Reduction kinetics of Fe<Subscript>2</Subscript>MoO<Subscript>4</Subscript> fine powder by hydrogen in a fluidized bed

Iron molybdate (Fe₂MoO₄) powders with an average particle size of 100 μm were reduced by hydrogen using a fluidized-bed batch reactor in the temperature range of 923 to 1173 K. The extent of the reaction was followed as a function of time by gas chromatography. The fluidizing-gas velocity was set at about 1.5 times the minimum fluidization velocity. The ratio of the height of the static bed to its diameter is about 1. Under the prevailing experimental conditions, it was found that the chemical reaction was the rate-controlling factor. The activation energy for this process was 158±17 kJ/mol. The crystal size of the Fe₂Mo powder produced at lower temperatures was in the nanometer range, indicating the possibility of mass production of alloys and intermetallics in the nanorange, using a fluidized bed.     

金属—PAN—S配合物的极谱研究——Ⅱ:Fe~(3+)—PAN—S—TEA—NH_3·H_2O—NH_4Cl体系配合吸附波

在NH_3·H_2O—NH_4Cl—三乙醇胺底液中Fe(Ⅲ)与PAN—S产生一灵敏的配合吸附波,峰电位在—0.50伏(vs.SCE)。峰电位与铁离子浓度在2.8×10~8～3.4×10~(-6)mol/L范围内线性良好,检出下限可达2.8×10~(-8)mol/L。该法用于乳粉、头发、血清等样品的测定,结果满意。     

Composition Range of Amorphous Mg-Ni-Y Alloys

Based on the thermodynamic point of view, a method for predication of the composition range of amorphous ter-nary alloys was proposed. The composition range of amorphous ternary alloys is determined by the comparison of the excess free energy of the amorphous alloy and the free energy of competing crystalline states. The free energy is extrapolated from the data of three binary alloys by using Toop‘s model. The method was applied to predict the composition range of amor-phous Mg-Ni-Y alloys. The theoretical results are in good agreement with the available experimental results. It indicates that the present method can be used to predict the composition range for amorphous ternary alloys.     

ZJ510L-B汽车用高强度热轧板的试制

珠钢150t电弧炉-LF(VD)-CSP(紧凑式带材生产)流程试生产的5～8mm ZJ510L-B(0．16C--1．22Mn)汽车用高强度热轧板的铁素体晶粒尺寸为6．0～9．2μm，带状组织为1．5～2．5级，强度极限σb562～610MPa，延伸率δ5 32．0％～38．6％。文中还分析和提出了带状组织的形成原因和改进措施。     

Preparation of Compound Ultrafine CeO2 by Wet-Solid-Phase Mechanochemical Modification

To satisfy practical requirements from industrial applications, an alternate route for synthesis compound ultrafine CeO2 powders by wet-solid-phase mechanochemical modification using industrial grade hydrated cerium carbonate as raw material was proposed.The effect of modifier reaction percentage, reaction time, calcining temperature and modifier amount on particle size, density, suspensibility, and hardness of compound CeO2 powder was investigated.The phase evolutions of preparation process were characterized by XRD.SEM micrograph of the final product shows that compound CeO2 powders obtained are well-dispersed, spherically-shaped, uniformly-sized and submicron-sized particles.The method is readily available in raw material, low in cost, simple in process, and has great potential for industrialization.The compound CeO2 powders of different physical properties can be synthesized by controlling the above-mentioned influence factors in preparation process.     

单壁碳纳米管的制备及生长特性研究

采用Fe/MgO作为催化剂 ,催化裂解CH4制备了较纯的单壁碳纳米管 ,用TEM和Raman对碳纳米管进行了表征 ,对不同生长温度下制备的碳纳米管Raman径向呼吸振动峰 (RBM)进行了分析 ,研究了生长温度对单壁碳纳米管生长特性和结构特性的影响     

Calciothermic reduction of titanium oxide in molten CaCl<Subscript>2</Subscript>

Titanium oxides were reduced to metallic titanium using the liquid calcium floating on the molten CaCl₂. A part of Ca dissolved into CaCl₂ and reacted with TiO₂ settled below CaCl₂. The by-product CaO also dissolved by about 20 mol pct into CaCl₂, which was effective in reducing the oxygen concentration in the obtained Ti particles. The compositional region in the Ca-CaCl₂-CaO system was examined for the less oxygen contamination in Ti and the better handling in leaching. A large amount of the residual calcium oxidized the titanium powder in leaching. The metallic Ti powder less than 1000 mass ppm oxygen could be obtained only for 3.6 ks using 5 to 7 mol pct Ca-CaCl₂ at 1173 K. The powder was slightly sintered like sponge, and contained approximately 1500 ppm Ca. The anatase phae, the intermediate product in the refining process of TiO₂, could be also supplied as raw material as well as rutile.     

The electrochemical behaviour of nitrogen-containing austenitic stainless steel in methanolic solution

The corrosion behaviour of nitrogen-containing austenitic stainless steel in methanol containing different concentrations of H₂SO₄, HCl, LiCl and H₂SO₄ + HCl has been investigated using a potentiostatic polarization method. The cathodic reaction in the H₂SO₄, HCl and H₂SO₄ + HCl solutions was proton reduction whereas in the neutral LiCl solution, oxygen reduction was the predominant cathodic reaction. Active, passive and transpassive behaviours were observed only for higher concentrations of H₂SO₄ (0.01–2.0 M) due to the inherent water content. A cathodic loop, characterized by measured negative current in the anodic region, was also observed in solutions, in which the concentration of H₂SO₄ was 1.0 M or higher. The relative stability of the passive films decreased as the H₂SO₄ concentration increased, and thus the steel suffered from mild pitting corrosion. In the chloride environment, the rate of corrosion increased as the Cl⁻ ion concentration increased. The presence of acid along with Cl⁻ ions enhanced corrosion, and the corrosion rate increased significantly. The steel suffered from mild intergranular corrosion in acidic chloride solutions of methanol. In the H₂SO₄ + HCl solutions, passive films were only formed when the H₂SO₄ to HCl concentration ratio was greater than ∼10:1.