assembly process involving the thermal shrinkage of polyimide. The proposed method enables hinged structures to be automatically rotated out of the wafer plane and to remain bent without the need to use any interlocking mechanisms. The hinged structures were fabricated using surface micromachining techniques involving heating in a furnace. An increase in the bending angle due to the shrinkage of polyimide was observed with increasing heating temperature, heating time, and length of the polyimide hinge. Of these three parameters, the heating time was found to be the most suitable for precise control of the bending angle. Furthermore, microcubes were fabricated by this method and the self-assembly process was successfully visualized using a CCD camera.