Monoclonal antibody 2D7 generated against a transition-state analog N-methyl mesoporphyrin catalyzes a reaction for insertion of a cupric ion into mesoporphyrin. To investigate amino acid residues responsible for the catalytic activity, site-directed mutagenesis of the amino acid residues in the third complementarity determining region of the heavy chain (CDRH3) was performed on the antigen-binding fragment (Fab) of the antibody. Recombinant Fab mutants, in which Arg95 is replaced with Ala (R95A), Asp96 with Asn (D96N) and Met97 with Gly (M97G), were examined in terms of the catalytic efficiency of the reaction (k/K(S)) and the dissociation constant for N-methyl mesoporphyrin binding (K(d)) and these values were compared with those of the wild type. The k/K(S) values of the R95A and D96N mutants were 0.96% and 1.0% of that of the wild type, respectively, whereas the M97G mutant had no detectable catalytic activity. The K(d) values of the R95A and D96N mutants were 165 and 69 times that of the wild type, respectively, while that of the M97G mutant was similar to that of the wild type. The relationship between the k/K(S) and 1/K(d) values in the wild type and the R95A and D96N mutants suggests that Arg95 and Asp96 are responsible for stabilizing the transition-state in the catalytic reaction. The results of the M97G mutant allow us to propose that Met97 plays an important role in the catalytic activity probably due to a subtle and specific conformation of the antibody.     

Fracture Energies of Tape-Cast Silicon Nitride with β-Si3N4 Seed Addition

The fracture energies of the tape-cast silicon nitride with and without 3 wt% rod-like β-Si₃N₄ seed addition were investigated by a chevron-notched-beam technique. The material was doped with Lu₂O₃–SiO₂ as sintering additives for giving rigid grain boundaries and good heat resistance. The seeded and tape-cast silicon nitride has anisotropic microstructure, where the fibrous grains grown from seeds were preferentially aligned parallel to the casting direction. When a stress was applied parallel to the fibrous grain alignment direction, the strength measured at 1500°C was 738 MPa, which was almost the same as room temperature strength 739 MPa. The fracture energy of the tape-cast Si₃N₄ without seed addition was 109 and 454 J/m² at room temperature and 1500°C, respectively. On the contrary, the fracture energy of the seeded and tape-cast Si₃N₄ was 301 and 781 J/m² at room temperature and 1500°C, respectively, when a stress was applied parallel to the fibrous gain alignment. The large fracture energies were attributable primarily to the unidirectional alignment fibrous Si₃N₄ grains.     

Transmission electron microscope observation of organic–inorganic hybrid thin active layers of light-emitting diodes

Low-resistivity indium tin oxide [ITO] film was successfully deposited on oxygen plasma-treated polyethylene terephthalate [PET] surfaces at room temperature. X-ray diffraction [XRD] measurements demonstrated that the film deposited on the PET surface that had not been treated with oxygen plasma had an amorphous structure. In contrast, after the low-power oxygen plasma treatment of the PET surface, the ITO film deposited on the PET surface had a poly-crystalline structure due to interactions between electric dipoles on the PET surface and electric dipoles in the ITO film. The minimum resistivity of the poly-crystalline ITO was about 3.6 times lower than that of the amorphous ITO film. In addition, we found that the resistivity of ITO film is proportional to the intensity of the (400) line in the film's XRD spectra.     

New Approach for Macro Porous RB‐SiC Derived from SiC/Novolac‐type Phenolic Composite

A novel fabrication route to make macroporous silicon carbide (SiC) has been proposed in this study. The route is composed of the following two steps: the fabrication of porous α‐SiC/novolac‐type phenolic composite using hexamethylenetetramine (HMT) as a curing/blowing agent for the novolac monomer and a conventional reaction‐bonded (RB) sintering of the composite. The α‐SiC/novolac‐type phenolic composite was carbonized at 800°C for 2 h in N₂ gas and then reacted with the molten silicon at 1450°C for 30 min under vacuum, resulting in the macroporous RB‐SiC with an open porosity of 48% and relatively large pore size of ~110 μm. The compressive strength of the macroporous RB‐SiC was 113 MPa, which is relatively high compared to those reported for macroporous SiC of equivalent porosities and pore sizes.     

Effects of Annealing on Dielectric Loss and Microstructure of Aluminum Nitride Ceramics

The effect of annealing on tan δ and microstructures of aluminum nitride (AlN) ceramics were explored. Yttria was added as a sintering additive to AlN powders, and the powders were pressureless-sintered at 1900°C for 2 h in a nitrogen flow atmosphere. In succession to sintering, AlN samples were annealed at 720, 970 and 1210°C for 2 and 4 h. Very low tan δ values between 2.6 and 6.0 × 10⁻⁴ at 28 GHz were obtained when the AlN samples were annealed for 4 h at all the annealing temperatures.     

High‐strength regenerated cellulose fibers spun from 1‐butyl‐3‐methylimidazolium chloride solutions

High‐performance regenerated cellulose fibers were prepared from cellulose/1‐butyl‐3‐methylimidazolium chloride (BMIMCl) solutions via dry‐jet wet spinning. The spinnability of the solution was initially evaluated using the maximum winding speed of the solution spinning line under various ambient temperatures and relative humidities in the air gap. The subsequent spinning trials were conducted under various air gap conditions in a water coagulation bath. It was found that low temperature and low relative humidity in the air gap were important to obtain fibers with high tensile strength at a high draw ratio. From a 10 wt % cellulose/BMIMCl solution, regenerated fibers with tensile strength up to 886 MPa were prepared below 22 °C and relative humidity of 50%. High strengthening was also strongly linked with the fixation effect on fibers during washing and drying processes. Furthermore, an effective attempt to prepare higher performance fibers was conducted from a higher polymer concentration solution using a high molecular weight dissolving pulp. Eventually, fibers with a tensile strength of ～1 GPa and Young's modulus over 35 GPa were prepared. These tensile properties were ranked at the highest level for regenerated cellulose fibers prepared by an ionic liquid–based process. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134, 45551.     

Laser Photolysis Study on Mechanism and Efficiency of Electron Transfer Between Fullerenes (C60 and C70) and Tetraselenafulvalenes

Abstract

Efficient electron-transfer reactions from three kind of tetraselenafulvalenes (TSeF's) to photoexcited triplet state of C₆₀ or C₇₀ in polar solvents have been confirmed by transient absorption spectroscopy observing the decay of ³C₆₀*/³C₇₀* and rise of C₆₀ ^??/C₇₀ ^??. Growth of single crystal seems to be stimulated by laser irradiation of the solution containing C₆₀ and bis(ethylenedithio)tetraselena-fulvalene (BEDT-TSeF), in which C₆₀ ^?? was effectively formed.     

Polyphenols Extracted from Black Tea (Camellia sinensis) Residue by Hot‐Compressed Water and Their Inhibitory Effect on Pancreatic Lipase in vitro

Abstract: Polyphenols, retained in black tea wastes following the commercial production of tea beverages, represent an underutilized resource. The purpose of this study was to investigate the potential use of hot‐compressed water (HCW) for the extraction of pancreatic lipase‐inhibiting polyphenols from black tea residues. Black tea residues were treated with HCW at 10 °C intervals, from 100 to 200 °C. The resulting extracts were analyzed using high‐performance liquid chromatography‐mass spectrometry and assayed to determine their inhibitory effect on pancreatic lipase activity in vitro. Four theaflavins (TF), 5 catechins, 2 quercetin glycosides, quinic acid, gallic acid, and caffeine were identified. The total polyphenol content of extracts increased with increasing temperature but lipase inhibitors (TF, theaflavin 3‐O‐gallate, theaflavin 3′‐O‐gallate, theaflavin 3,3′‐O‐gallate, epigallocatechin gallate, and epicatechin gallate) decreased over 150 °C. All extracts inhibited pancreatic lipase but extracts obtained at 100 to 140 °C showed the greatest lipase inhibition (IC₅₀s of 0.9 to 1.3 μg/mL), consistent with the optimal extraction of TFs and catechins except catechin by HCW between 130 and 150 °C. HCW can be used to extract pancreatic lipase‐inhibiting polyphenols from black tea waste. These extracts have potential uses, as dietary supplements and medications, for the prevention and treatment of obesity. Practical Application: Active forms of lipase inhibitors can be recovered from black tea residues. They could be used as dietary supplements or medications.     

Visible Light Irradiation of [60]Fullerene Causes Killing and Initiation of Transformation in Balb/3T3 Cells

Abstract

Cell transformation in vitro is a model of carcinogenesis in vivo. Two-stage transformation assay increases the sensitivity of cells to chemicals and permits detection of carcinogens acting as initiating agents. [60]Fullerene (C₆₀) was cytotoxic in BALB/3T3 cells when it was irradiated by visible light, but not without light irradiation. Under conditions when C₆₀ was cytotoxic, it acted as an initiating agent for cell transformation, but it did not act as a complete transforming agent. the initiating activity of visible-light-irradiated C₆₀ was statistically significant in a modified two-stage transformation assay including a procedure for replating cells treated by C₆₀ and light, but it was equivocal in the standard two-stage transformation assay.     

Spatial mapping of electronic states in κ-(BEDT-TTF)2X using infrared reflectivity

We review our recent work on spatial inhomogeneity of the electronic states in the strongly correlated molecular conductors κ-(BEDT-TTF)₂X. Spatial mapping of infrared spectra (SMIS) is used for imaging the distribution of the local electronic states. In molecular materials, the infrared response of the specific molecular vibration mode with a strong electron–molecular vibration coupling can reflect the electronic states via the change in the vibration frequency. By spatially mapping the frequency shift of the molecular vibration mode, an electronic phase separation has been visualized near the first-order Mott transition in the bandwidth-controlled organic conductor κ-(BEDT-TTF)₂Cu[N(CN)₂]Br. In addition to reviewing SMIS of the phase separation, we briefly mention the electronic and optical properties of κ-(BEDT-TTF)₂X.